Production method of deciduous tooth jewelry
A production method and technology of deciduous teeth, applied in jewelry and other directions, can solve the problems of inability to know what deciduous teeth look like, no second experience, no new ideas, etc., and achieve the effect of enriching the diversification of products.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0041] A method for making deciduous teeth jewelry comprises the following steps:
[0042] Step 1: The deciduous teeth are soaked in a hydrogen peroxide solution, and the organic matter of the deciduous teeth is removed by the oxidation of the hydrogen peroxide solution. Wherein the hydrogen peroxide solution is prepared by the following method: dilute the food additive hydrogen peroxide with a concentration of 35% by 50 times with distilled water to obtain the hydrogen peroxide solution. The deciduous teeth were soaked in the hydrogen peroxide solution for 12 hours at normal temperature.
[0043] Step 2: soak the deciduous teeth treated in step 1 with ethanol solution at low temperature. Wherein the concentration of ethanol solution is 75%. The deciduous teeth were soaked in the ethanol solution for 12 hours.
[0044] Step 3: Apply the acrylic resin oligomer on the surface of the deciduous teeth treated in step 2, and irradiate with ultraviolet light for 30 minutes to init...
Embodiment 2
[0047]A method for making deciduous teeth jewelry comprises the following steps:
[0048] Step 1: The deciduous teeth are soaked in a hydrogen peroxide solution, and the organic matter of the deciduous teeth is removed by the oxidation of the hydrogen peroxide solution. Wherein the hydrogen peroxide solution is prepared by the following method: dilute 20% food additive hydrogen peroxide with distilled water 28.6 times to obtain the hydrogen peroxide solution. The deciduous teeth were soaked in the hydrogen peroxide solution for 24 hours at normal temperature.
[0049] Step 2: soak the deciduous teeth treated in step 1 with ethanol solution at low temperature. Wherein the concentration of ethanol solution is 60%. The deciduous teeth were soaked in the ethanol solution for 24 hours.
[0050] Step 3: Apply the acrylic resin oligomer to the surface of the deciduous teeth treated in step 2, and irradiate with ultraviolet light for 60 minutes to initiate the curing of the acrylic...
Embodiment 3
[0053] A method for making deciduous teeth jewelry comprises the following steps:
[0054] Step 1: The deciduous teeth are soaked in a hydrogen peroxide solution, and the organic matter of the deciduous teeth is removed by the oxidation of the hydrogen peroxide solution. Wherein the hydrogen peroxide solution is prepared by the following method: dilute 40% food additive hydrogen peroxide with distilled water 57 times to obtain the hydrogen peroxide solution. The deciduous teeth were soaked in the hydrogen peroxide solution for 18 hours at normal temperature.
[0055] Step 2: soak the deciduous teeth treated in step 1 with ethanol solution at low temperature. Wherein the concentration of ethanol solution is 80%. The deciduous teeth were soaked in the ethanol solution for 18 hours.
[0056] Step 3: Apply the acrylic resin oligomer on the surface of the deciduous teeth treated in step 2, and irradiate with ultraviolet light for 45 minutes to initiate the curing of the acrylic ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com