980mpa grade cold-rolled dual-phase steel with low requirement on production line cooling capacity and manufacturing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of cooling capacity and manufacturing method, applied in the field of steelmaking, can solve the problems of high requirements for production line cooling capacity, no ultra-high-strength production line, and difficulty in controlling on-site production stability.
Active Publication Date: 2020-09-04
武汉钢铁有限公司
View PDF7 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
With the continuous upgrading of lightweight, 980MPa grade cold-rolled dual-phase steel will gradually be applied in large quantities in future automotive materials. The principle is that it has high requirements on the cooling capacity of the production line, and generally needs to be produced on a special line for ultra-high-strength steel. Only a few domestic steel mills have mass production capacity
[0004] At present, Wuhan Iron and Steel Co., Ltd. only has an ordinary automobile sheet production line, and has not built a dedicated ultra-high-strength production line. The existing continuous annealing production line generally has a cooling rate of less than 30°C / s. With the continuous increase in market demand for 980MPa grade cold-rolled dual-phase steel, how to The problem of producing high-quality ultra-high-strength steel products on the current production line needs to be solved urgently
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0058] This embodiment provides a 980MPa grade cold-rolled dual-phase steel with low requirements on the cooling capacity of the production line, which is composed of the following chemical components in mass percentages: C: 0.141%, Si: 0.23%, Mn: 1.91%, P: 0.009%, Cr: 0.46%, Alt: 0.04%, Nb: 0.02%, B: 0.0008%, S: 0.003%, N: 0.0022%, and the balance is Fe and unavoidable impurities.
[0059] The production method of above-mentioned duplex steel, its step is as follows:
[0060] In the hot rolling process, the slab heating temperature is 1270-1282°C, the final rolling temperature is 892-901°C, the coiling temperature is 639-657°C, the cold rolling reduction is 62%, the annealing temperature is 805-812°C during the annealing process, and the slow cooling The end temperature of the section is 629~637°C, the end temperature of the fast cooling section is 301~315°C, the cooling rate of the slow cooling section is 6°C / s, the cooling rate of the fast cooling section is 25°C / s, the ove...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
thickness
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses 980MPa grade cold-rolled dual-phase steel with low requirements for cooling capacity of a production line and a manufacturing method thereof, and belongs to the technical fieldof steelmaking. The 980MPa grade cold-rolled dual-phase steel consists of the following chemical composition of, by mass, 0.14-0.17% of C, 0.10-0.30% of Si, 1.8-2.2% of Mn, less than or equal to 0.012% of P, 0.4-0.6% of Cr, 0.02-0.07% of Alt, 0.01-0.02% of Nb, 0.0005-0.002% of B, less than or equal to 0.005% of S, less than or equal to 0.005% of N, and the balance Fe and unavoidable impurities. According to the chemical composition, the 980MPa grade cold-rolled dual-phase steel is manufactured through smelting and slab casting process, and slab heating, hot rolling, coiling, pickling, cold rolling and continuous annealing process. In the continuous annealing process, the annealing temperature is controlled to be 800-820 DEG C, the cooling rate of a slow cooling section is less than 8 DEGC / s, the finish temperature of the slow cooling section is 620-640 DEG C, the finish temperature of a rapid cooling section is 300-320 DEG C, the cooling rate of the rapid cooling section is less than30 DEG C / s, and the over aging temperature is 270-310 DEG C. The dual-phase steel is prepared according to the chemical composition and the process of the 980MPa grade cold-rolled dual-phase steel with the low requirements for the cooling capacity of the production line and the manufacturing method thereof, the requirements for the rapid cooling rate in the production line are low, and the 980MPagrade cold-rolled dual-phase steel with the low requirements for the cooling capacity of the production line and the manufacturing method thereof can be used in a conventional common production line.
Description
technical field [0001] The invention relates to a method for manufacturing high-strength cold-rolled dual-phase steel, belonging to the technical field of steelmaking, and in particular to a 980MPa grade cold-rolled dual-phase steel with low requirements on the cooling capacity of a production line and a manufacturing method thereof. Background technique [0002] With the development of the automobile industry, the market demand for vehicles with small displacement and low energy consumption is increasing day by day. According to statistics, for every 10% reduction in vehicle quality, fuel consumption can be reduced by 3-7%. Due to considerations of cost, energy, safety, and the environment, automobile lightweight is the development direction of the modern automobile industry. Optimizing and upgrading the performance of steel materials, which account for 55-70% of the total weight of the vehicle, plays an important role in the process of vehicle lightweighting. In order to...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.