A quick-acting hemostatic gauze for promoting wound healing and its preparation method and application
A technology of wound healing and hemostatic gauze, which can be applied in medical formulations, bandages, and drug delivery. compatibility, effect of promoting rapid healing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0058] In this embodiment, the raw materials for the preparation of the hemostatic quick-acting hemostatic yarn that promotes wound healing include the following components in parts by weight:
[0059]
[0060] Wherein the chitosan is a mixture of lauroyl sulfate deacetyl chitosan and carboxymethyl chitosan, and the mass ratio of lauroyl sulfate deacetyl chitosan to carboxymethyl chitosan is 3:1.
[0061] The preparation method of the quick-acting hemostatic gauze for promoting wound healing comprises the steps:
[0062] (1) Sodium carboxymethyl cellulose and xanthan gum are mixed to obtain mixture A;
[0063] (2) α-n-octyl cyanoacrylate, lauroyl sulfate deacetylated chitosan, propyl p-hydroxybenzoate and methyl p-hydroxybenzoate are at a temperature of 120°C and a stirring rate of 140r / min Stirring and mixing for 80min to obtain mixture B;
[0064] (3) Stir and mix the mixture A prepared in step (1) and the mixture B prepared in step (2) for 30 minutes at a temperature o...
Embodiment 2
[0067] In this embodiment, the raw materials for the preparation of the hemostatic quick-acting hemostatic yarn that promotes wound healing include the following components in parts by weight:
[0068]
[0069] Wherein the chitosan is a mixture of lauroyl sulfate deacetyl chitosan and carboxymethyl chitosan, and the mass ratio of lauroyl sulfate deacetyl chitosan to carboxymethyl chitosan is 2:1.
[0070] The preparation method of the quick-acting hemostatic gauze for promoting wound healing comprises the steps:
[0071] (1) Sodium carboxymethyl cellulose and xanthan gum are mixed to obtain mixture A;
[0072] (2) α-n-octyl cyanoacrylate, lauroyl sulfate deacetylated chitosan, propyl p-hydroxybenzoate and methyl p-hydroxybenzoate are at a temperature of 100°C and the stirring speed is 130r / min. Stir and mix for 120min to obtain mixture B;
[0073] (3) Stir and mix the mixture A prepared in step (1) and the mixture B prepared in step (2) for 40 minutes at a temperature of ...
Embodiment 3
[0076] In this embodiment, the raw materials for the preparation of the hemostatic quick-acting hemostatic yarn that promotes wound healing include the following components in parts by weight:
[0077]
[0078] Wherein the chitosan is a mixture of lauroyl sulfate deacetyl chitosan and carboxymethyl chitosan, and the mass ratio of lauroyl sulfate deacetyl chitosan to carboxymethyl chitosan is 4:1.
[0079] The preparation method of the quick-acting hemostatic gauze for promoting wound healing comprises the steps:
[0080] (1) Sodium carboxymethyl cellulose and xanthan gum are mixed to obtain mixture A;
[0081] (2) α-n-octyl cyanoacrylate, lauroyl sulfate deacetylated chitosan, propyl p-hydroxybenzoate and methyl p-hydroxybenzoate are at a temperature of 150°C and a stirring rate of 150r / min Stirring and mixing for 50 min to obtain mixture B;
[0082] (3) Stir and mix the mixture A prepared in step (1) and the mixture B prepared in step (2) for 20 minutes at a temperature ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com