High-strength cast aluminium alloy material

A casting aluminum alloy, high-strength technology, applied in the field of aluminum alloy materials, can solve the problems of high-cost formula, poor castability, short fatigue life, etc., achieve the effect of reducing formula cost and breaking the technical bottleneck

Inactive Publication Date: 2009-02-11
贵州铝厂有限责任公司 +2
View PDF0 Cites 238 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is aimed at technical problems such as high-cost formula existing in the field of high-strength cast aluminum alloy, low strength, poor castability, short fatigue life, and poor stress corrosion resistance. and other processes, developed a high-strength, high-toughness, high-corrosion-resistant cast aluminum alloy material for military and civilian purposes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength cast aluminium alloy material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0024] Embodiment: By weight percentage, the alloy composition is Cu 2.0-6.0%, Mn 0.05-1.0%, Ti 0.01-0.5%, Cr 0.01-0.2%, Cd 0.01-0.4%, Zr 0.01-0.25%, B 0.005 ~0.04%, Ce 0.05~0.3%, and the rest are Al and trace impurity elements.

[0025] (1) Add an appropriate amount of aluminum ingot or molten aluminum into the melting furnace, heat it to melt it completely and keep it warm at 660-850°C;

[0026] (2) Add Cu and Mn alloy elements according to the formula ratio and stir evenly, then add Ti, Cr, Cd, Zr, B, Ce trace elements, and stir evenly;

[0027] (3) Then carry out in-furnace refining to above-mentioned alloy melt; Add refining agent (can adopt chlorine, hexachloroethane, manganese chloride etc. as refining agent according to different working conditions) in alloy melt, and stir evenly, simultaneously In order to prevent the melt from absorbing moisture and burning, melt refining should be operated in a closed environment as much as possible;

[0028] (4) The alloy liquid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength aluminum casting alloy material which comprises the following components by weight percentages: 2.0-6.0% of Cu, 0.05-1.0% of Mn, 0.01-0.5% of Ti, 0.01-0.2% of Cr, 0.01-0.4% of Cd, 0.01-0.25% of Zr, 0.005-0.04% of B, 0.05-0.3% of Ce, Al and other microimpurity elements. The material adopts the advanced design of alloy components and microalloying design. Based on the Al-Cu-Mn as the major components, rational microalloy elements (the Ti, the Cr, the B, the Zr, mixed rare earth, etc.) are found and the ranges thereof are determined, which can realize the function of substituting the precious rare metals Ag, V, and the like, thus lowering the formula cost by 5-10%.

Description

technical field [0001] The invention relates to an aluminum alloy material, in particular to a high-strength cast aluminum alloy material. Background technique [0002] Aluminum alloy is a relatively young metal material, which only began to be used industrially in the early 20th century. During World War II, aluminum was mainly used in the manufacture of military aircraft. After the war, due to the sharp decrease in the demand for aluminum in the military industry, the aluminum industry began to develop civilian aluminum alloys, expanding its application scope from the aviation industry to the construction industry, container packaging industry, transportation industry, electric power and electronics industry, Various sectors of the national economy such as machinery manufacturing and petrochemicals are applied to people's daily lives. At present, aluminum is used in a large amount and in a wide range, second only to steel, and has become the second largest metal material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/12
Inventor 车云卢锦德张中可张德恩张晓燕
Owner 贵州铝厂有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap