Coating technology

A coating process and coating technology, applied in covering/lining, construction, building construction, etc., can solve the problems of high cost, poor material quality and performance, waterproof and short durability, and achieve cost-saving effect.

Inactive Publication Date: 2020-02-11
广东立盈新材料有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cost of traditional interior renovation is high, the construction period is long, and it is easy to cause damage to the substrate, and the quality and performance of the repaired material are not good, the waterproof and durable time is extremely short, and the decorative effect is extremely poor
Especially in small places such as bathrooms and kitchens, it is difficult for the owner to find a construction unit for repair work

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating technology
  • Coating technology
  • Coating technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Embodiment 1: the preparation of aqueous cleaning agent

[0069] Take 40 parts of alumina micropowder, 60 parts of water, 0.3 parts of BYK-346, 0.7 parts of BYK-425, add the above materials in sequence, and stir evenly, the speed is controlled at about 500 rpm, and the time is controlled at about 5 minutes. Get an aqueous cleaner.

[0070] Take 30 parts of alumina micropowder, 70 parts of water, 0.1 part of BYK-346, 0.5 part of BYK-425, add the above materials in sequence, and stir evenly, the speed is controlled at about 500 rpm, and the time is controlled at about 5 minutes. Get water-based cleaning agent 2.

[0071] Take 50 parts of alumina micropowder, 50 parts of water, 0.5 part of BYK-346, and 1 part of BYK-425, add the above materials in sequence, and stir evenly, the speed is controlled at about 500 rpm, and the time is controlled at about 5 minutes. Get water-based cleaning agent 3.

Embodiment 2

[0072] Embodiment 2: the preparation of interface agent

[0073] Take 25 parts of nano-silicone resin, 75 parts of edible alcohol, 0.3 parts of Tego-245, 0.3 parts of Tego-410, add the above materials in sequence, and stir evenly. The speed is controlled at about 700 rpm and the time is controlled at about 5 minutes. Interface agent 1 was prepared.

[0074] Take 20 parts of nano-silicone resin, 80 parts of edible alcohol, 0.2 parts of Tego-245, 0.2 parts of Tego-410, add the above materials in sequence, and stir evenly. The speed is controlled at about 700 rpm and the time is controlled at about 5 minutes. Interface agent 2 is prepared.

[0075] Take 30 parts of nano-silicone resin, 70 parts of edible alcohol, 0.5 parts of Tego-245, 0.5 parts of Tego-410, add the above materials in sequence, and stir evenly, the speed is controlled at about 700 rpm, and the time is controlled at about 5 minutes. The interface agent 3 is prepared.

Embodiment 3

[0076] Embodiment 3: the preparation of waterborne two-component waterproof primer

[0077] Take 50 parts of water-based epoxy resin, 50 parts of water-based color paste, 0.3 parts of BYK-346, 0.3 parts of BYK-333, 0.1 part of BYK-028, and add them to the mixing tank in turn, and stir for 20 minutes according to the stirring speed of 600 rpm , A water-based two-component waterproof primer was prepared.

[0078] Take 40 parts of water-based epoxy resin, 60 parts of water-based color paste, 0.3 parts of BYK-346, 0.3 parts of BYK-333, 0.1 part of BYK-028, add them to the mixing tank in turn, and stir for 20 minutes at a stirring speed of 800 rpm , to prepare water-based two-component waterproof primer II.

[0079] Take 60 parts of water-based epoxy resin, 40 parts of water-based color paste, 0.3 parts of BYK-346, 0.3 parts of BYK-333, and 0.1 part of BYK-028, and add them to the mixing tank in turn, and stir for 20 minutes at a stirring speed of 700 rpm , to prepare a water-bas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a coating technology used for surface water preventing and renovating of surfaces of glazed tiles and other building materials. The coating technology comprises the following steps that firstly, the surface of a raw building material is cleaned and ground, and the surface roughness is increased; secondly, coating of an interface agent is conducted; thirdly, coating of waterproof primer is conducted; fourthly, coating of a non-solvent ultraviolet light curing finishing coat is conducted, ultraviolet light irradiation curing is conducted, and a new surface is obtained; and the building material is glazed tiles, stone, glass, metal or wood products. The coating technology has the characteristics of being waterproof, firm in bonding, good in decoration effect, free of noise in the construction process, high in renovating speed and the like; and good adhesive force is achieved for tile glaze faces / polished faces, technology patterns can be customized, the surface decoration effect is further improved, and the personalized new decorating effect is achieved.

Description

technical field [0001] The invention relates to the field of building decoration, in particular to a coating process for waterproofing the surface of building materials such as glazed tiles, stone, glass, metal, and wood products. Background technique [0002] With the advancement of science and technology and the rapid development of my country's economy, people's requirements for the living environment of residents in the construction field are gradually increasing. At present, in addition to high-end residential areas and emerging buildings in my country, the protection and renovation of walls, floors and countertops in most residential buildings has always been a concern of people. In the prior art, the protection and refurbishment of indoor walls, floors and countertops (glazed ceramic tiles, stone or other materials) basically all redecorate after smashing bricks, or directly discard them. The cost of traditional interior renovation is high, the construction period is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/02
CPCE04F13/02
Inventor 程金玉
Owner 广东立盈新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com