Ferromagnetic material, preparation method thereof and sensor

A ferromagnetic material and sensor technology, applied in the field of materials, can solve the problems of complex preparation methods, difficult preparation, and low quality of two-dimensional metallic ferromagnetic materials

Active Publication Date: 2019-12-17
TSINGHUA UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Based on this, it is necessary to provide a fer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ferromagnetic material, preparation method thereof and sensor
  • Ferromagnetic material, preparation method thereof and sensor
  • Ferromagnetic material, preparation method thereof and sensor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] In order to make the object, technical solution and advantages of the present invention clearer, the ferromagnetic material, its preparation method and sensor of the present invention will be further described in detail below with reference to the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0032] In the embodiment of the present application, a ferromagnetic material is provided. The structural formula of the ferromagnetic material is A 3 B 3 o 8 , wherein A is one or more of alkaline earth metal elements and rare earth metal elements. B is one or more transition group metal elements. The ferromagnetic material is a two-dimensional metallic oxide material. The alkaline earth metal includes one or more of Be, Mg, Ca, Sr, Ba. The rare earth metal elements include one or more of La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, H...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Resistivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a ferromagnetic material. The structural formula of the ferromagnetic material is A3B3O8, wherein A is one or more of alkaline earth metal elements and rare earth metal elements; B is one or more of transition metal elements, and the ferromagnetic material is a two-dimensional metallic oxide material. The ferromagnetic material is stable in structure and high in crystallization quality and has two-dimensional ferromagnetic metal characteristics. The ferromagnetic material has obvious magnetic anisotropy at a low temperature. The ferromagnetic transition temperature ofthe ferromagnetic material is about 200K. The ferromagnetic material has a quasi-two-dimensional conductivity characteristic along an in-plane direction. The ferromagnetic material can be widely applied to the field of electromagnetic sensors.

Description

technical field [0001] The invention relates to the field of materials, in particular to a ferromagnetic material, a preparation method thereof, and a sensor. Background technique [0002] Most of the material structures in nature are three-dimensional, and the magnetic and electrical properties of materials are therefore mostly three-dimensional. The in-plane and out-of-plane directions of materials with three-dimensional properties do not have a significant difference. Under certain conditions, on the surface of a three-dimensional material or the interface of two three-dimensional materials, a two-dimensional magnetic layer or a special electronic state different from that of the bulk material will be formed. For example, on the surface of a three-dimensional topological insulator, LaAlO 3 / SrTiO 3 The bulk state of the heterojunction interface is an insulator, and the surface or interface is a two-dimensional metallic state. while LaAlO 3 / SrTiO 3 At the same time,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F1/34H01F41/02G01R33/10G01R33/09
CPCG01R33/093G01R33/096G01R33/10H01F1/342H01F41/0273G01R33/09H01F1/34H01F41/02
Inventor 于浦张建兵王猛
Owner TSINGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap