Aluminum alloy plate for battery cover for forming integrated explosion-proof valve and manufacturing method thereof

A technology of aluminum alloy plate and manufacturing method, applied in the direction of battery cover/end cover, battery, metal rolling, etc., can solve the problem of valve automatic fracture, etc., and achieve the characteristics of small working pressure deviation, excellent processing softening property, and resistance to repeated fatigue excellent effect

Active Publication Date: 2021-10-22
NIPPON LIGHT METAL CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The explosion-proof valve must work reliably, and the valve will automatically break when the internal pressure of the container exceeds the specified pressure, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy plate for battery cover for forming integrated explosion-proof valve and manufacturing method thereof
  • Aluminum alloy plate for battery cover for forming integrated explosion-proof valve and manufacturing method thereof
  • Aluminum alloy plate for battery cover for forming integrated explosion-proof valve and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0103]

[0104] 〔Preparation of test materials〕

[0105] 5 kg of ingots with component compositions of 16 levels (Examples 1-6, Comparative Examples 1-10) were inserted into No. 20 crucibles, and the crucibles were heated in a small electric furnace to melt the ingots. Next, insert a spray gun into the melt, and feed N at a flow rate of 1.0 L / min. 2 The gas was degassed for 5 minutes. Thereafter, it was allowed to rest for 30 minutes, and dross floating to the surface of the melt was removed with a stirring bar. Then, the crucible was taken out from the small electric furnace, the melt was poured into a mold with an inner size of 250×200×30 mm to make an ingot, and the melts of Examples 1 to 6 and Comparative Examples 1 to 10 were obtained from the melt in each crucible. Each test material. The disc samples of these test materials were analyzed for composition by emission spectroscopic analysis. The results are shown in Table 1.

[0106] [Table 1]

[0107] [Composition...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention provides an aluminum alloy plate for a battery cover and a method for producing the same. The aluminum alloy plate for a battery cover is an aluminum alloy plate for a battery cover that has moderate strength and is excellent in formability and work softening property, and can be formed into variations in operating pressure. An integral explosion-proof valve that is small and has excellent resistance to repeated fatigue. An aluminum alloy plate for a battery cover for forming an integrated explosion-proof valve is characterized in that it has the following composition: 1.05 to 1.50 mass % of Fe, 0.15 to 0.70 mass % of Mn, 0.002 to 0.15 mass % of Ti, and less With 0.03% by mass of B, the rest is composed of Al and impurities, the Fe / Mn ratio is limited to 1.8 to 7.0, Si as impurities is limited to less than 0.40% by mass, Cu is limited to less than 0.03% by mass, and Mg is limited to less than 0.03% by mass. 0.05% by mass, V is limited to less than 0.03% by mass, the tensile strength is above 95MPa, the value of elongation is above 40%, has a recrystallized structure, and will be cold-rolled at a reduction rate of 70%. When the tensile strength is defined as TS70 and the tensile strength after cold rolling at a rolling reduction of 95% is defined as TS95, the value of (TS95-TS70) is less than -1MPa, after cold rolling at a rolling reduction of 90% The elongation value is above 5.0%. More preferably, the average grain size of the recrystallized grains of the recrystallized structure is 15 to 30 μm.

Description

technical field [0001] The present invention relates to an aluminum alloy plate for a battery cover for forming an integrated explosion-proof valve used in square, cylindrical and other lithium-ion batteries and having a small working pressure deviation. Background technique [0002] In recent years, countries have imposed stricter regulations on automobile exhaust, and the production of electric vehicles, which are environmentally friendly vehicles, is rapidly expanding. Currently, the mainstream of secondary batteries used in electric vehicles is lithium-ion batteries. Lithium-ion battery casings come in various types such as square, cylindrical, and sheet-shaped. In the case of square and cylindrical shapes, aluminum alloy plates that can achieve weight reduction are drawn and processed. Or a shell obtained by thinning and deep drawing processing (also called DI processing). [0003] Thus, as a material for a battery case, development of an aluminum alloy plate having e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22F1/04H01M50/159H01M50/152H01M50/30C22F1/00H01M50/147
CPCC22F1/04C22C21/00Y02E60/10H01M50/3425H01M50/147B21B1/24B21B37/74H01M2200/20H01M50/159
Inventor 玉置雄一金森圭治下坂大辅穴见敏也
Owner NIPPON LIGHT METAL CO LTD
Who we serve
  • R&D Engineer