Multifunctional lubricating oil additive and application thereof

A lubricating oil additive, multi-functional technology, applied in the directions of additives, lubricating compositions, petroleum industry, etc., can solve the problems of inability to meet the use requirements, single function of lubricating oil additives, etc., to improve anti-wear and extreme pressure, enhance mutual effect of action

Active Publication Date: 2019-11-08
广东顺德菲尔特润滑科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing lubricating oil additives have relatively single functions and cannot meet the requirements for use in extremely harsh environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional lubricating oil additive and application thereof
  • Multifunctional lubricating oil additive and application thereof
  • Multifunctional lubricating oil additive and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of multifunctional lubricating oil additive, described additive is made up of the raw material of following parts by weight:

[0034] 50 parts of morpholine ionic liquid;

[0035] 0.8 parts of detergent;

[0036] 1.2 parts of antirust agent;

[0037] Antioxidant 7 parts; and

[0038] Foam inhibitor 0.2 parts.

[0039] The morpholine ionic liquid has the following structural formula:

[0040]

[0041] Among them, Y - from BF 4- .

[0042] The preparation method of described morpholine ionic liquid is as follows:

[0043] Step S1: After mixing 2,2-dimethyl-3-vinylcyclopropanecarbonyl chloride and 2,6-dimethyl-4-(4-morpholinylmethyl)phenol in a molar ratio of 1.05:1 Microwave radiation was heated for 1 min, and then stirred for 3 min to obtain chlorinated 2,2-dimethyl-3-vinylcyclopropanecarbonyl-2,6-dimethyl-4-(4-morpholinomethyl)phenol;

[0044] Step S2: the chlorinated 2,2-dimethyl-3-vinylcyclopropanecarbonyl-2,6-dimethyl-4-(4-morpholinomethyl)phenol a...

Embodiment 2

[0053] A kind of multifunctional lubricating oil additive, described additive is made up of the raw material of following parts by weight:

[0054] 80 parts of morpholine ionic liquid;

[0055] 3.5 parts of detergent;

[0056] 1.8 parts of antirust agent;

[0057] Antioxidant 12 parts; and

[0058] Foam inhibitor 1.6 parts.

[0059] Preferably, the morpholine ionic liquid has the following structural formula:

[0060]

[0061] Among them, Y - from PF 6- .

[0062] The preparation method of described morpholine ionic liquid is as follows:

[0063] Step S1: After mixing 2,2-dimethyl-3-vinylcyclopropanecarbonyl chloride and 2,6-dimethyl-4-(4-morpholinylmethyl)phenol at a molar ratio of 1.1:1 Microwave radiation was heated for 3 minutes, and then stirred for 8 minutes to obtain chlorinated 2,2-dimethyl-3-vinylcyclopropanecarbonyl-2,6-dimethyl-4-(4-morpholinomethyl)phenol;

[0064] Step S2: the chlorinated 2,2-dimethyl-3-vinylcyclopropanecarbonyl-2,6-dimethyl-4-(4-morphol...

Embodiment 3

[0073] A kind of multifunctional lubricating oil additive, described additive is made up of the raw material of following parts by weight:

[0074] 100 parts of morpholine ionic liquid;

[0075] 7.5 parts of detergent;

[0076] 2.6 parts of antirust agent;

[0077] Antioxidant 16 parts; and

[0078] Foam inhibitor 3.8 parts.

[0079] Preferably, the morpholine ionic liquid has the following structural formula:

[0080]

[0081] Among them, Y - from BF 4- .

[0082] The preparation method of described morpholine ionic liquid is as follows:

[0083] Step S1: After mixing 2,2-dimethyl-3-vinylcyclopropanecarbonyl chloride and 2,6-dimethyl-4-(4-morpholinylmethyl)phenol in a molar ratio of 1.2:1 Microwave radiation was heated for 5 minutes, and then stirred for 10 minutes to obtain chlorinated 2,2-dimethyl-3-vinylcyclopropanecarbonyl-2,6-dimethyl-4-(4-morpholinomethyl)phenol;

[0084] Step S2: the chlorinated 2,2-dimethyl-3-vinylcyclopropanecarbonyl-2,6-dimethyl-4-(4-mor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional lubricating oil additive. The multifunctional lubricating oil additive is prepared from the following raw materials in part by weight: 50-100 parts of morpholine ionic liquid, 0.8-7.5 parts of a clearing agent, 1.2-2.6 parts of an antirust agent, 7-16 parts of an antioxidant and 0.2-3.8 parts of a foam inhibitor. The multifunctional lubricating oil additive is applied to a steel / steel or steel / aluminum friction pair, thus the antifriction and abrasion-resistant performance of the lubricating oil additive in the friction pair is significantly improved,meanwhile, the extreme pressure bearing performance of the lubricating oil additive is improved, and the friction pair is small in loss and long in service life.

Description

technical field [0001] The invention relates to the technical field of additives, in particular to a multifunctional lubricating oil additive and its application. Background technique [0002] The operation of equipment is inseparable from lubricating oil additives, and lubricating oil cannot be separated from lubricating oil additives. Lubricating oil additives are the essence of various modern high-grade lubricating oils. According to statistics, about 30% of energy consumption is on friction, and 70% of damaged parts are scrapped by wear and tear. Therefore, improving lubricating performance to reduce friction, wear and prevent sintering is of great significance to the national economy. Additives commonly used in lubricating oil are divided into antioxidants, anti-wear agents, friction modifiers (also known as oily agents), extreme pressure additives, detergents, dispersants, foam inhibitors, anti-corrosion and anti-rust agents, and flow point improvement. Additives, vi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M167/00C10M133/50C07D295/185C10N30/06C10N30/04C10N30/10C10N30/12
CPCC10M167/00C10M133/50C07D295/185C10M2215/226C10M2215/28C10M2219/044C10M2207/046C10M2209/104C10M2209/108C10M2215/066C10M2201/087C10N2030/04C10N2030/10C10N2030/43C10N2030/42C10N2030/45C10N2030/56C10N2030/72C10N2030/64C10N2030/12C10N2030/06C10N2010/04C10N2060/14C10N2020/04
Inventor 徐武警
Owner 广东顺德菲尔特润滑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com