Cross-linked polyolefin foam material with high temperature resistance and preparation method thereof
A technology for cross-linked polyolefin and foam materials, which is applied in the field of cross-link polyolefin foam materials and their preparation, and can solve problems such as the influence of sealing and cushioning effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0049] The raw material of cross-linked polyolefin foam material 1 with high temperature resistance includes 60 parts of polyolefin resin, 18 parts of blowing agent, 4 parts of toughening agent, 3 parts of coupling agent and 3 parts by weight. parts of antioxidants;
[0050] Among them, the polyolefin resin is composed of ultra-low density polyethylene, medium density polyethylene, and ethylene-methyl acrylate copolymer, the ratio is 1:3:1, and the fastest crystallization rate temperature T_(c,max)≤100℃ The mass fraction of olefin resin accounting for polyolefin resin is 40%;
[0051] The method for preparing the above-mentioned cross-linked polyolefin foam material 1 with high temperature resistance comprises the following steps:
[0052] ① Weighing polyolefin, foaming agent, toughening agent, coupling agent and antioxidant according to the weight percentage;
[0053] ②Mix polyolefin, foaming agent, toughening agent, coupling agent and antioxidant;
[0054] ③The raw materi...
Embodiment 2
[0058] The raw material of the cross-linked polyolefin foam material 2 with high temperature resistance comprises 90 parts of polyolefin resin, 7 parts of foaming agent, 0.1 part of coupling agent and 0.4 part of antioxidant in parts by weight. ;
[0059] Wherein the polyolefin resin is low-density polyethylene, wherein the polyolefin resin with the fastest crystallization rate temperature T_(c,max)≤100°C accounts for 70% of the mass fraction of the polyolefin resin;
[0060] The method for preparing the above-mentioned cross-linked polyolefin foam material 2 with high temperature resistance comprises the following steps:
[0061] ① Weigh polyolefin, foaming agent, coupling agent and antioxidant according to the weight percentage
[0062] ②Mix polyolefin, foaming agent, coupling agent and antioxidant;
[0063] ③The raw materials mixed in step ② are melted and extruded into sheets;
[0064] ④ subjecting the sheet in step ③ to cross-linking treatment by high-energy electron i...
Embodiment 3
[0067] The raw material of the cross-linked polyolefin foam material 3 with high temperature resistance includes 75 parts of polyolefin resin, 4 parts of blowing agent, 0.1 part of toughening agent, 0.2 part of coupling agent and 0.7 part by weight. parts of antioxidants;
[0068] Among them, the polyolefin resin is composed of low-density polyethylene, metallocene polyethylene, linear low-density polyethylene, ethylene-octene copolymer, ethylene-vinyl acetate copolymer, the ratio is 10:6:15:7:15, the most The mass fraction of polyolefin resin with fast crystallization rate temperature T_(c,max)≤100°C is 65%;
[0069] The method for preparing the above-mentioned cross-linked polyolefin foam material 3 with high temperature resistance comprises the following steps:
[0070] ① Weighing polyolefin, foaming agent, toughening agent, coupling agent and antioxidant according to the weight percentage; ② mixing polyolefin, foaming agent, toughening agent, coupling agent and antioxidan...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com