Controlled rolling and cooling method for improving sulfide form of easy-cutting steel wire rod

A technology of controlled rolling and controlled cooling, steel wire rod, applied in temperature control, metal rolling, etc., can solve problems such as steel holding, and achieve the effect of ensuring normal rolling, reducing the number of accidents, and reducing the number

Active Publication Date: 2021-02-26
ZENITH STEEL GROUP CORP +1
View PDF16 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] In order to solve the problems in the background technology, the object of the present invention is to provide a controlled rolling and controlled cooling method for improving the sulfide form of free-cutting steel wire rods. The present invention chooses to heat and roll at a lower temperature, which can not only effectively avoid The hot-brittle temperature range of free-cutting steel wire rod solves the problem of steel holding due to splitting during the rolling process of free-cutting steel wire rod, ensures the normal rolling of free-cutting steel wire rod, and effectively inhibits the sulfide from rolling with the billet. The phenomenon of being elongated during the molding process effectively reduces the number of long strips of sulfide, improves the cutting efficiency of downstream users and the service life of cutting tools

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Controlled rolling and cooling method for improving sulfide form of easy-cutting steel wire rod
  • Controlled rolling and cooling method for improving sulfide form of easy-cutting steel wire rod
  • Controlled rolling and cooling method for improving sulfide form of easy-cutting steel wire rod

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] 1. Billet heating:

[0060] Slab composition C: 0.08%, Si: 0.02%, Mn: 1.32%, P: 0.08%, S: 0.40%, Cr: 0.10%, Ni: 0.06%, Cu: 0.02%.

[0061] The continuous casting billet with a section of 160mm*160mm is heated at a temperature of 760-945°C for 3.8 hours, wherein the heating temperature of the preheating section is 760-845°C, the heating temperature of the heating section is 930-945°C, and the heating temperature of the soaking section is 870-900°C.

[0062] 2. Controlled rolling

[0063] The starting temperature of rough rolling is 837-850°C. The head of the rolled piece after rough rolling is heated by an online burner and then enters the middle rolling unit for rolling. The rolling temperature of the middle rolling unit is 832-841°C. After the rolling in the intermediate rolling group, the rolled pieces enter the pre-finishing rolling group for rolling, and the rolling temperature of the pre-finishing rolling group is 838-850°C. The rolled piece rolled by the pre-fin...

Embodiment 2

[0070] 1. Billet heating:

[0071] Slab composition C: 0.05%, Si: 0.07%, Mn: 1.18%, P: 0.05%, S: 0.35%, Cr: 0.07%, Ni: 0.03%, Cu: 0.03%.

[0072] The continuous casting billet with a section of 160mm*160mm is heated at 755-935°C for 3.2 hours, wherein the heating temperature of the preheating section is 761-828°C, the heating temperature of the heating section is 920-935°C, and the heating temperature of the soaking section is 860-896°C.

[0073] 2. Controlled rolling

[0074] The starting temperature of rough rolling is 831-841°C. The head of the rolled piece after rough rolling is heated by an online burner and then enters the middle rolling unit for rolling. The rolling temperature of the middle rolling unit is 830-839°C. After the rolling in the intermediate rolling group, the rolled pieces enter the pre-finishing rolling group for rolling, and the rolling temperature of the pre-finishing rolling group is 836-849°C. The rolled piece rolled by the pre-finishing rolling gr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of rolling, and relates to a controlled rolling and cooling method for improving a sulfide form of an easy-cutting steel wire rod. The controlled rolling and cooling method comprises the following steps: heating steel billets for 3-4 hours at a temperature not higher than 950 DEG C; performing rolling at a temperature not higher than 850 DEG C by a rough rolling unit, a finish rolling unit and a pre-finish rolling unit; spinning the rolled wire rod into a ring through a spinning machine; and performing controlled cooling on the spun wire rod througha Stelmor controlled cooling line. According to the process, the hot brittleness temperature interval of the easy-cutting steel wire rod is effectively avoided, the problem of steel building caused by head splitting in the rolling process of the easy-cutting steel wire rod is solved, normal rolling of the easy-cutting steel wire rod is guaranteed, the phenomenon that sulfide is lengthened in thebillet rolling forming process is restrained, the number of long-strip-shaped sulfides is effectively reduced, and cutting and processing efficiency of downstream users is improved, and the service life of a cutting tool is prolonged. Meanwhile, compared with a traditional high-temperature rolling process, energy consumption is reduced, the service life of a steel rolling roll ring is prolonged, and accidents of a high-speed rolling mill are reduced.

Description

technical field [0001] The invention belongs to the technical field of rolling, and relates to a controlled rolling and controlled cooling method for improving the form of sulfides in free-cutting steel wire rods. Free-cutting steel wire rod production process that improves tool life while reducing energy consumption. Background technique [0002] Free-cutting steel refers to the alloy steel that adds a certain amount of one or more than one kind of free-cutting elements such as sulfur, phosphorus, lead, calcium, selenium and tellurium to the steel to improve its machinability. With the automation, high speed and precision of cutting processing, it is very important to require good machinability of steel. This kind of steel is mainly used for processing on automatic cutting machine tools, so it is also a special steel. [0003] With the development of modern industry towards automation, high-speed and precision processing, steel is required to have good cutting process perf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B21B1/22B21B37/74C22C38/02C22C38/04C22C38/42C22C38/60
CPCB21B1/22B21B37/74C22C38/02C22C38/04C22C38/002C22C38/60C22C38/42B21B2001/225
Inventor苏振伟周淼
OwnerZENITH STEEL GROUP CORP