A technology of C-276 and Hastelloy, which is applied in the field of metal forging technology, can solve the problems that affect the production progress and yield of materials, the small forging temperature window, and reduce the thermoplasticity of materials, so as to improve production and processing efficiency, save forging time, Eliminate the effect of forging cracking

Active Publication Date: 2021-02-12
HEBEI IRON AND STEEL
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Hastelloy C-276 has a broad application market, but its production is severely limited, one of the important factors is the hot working of Hastelloy C-276
During the hot forging process of Hastelloy C-276, due to the small forging temperature window, the optimum temperature range is 1000-1150 °C. When the temperature is lower than this temperature range, precipitated phases will be rapidly generated at the grain boundaries, resulting in grain Boundary brittleness, reducing the thermoplasticity of the material, a little carelessness, there will be forging cracking, which seriously affects the production progress and yield of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Forging Process of Hastelloy C-276
  • A Forging Process of Hastelloy C-276
  • A Forging Process of Hastelloy C-276

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: The forging process of the Hastelloy C-276 is specifically as follows.

[0024] (1) Hastelloy C-276 electroslag casting ingot, the size is Φ300×500mm, the composition is (wt): Fe 5.32%, Cr16.23%, Mo 16.45%, W 3.83%, Mn 0.53%, C 0.008% , Si 0.03%, P 0.004%, S 0.003%, and the balance is Ni.

[0025] (2) First, heat treat Hastelloy C-276. The original temperature of the heating furnace is 36°C. Set the program to raise the temperature to 1000°C at a heating rate of 300°C / h and keep it for 1 hour; then raise the temperature to 100°C / h. 1100°C, keep warm for 15 hours, and air cool after taking out the oven. Before forging, put the Hastelloy C-276 into the heating furnace in front of the forging press for heating, raise the temperature to 1000℃ at a heating rate of 300℃ / s, and keep it for 1h; then raise it to 1150℃ at a heating rate of 100℃ / s, and keep it Start forging after 5h.

[0026] (3) Turn on the temperature replenishing device during forging, and spra...

Embodiment 2

[0028] Example 2: The forging process of the Hastelloy C-276 is as follows.

[0029] (1) Cast Hastelloy C-276, size 150×150×300mm, composition (wt): Fe 5.49%, Cr 15.88%, Mo 15.85%, W 3.73%, Mn 0.50%, C 0.006% , Si 0.05%, P 0.005%, S 0.005%, and the balance is Ni.

[0030] (2) Use a heating furnace to heat-treat the material. The original temperature of the heating furnace is 53°C. Set the program to raise the temperature to 990°C at a heating rate of 250°C / h and keep it for 1.5h; then raise the temperature to 1110°C at 80°C / h , keep warm for 15.5 hours, take out the oven and air cool. Before forging, put the Hastelloy C-276 into the heating furnace before the forging press for heating, raise the temperature to 1010°C at a heating rate of 200°C / s, and keep it for 1.2h; then raise the temperature to 1160°C at a heating rate of 90°C / s, Start forging after 5.5 hours of heat preservation.

[0031] (3) Turn on the temperature replenishing device during forging, spray nozzles from...

Embodiment 3

[0033]Embodiment 3: The forging process of the Hastelloy C-276 is as follows.

[0034] (1) As-cast Hastelloy C-276, the billet size is 150×150×260mm, the composition is (wt): Fe 5.69%, Cr16.03%, Mo 16.12%, W 3.92%, Mn 0.55%, C 0.008 %, Si 0.06%, P 0.004%, S 0.003%, and the balance is Ni.

[0035] (2) Use a heating furnace to heat-treat the material. The original temperature of the heating furnace is 73°C. Set the program to raise the temperature to 1010°C at a heating rate of 200°C / h and keep it for 1.2h; then raise the temperature to 1080°C at 90°C / h , keep warm for 16 hours, take out the oven and air cool. Before forging, put the Hastelloy C-276 into the heating furnace before the forging press for heating, raise the temperature to 1020°C at a heating rate of 250°C / s, and keep it for 1.3h; then raise the temperature to 1155°C at a heating rate of 80°C / s, Start forging after 6 hours of heat preservation.

[0036] (3) Turn on the temperature compensation device during forgi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a forging process of Hastelloy C-276, which includes pre-forging heat treatment, heating and forging process; the pre-forging heat treatment process is as follows: the alloy material is heated to 980°C-1020°C and kept for 1-1.5h ; heat up to 1080°C-1120°C again, keep warm for 15-16h; leave the furnace and air cool; the heating process is: heat up the alloy material to 980°C-1020°C, keep warm for 1-1.5h; then heat up to 1140°C-1160°C, keep warm 5 to 6 hours; the forging process: adopt multi-fire forging, use the temperature compensation device of the forging press to heat during forging, and control the final forging temperature of each fire to be 1000° C. or above. Through the heat treatment process, this process can dissolve the precipitated phase in Hastelloy C-276, reduce the brittle phase of the grain boundary, and eliminate the forging crack caused by the weakening of the grain boundary; Compensation, prolonging the residence time of the blank in the forging temperature range, thereby increasing the forging time of each fire.

Description

technical field [0001] The invention relates to a metal forging process, in particular to a Hastelloy C-276C forging process. Background technique [0002] As an important member of nickel-based alloy, Hastelloy C-276C has super corrosion resistance because it contains a large amount of nickel, chromium, molybdenum and tungsten elements, and has strong corrosion resistance in oxidizing and reducing media Ability, while taking into account good mechanical properties, known as the "king of corrosion resistance". Hastelloy C-276 is suitable for corrosive environments in many fields such as chemical manufacturing, power plant flue gas desulfurization, papermaking, and marine; therefore, it is also known as one of the most widely used nickel-based corrosion-resistant alloys. Hastelloy C-276 has a broad application market, but its production is severely limited, one of the important factors is the hot working of Hastelloy C-276. During the hot forging process of Hastelloy C-276,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21J1/06B21J5/00B21K29/00
CPCB21J1/06B21J5/00B21K29/00
Inventor 赵英利张雲飞嵇爽韩彦光陈文王学慧
Owner HEBEI IRON AND STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap