Hydrogel gasket material for dentures and preparation method thereof

A hydrogel and spacer technology, which is applied in the field of denture soft lining materials, can solve the problems of denture spacers with single function, periodontal swelling, bleeding, and easy gingivitis, so as to improve the sterilization effect, improve chewing efficiency, and improve The effect of aesthetic effect

Active Publication Date: 2018-08-28
蚌埠佳美仕义齿有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing denture spacers have single functions and poor comfort, which can easily cause symptoms such as gingivitis, periodontal swelling, and bleeding, which brings inconvenience to patients.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogel gasket material for dentures and preparation method thereof
  • Hydrogel gasket material for dentures and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A denture hydrogel spacer material is made of the following raw materials in parts by weight:

[0019] Palm fiber 5, sodium hypochlorite 3, peppermint oil 4, longan core 2, nettle root 3, chitosan 30, polyvinyl alcohol solution 50, glutaraldehyde solution 15;

[0020] The mass fraction of the glutaraldehyde solution is 30%. .

[0021] Further, the preparation method of the polyvinyl alcohol solution is as follows: adding polyvinyl alcohol into deionized water 5 times its volume, heating to 40°C to fully dissolve it, then adding tea tree oil, stirring evenly, and placing it in a water bath at 70°C , stirred and swelled for 3h, then raised the temperature to 80°C and stirred for 20min.

[0022] Further, its preparation method comprises the following steps:

[0023] (1) Put the palm fiber into a pulverizer for 10 minutes, pass through a 200-mesh sieve, immerse in distilled water 15 times the volume of the palm fiber, heat and stir until boiling, let it fully swell for 2...

Embodiment 2

[0029] A denture hydrogel spacer material is made of the following raw materials in parts by weight:

[0030] Palm fiber 6, sodium hypochlorite 4, peppermint oil 5, longan core 3, nettle root 4, chitosan 40, polyvinyl alcohol solution 60, glutaraldehyde solution 17;

[0031] The glutaraldehyde solution mass fraction is 40%.

[0032] Further, the preparation method of the polyvinyl alcohol solution is as follows: adding polyvinyl alcohol into deionized water 7 times its volume, heating to 45°C to fully dissolve it, then adding tea tree oil, stirring evenly, and placing it in a water bath at 72°C , stirred and swelled for 3.5 hours, then raised the temperature to 82°C and stirred for 25 minutes.

[0033] Further, its preparation method comprises the following steps:

[0034] (1) Put the palm fiber into a pulverizer for 15 minutes, pass through a 250-mesh sieve, immerse in distilled water 17 times the volume of the palm fiber, heat and stir until it boils, make it fully swell f...

Embodiment 3

[0040]A denture hydrogel spacer material is made of the following raw materials in parts by weight:

[0041] Palm fiber 10, sodium hypochlorite 5, peppermint oil 6, longan core 5, nettle root 6, chitosan 50, polyvinyl alcohol solution 80, glutaraldehyde solution 20;

[0042] The mass fraction of the glutaraldehyde solution is 50%.

[0043] Further, the preparation method of the polyvinyl alcohol solution is as follows: adding polyvinyl alcohol into deionized water 10 times its volume, heating to 50°C to fully dissolve it, then adding tea tree oil, stirring evenly, and placing it in a water bath at 75°C , stirred and swelled for 4h, then raised the temperature to 85°C and stirred for 30min.

[0044] Further, its preparation method comprises the following steps:

[0045] (1) Put the palm fiber into a pulverizer for 20 minutes, pass through a 300-mesh sieve, immerse in distilled water 20 times the volume of the palm fiber, heat and stir until boiling, make it fully swell for 30...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hydrogel gasket material for dentures and a preparation method thereof. After palm fiber is treated, modification is conducted by using longan seed and urticae radix leachingliquid, so that the palm fiber is soft and has toughness, the tensile strength of the hydrogel material is improved, the service life of the hydrogel material is prolonged, the prepared hydrogel haseffects of stopping bleeding, relieving pain and reducing inflammation, and improving the symptoms such as gingivitis, periodontal swelling, bleeding and the like caused by gaps between dentures and gums, loosening and friction, the dentures are fixed, and the chewing efficiency is improved.

Description

technical field [0001] The invention belongs to the technical field of denture soft lining materials, and in particular relates to a denture hydrogel spacer material and a preparation method thereof. Background technique [0002] Immediate restoration of complete dentures can maintain the patient's facial aesthetics, language and chewing functions, and relieve the patient from the pain of missing teeth. However, within a period of time when the immediate denture is worn, due to the rapid absorption of the alveolar bone after tooth extraction, a gap will appear between the denture base and the supporting tissue, resulting in denture looseness and tenderness. Adhesive spacers can improve the satisfaction rate of denture use, improve the chewing function of dentures, and obtain better clinical results. However, the existing denture spacers have single functions and poor comfort, which can easily cause symptoms such as gingivitis, periodontal swelling, and bleeding, which bring...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/097A61K6/083A61K6/02A61K6/00A61K6/898
CPCA61K6/15A61K6/30A61K6/69A61K6/80A61K6/887A61K6/898C08L29/04
Inventor 冷朋
Owner 蚌埠佳美仕义齿有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap