6-series aluminum alloy automotive outer panel with excellent comprehensive performance and preparation method thereof

A comprehensive performance and aluminum alloy technology, which is applied in the field of 6-series aluminum alloy automobile outer panels and its preparation, can solve the problems affecting the large-scale application of automobile body outer panels, the surface quality, formability and paint strength performance of 6-series aluminum alloy sheets Can not take into account other issues, to achieve the effect of speeding up the lightweight process and improving the texture distribution

Active Publication Date: 2021-11-09
TIANJIN ZHONGWANG ALUMINUM IND CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention provides a 6-series aluminum alloy sheet with excellent comprehensive performance in order to solve the problem that the surface quality, formability and paint strength performance of the 6-series aluminum alloy sheet prepared by the existing technology cannot be taken into account, which affects the large-scale application of the outer panel of the automobile body. Preparation method of aluminum alloy automobile outer panel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 6-series aluminum alloy automotive outer panel with excellent comprehensive performance and preparation method thereof
  • 6-series aluminum alloy automotive outer panel with excellent comprehensive performance and preparation method thereof
  • 6-series aluminum alloy automotive outer panel with excellent comprehensive performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0030] Such as figure 1 Shown is a preparation method for a 6-series aluminum alloy automobile outer panel, comprising the steps of:

[0031] A. The aluminum alloy raw material for preparing the outer panel of the automobile body is batched according to the weight percentage, and the mass percentage ratio of each element of the aluminum alloy raw material is as follows:

[0032] element Si Fe Cu mn Mg Cr Zn Impurities Al content 1.05 0.30 0.45 0.13 0.35 0.10 0.10 0.05 margin

[0033] Aluminum alloy raw materials are industrial pure aluminum, industrial pure Mg, industrial pure Zn, intermediate alloy Al-Si, intermediate alloy Al-Cu, intermediate alloy Al-Fe, intermediate alloy Al-Mn, etc., and the prepared aluminum alloy raw materials are placed in It is melted into liquid aluminum alloy in the melting furnace, and melted in the melting furnace at a temperature range of 700-760 °C. During the melting process, electromagnetic stirrin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of aluminum alloy plates for automobile bodies, and relates to a preparation method of a 6-series aluminum alloy automobile outer plate with excellent comprehensive performance, which is prepared from the following element components according to weight percentage: Si: 0.6-1.5%, Fe: 0.1~0.5%, Cu: 0.3~0.6%, Mn: 0.05~0.20%, Mg: 0.25~0.45%, Cr≤0.1%, Zn≤0.1%, single impurity≤0.03%, total impurity≤0.10%, balance It is Al, and its preparation method is to obtain a specific deformation texture structure by controlling the hot rolling reduction and the final rolling temperature, and then combine with the subsequent two annealing processes and appropriate cold rolling passes to finally obtain an excellent comprehensive performance. The 6-series aluminum alloy material is superior to the commonly used 6016 automotive sheet in terms of formability, paint strengthening performance, and surface quality.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy plates for automobile bodies, and relates to a preparation method of a 6-series aluminum alloy automobile outer panel with excellent comprehensive performance, in particular to a 6-series aluminum alloy automobile with excellent surface quality, formability and paint strength performance Outer panel and method for preparing the same. Background technique [0002] Under the current theme of energy saving and emission reduction, automobile lightweight is the most direct and effective way to reduce pollution and reduce consumption. Aluminum alloy and its processing materials have become the main application of automobile manufacturers to reduce vehicle weight due to a series of excellent characteristics such as low density, high specific strength and specific stiffness, good elasticity, good impact resistance, corrosion resistance and good processing performance Material. [0003] The alumin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02C22C1/03C22C1/06C22F1/043
CPCC22C1/026C22C1/03C22C1/06C22C21/02C22F1/043
Inventor 冉凡青王飞祖立成崔立治张旭鹏白永芳李玉博
Owner TIANJIN ZHONGWANG ALUMINUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products