Ultrahigh-impact-toughness high-purity-degree steel for low temperature pressure vessel and production method thereof

An impact toughness and pressure vessel technology, applied in the field of high-purity low-temperature pressure vessel steel, can solve the problem of difficulty in meeting the requirements of strength and toughness stably, and achieve the effects of excellent comprehensive mechanical properties, improved cleanliness, high and low temperature impact toughness

Active Publication Date: 2018-10-26
JIANGSU LIHUAI IRON AND STEEL CO LTD +1
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the 09MnD steel commonly used in China is difficult to stably meet the above toughness requirements after normalizing, and can only ensure the safe use at -45°C. In order to ensure the safe use of pressure vessels at -50°C-55°C, it must be re- Design composition and optimize process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrahigh-impact-toughness high-purity-degree steel for low temperature pressure vessel and production method thereof
  • Ultrahigh-impact-toughness high-purity-degree steel for low temperature pressure vessel and production method thereof
  • Ultrahigh-impact-toughness high-purity-degree steel for low temperature pressure vessel and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0045] Such as figure 2 Shown, the chemical composition of the present invention is compared with the chemical composition of 09MnD steel.

[0046] And according to the following method to produce 4 sets of examples:

[0047] 1) Converter smelting: smelting in a top-bottom combined blowing converter of more than 100 tons, using molten iron and high-quality scrap steel as raw materials for preliminary smelting, to achieve pre-de-P removal, and adding synthetic refining slag, composite deoxidizer and a variety of high purity to the steel The alloy is pre-deoxidized and the composition is initially adjusted, and the sliding plate is used to block slag to keep the steel from tapping to prevent back to P;

[0048] 2) Refining: deep deoxidation and alloying of molten steel in an LF furnace of more than 100 tons, making a refined slag with a basicity slag R=5~8, and strengthening the removal of S and removing inclusions through the steel slag reaction; stirring throughout the refining proc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses ultrahigh-impact-toughness high-purity-degree steel for a low temperature pressure vessel. The ultrahigh-impact-toughness high-purity-degree steel comprises the chemical components of, by mass, 0.06-0.08% of C, 0.20-0.35% of Si, 1.15-1.35% of Mn, 0.01-0.02% of Ti, 0.12-0.15% of Ni, 0.020-0.045% of Al, 0-0.010% of P, 0-0.003% of S, 0-0.0015% of [O], 0-0.0050% of [N], 0-0.00015% of [H] and the balance Fe. In this way, according to the ultrahigh-impact-toughness high-purity-degree steel for the low temperature pressure vessel and a production method thereof, the content ofthe C is decreased through precise control, strong deoxidization and crystalline grain refining are conducted through the Al, alloying is conducted through the Ni and the Ti, thus, compared with 09MnD steel of Q / TDGG 0040-2004, the ultrahigh-impact-toughness high-purity-degree steel is suitable for the lower medium temperature which is from -50 DEG C to -55 DEG C, and has higher low-temperature impact toughness, and the overall mechanical property of the ultrahigh-impact-toughness high-purity-degree steel is more stable.

Description

Technical field [0001] The invention relates to the technical field of low-alloy steel in the iron and steel industry, in particular to a steel for low-temperature pressure vessels with ultra-high impact toughness and high purity and a production method thereof. Background technique [0002] Cryogenic pressure vessel is a kind of cryogenic vessel. The ferritic steel commonly used in general pressure vessels reaches the brittle transition temperature when the temperature drops to a certain temperature, the toughness of the steel drops sharply, and it is extremely easy to break. When the pressure vessel is used below the transition temperature, if there is a local stress concentration in the vessel caused by defects, residual stress and other factors, the vessel is likely to undergo brittle fracture without obvious plastic deformation, resulting in Catastrophic accident. [0003] For low-temperature pressure vessels, appropriate materials must first be selected according to the pur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/14C22C38/08C22C38/06C21C7/06C21C7/10C21C7/072C21D8/06
CPCC21C7/0006C21C7/06C21C7/072C21C7/10C21D8/065C22C38/02C22C38/04C22C38/06C22C38/08C22C38/14Y02P10/20
Inventor 左辉翟万里郑力宁肖波印传磊许光乐石可伟谭利
Owner JIANGSU LIHUAI IRON AND STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products