Waterproof breathable biological soft-shell plaster patch and preparation method thereof

A waterproof and breathable, waterproof and breathable film technology, applied in the field of plasters, can solve the problems of unsatisfactory large-scale industrial production, skin allergies, poor air permeability, etc.

Pending Publication Date: 2022-04-05
深圳市巨印科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In ancient times, when making plasters, substances such as oil and dan were added to form a film, but the production method was only suitable for family workshops and could not meet the needs of large-scale industrial production, so plaster glue appeared.
[0003] However, the traditional plaster glue is a kind of hot melt adhesive. Because of its ultra-high temperature (150-160°C), it is easy to damage the internal structure of the traditional Chinese medicine components, resulting in the failure of the medicine, and the medicine content is only up to 100% of the whole ointment quality. 30 / 30
[0004] In addition, many types of plasters currently do not have good air permeability, resulting in the growth of bacteria on the plasters, which can easily cause problems such as skin allergies. However, most of the breathable films used in the market do not have ideal ventilation effects.
[0005] Patent CN110384586A, Zhu Jiangtao and others invented a chitosan trauma dressing, its structure mainly includes base lining, matrix and anti-adhesive paper, but due to lack of good air permeability, it is easy to cause skin allergies
[0006] Patent CN107929585A, Gao Yu et al. use bamboo vinegar to dissolve chitosan, adjust pH to strong acidity, add emulsifier and vaseline, and make ointment with slow fire. This ointment is adjusted to strong acid system, which is easy to cause skin burns, and chitosan itself After the film is formed, its air permeability is poor, and the skin is corroded or burned, which is more likely to cause problems such as bacterial growth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof breathable biological soft-shell plaster patch and preparation method thereof
  • Waterproof breathable biological soft-shell plaster patch and preparation method thereof
  • Waterproof breathable biological soft-shell plaster patch and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] In order to achieve the above object, the present invention also provides a preparation method of a waterproof and breathable biological soft shell plaster, comprising the following steps:

[0048] The total mass of each plaster base component;

[0049] Step 1: Take about 1.5-2.5g of the film-forming agent propylhydroxytrimethylammonium chloride chitosan in the medicine container, add 1mL of deionized water to stir, and seal it for 30-45min;

[0050] Step 2: Stir the light absorbing agent and dispersing agent evenly according to the ratio of 1:2; bake at a constant temperature of 50-60°C for 30-45min;

[0051] Step 3: Mix the traditional Chinese medicine powder, antioxidant, wetting agent (APG), and antibacterial auxiliary agent in sequence according to equivalent weighing, then stir evenly, then add 1mL deionized water for stirring, and place in ultrasonic wave for 15 minutes;

[0052] Step 4: Mix the above three groups of mixtures again, bake the final mixture in a t...

Embodiment 1

[0067] A kind of plaster, the total mass of each plaster base component:

[0068]

[0069] Operation steps and conditions:

[0070] Step 1: Take 2.5g of the film-forming agent propylhydroxytrimethylammonium chloride chitosan in the medicine container, add 1mL of deionized water to stir, seal and place for 30min;

[0071] Step 2: Stir the light absorbing agent and dispersant evenly according to the above used quality; bake at a constant temperature of 50°C for 30nm;

[0072] Step 3: Mix the traditional Chinese medicine powder, antioxidant, wetting agent, and antibacterial auxiliary agent in sequence according to equivalent weighing, then stir evenly, then add 1mL deionized water for stirring, and shake in ultrasonic wave for 15 minutes;

[0073] Step 4: Mix the above three groups of mixtures again, bake the final mixture in a thermostat at 50°C for 60 minutes, evaporate the water to dryness, and finally prepare a waterproof and breathable biological soft shell plaster.

[...

Embodiment 2

[0076] A kind of plaster, the total mass of each plaster base component:

[0077]

[0078]

[0079] Operation steps and conditions:

[0080] Step 1: Take 1.5g of the film-forming agent propylhydroxytrimethylammonium chloride chitosan in the medicine container, add 1mL of deionized water to stir, seal and place for 45min;

[0081] Step 2: Stir the light absorbing agent and dispersant evenly according to the above used quality; bake at a constant temperature of 50°C for 45 minutes;

[0082] Step 3: Mix the traditional Chinese medicine powder, antioxidant, wetting agent, and antibacterial auxiliary agent in sequence according to equivalent weighing, then stir evenly, then add 1mL deionized water for stirring, and shake in ultrasonic wave for 15 minutes;

[0083] Step 4: Mix the above three groups of mixtures again, bake the final mixture in a thermostat at 50°C for 60 minutes, evaporate the water to dryness, and finally prepare a waterproof and breathable biological soft s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof breathable biological soft shell plaster and a preparation method thereof. The basic structure of the plaster sequentially comprises release paper (6), a waterproof breathable film (5), an air suction layer (4), a base lining (3), a substrate (2) and release paper (1) from outside to inside. The release paper can be peeled off and is used as a plaster shell; the waterproof breathable film is a film made of high-molecular compounds of polyether sulfone and aryl polyether; the air suction layer is an activated carbon powder layer (7) added between the base lining and the waterproof breathable film; the base lining is a non-stick gauze layer; components of the matrix comprise traditional Chinese medicine powder and additives, and the additives comprise a film-forming agent, an antioxidant, a wetting agent, a bacteriostatic auxiliary agent, a light absorbing agent, a dispersing agent and the like. The waterproof breathable biological soft-shell plaster provided by the invention ensures the curative effect of traditional Chinese medicines, has good waterproof and breathable properties, and does not cause allergy and other damages to the skin.

Description

technical field [0001] The invention relates to a waterproof and breathable biological soft shell plaster and a preparation method thereof, belonging to the technical field of plasters. Background technique [0002] External application of traditional Chinese medicine is an important method of traditional Chinese medicine. It has a good effect on healing trauma and even some internal injuries, and it is also one of the easiest and safest methods. In ancient times, when making plasters, substances such as oil and dan were added to form a film, but the production method was only suitable for family workshops and could not meet the needs of large-scale industrial production, so plaster glue appeared. [0003] However, the traditional plaster glue is a kind of hot melt adhesive. Because of its ultra-high temperature (150-160°C), it is easy to damage the internal structure of the traditional Chinese medicine components, resulting in the failure of the medicine, and the medicine c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K9/70A61K47/36A61K47/22A61K47/14A61K47/26A61K47/34A61K47/10A61L9/16B01D53/02A61L101/04
Inventor 魏晶
Owner 深圳市巨印科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products