Positive plate and lithium ion battery
A technology of positive electrode sheet and positive active material, which is applied in the field of positive electrode sheet and lithium-ion battery, can solve problems such as battery damage, and achieve the effect of avoiding battery damage and improving safety
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0059] Example 1:
[0060] A aluminum foil having a thickness of 10 microns is used as the positive electrode concentration fluid, and the positive electrode concentration fluid is a multi-poorer structure. The positive electrode active material coating was obtained by using a positive electrode active substance, a conductive agent, and an adhesive according to 96: 1.5: 2.5. The mixed coating was obtained in accordance with the ceramic and antioxidant component ratio of 7: 3.
[0061] At the first coating region 10 of the positive electrode aggregate, a mixed coating is applied, and the positive electrode active material coating is coated at the second coating region 20 of the positive electrode current collector, wherein the coating device can be used simultaneously on the positive electrode fluid. The first coating region 10 and the second coating region 20 are coated. A mixed coating is applied to the third coating region 31 of the ears 30. Wherein, the width of the first coati...
Example Embodiment
[0065] Example 2:
[0066] The thickness of 10 microns is used as a positive electrode current collector, and the positive electrode current collector is a winding structure. The positive electrode active material coating was obtained by using a positive electrode active substance, a conductive agent, and an adhesive according to 96: 1.5: 2.5. The mixed coating was obtained in accordance with the ceramic and antioxidant component ratio of 7: 3.
[0067] At the first coating region 10 of the positive electrode aggregate, a mixed coating is coated at the second coating region 20 of the positive electrode current collector, wherein the coating device can be used first to the positive electrode fluid. A coating region 10 is coated, and the second coating region 20 of the positive electrode current collector is coated. The width of the first coating region 10 is provided is 105 mm.
[0068] The positive electrode sheet is obtained after drying treatment, roller press treatment, dividin...
Example Embodiment
[0071] Example 3:
[0072] A aluminum foil having a thickness of 10 microns is used as the positive electrode concentration fluid, and the positive electrode concentration fluid is a multi-poorer structure. The positive electrode active material coating was obtained by using a positive electrode active substance, a conductive agent, and an adhesive according to 96: 1.5: 2.5. The mixed coating was obtained in accordance with the ceramic and antioxidant component ratio of 7: 3.
[0073] The second coating region 20 of the positive electrode collector is coated with a positive electrode active material coating, and a mixed coating is coated at the first sub-coating region 11 of the positive electrode current collector, and the second sub-coating region 12 of the positive electrode current collector is applied. The mixed coating is coated with a mixed coating of the positive electrode active material coating and a mixed coating. Among them, the width of the second sub-coating region 1...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap