Adhesive and preparation method thereof

A technology of adhesives and adhesive resins, applied in the direction of adhesive types, mineral oil hydrocarbon copolymer adhesives, non-polymer adhesive additives, etc., can solve the problem of poor adhesion of adhesives, adhesion Excessive fluidity of the agent, falling off of the noise absorber, etc., to achieve the effects of prolonging the service life, good adhesion, and improving quality

Active Publication Date: 2019-08-16
GITI RADIAL TIRE (ANHUI) CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, the adhesives commonly used in tires have poor adhesion performance. When the inner surface of the tire adheres to the noise absorber, the noise absorber will fall off after a short period of time. Moreover, The fluidity of commonly used adhesives is either too large or too small, which is not convenient for adhesion operation. Therefore, in order to solve the problems of poor adhesive adhesion and inconvenient adhesion operation, there is an urgent need for an adhesive that can satisfy the above two conditions at the same time. Adhesives for use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive and preparation method thereof
  • Adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A kind of adhesive, described adhesive comprises the component of following mass parts:

[0045] Rubber compound 168.55phr

[0046] Adhesive resin 25-40phr

[0047] Gasoline 250-450phr

[0048] Wherein said rubber compound comprises the component of following mass parts:

[0049] Butyl rubber 100phr

[0050] N660 50phr

[0051] Other systems 18.55phr.

[0052] The butyl rubber is halogenated butyl rubber, and the halogenated butyl rubber is one or more of chlorinated butyl rubber or brominated butyl rubber.

[0053] Such other systems include activators, vulcanizing agents, accelerators, and scorch retarders.

[0054] The binder resin is at least one of hydrocarbon resin, terpene resin and indene resin.

[0055] The gasoline is one of No. 93 gasoline, No. 97 gasoline and No. 120 gasoline; No. 120 gasoline is preferred for gasoline.

[0056] The viscosity of the adhesive at room temperature is 20000-40000 centipoise.

[0057] For details, see Table 1 below:

[...

Embodiment 2

[0070] A method for preparing an adhesive, comprising the steps of:

[0071] S1. Preparation of mixed rubber in M1 section

[0072] (1) Start the internal mixer to preheat, then take 2 / 3 of 50phrN660 and 100phr butyl rubber into the preheated internal mixer, press the top bolt of the internal mixer for 60s, and then lift the top bolt 10s;

[0073] In (1) of the step S1, before adding the N660 and butyl rubber, it is necessary to adjust the rotational speed of the internal mixer to 40 r / min. (2) Add the remaining 1 / 3 of 50phrN660, press the top bolt of the internal mixer for 30s, and then lift the top bolt for 10s;

[0074] (3) Finally, when the top bolt is pressed for 90s or the temperature reaches 145°C, the rubber is discharged to obtain the mixed rubber of the M1 stage;

[0075] Before weighing N660 and butyl rubber, start the internal mixer for preheating. During the preheating process of the internal mixer, the weighing and proportioning of N660 and butyl rubber can be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an adhesive and a preparation method thereof. The adhesive comprises the following ingredients (by mass): 168.55 phr of a rubber compound, 25-40 phr of bonding resin and 250-450 phr of gasoline. The rubber compound comprises the following ingredients (by mass): 100 phr of butyl rubber, 50 phr of N660 and 18.55 phr of other systems. According to the invention, the rubber compound, bonding resin and gasoline are adopted, and the mass ratio of the rubber compound to bonding resin to gasoline is strictly controlled within the range of 1:0.15-0.24: 1.48-2.67. Thus, it can beensured that fluidity of the prepared adhesive is appropriate and viscosity of the adhesive at room temperature is within the range of 20,000-40,000 centipoises. In addition, when the prepared adhesive is in use, the curing time as required is proper, the adhesive effect is good, and the adhesive can meet the use requirement.

Description

technical field [0001] The invention relates to the technical field of adhesives, in particular to an adhesive and a preparation method thereof. Background technique [0002] At present, the adhesive used for tire bonding needs to comprehensively consider the movement of the tire during use and the adhesive effect of the adhesive itself. Considering that during the driving process of the tire, its adhesion part will undergo continuous and repeated deformation as the tire runs. When it is necessary to adhere inside the tire, it is necessary to consider the firmness and durability of the adhesion. [0003] In the prior art, the adhesives commonly used in tires have poor adhesion performance. When the inner surface of the tire adheres to the noise absorber, the noise absorber will fall off after a short period of time. Moreover, The fluidity of commonly used adhesives is either too large or too small, which is not convenient for adhesion operation. Therefore, in order to solve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/28C09J157/02C09J145/00C09J11/04
CPCC08L2205/025C08L2205/035C09J11/04C09J123/283C08L57/02C08L45/00C08K3/04
Inventor 陈玲卢荣丽李宁学云雨
Owner GITI RADIAL TIRE (ANHUI) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap