Getter composition and device for introducing of mercury into fluorescence lamp for BLU

An introduction device and composition technology, applied in the direction of electric tube/lamp degassing, discharge tube/lamp manufacturing, gas discharge lamp parts, etc., can solve the problems of increased manufacturing cost, serious dust, and inability to maintain mercury release rate, etc. problems, to achieve the effect of improving the working environment and solving environmental problems

Inactive Publication Date: 2010-12-15
HEESUNG MATERIAL
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The shape of the mercury introduction device filled with the original getter composition is cylindrical, spherical or rod-shaped, and there is no groove for releasing mercury, or even if there is a groove for releasing mercury, its width is very narrow, so mercury The release effect is not high
[0014] In addition, after the getter composition is pressed into the metal structure, in the case of a getter that generates slits due to the overlapping of plates, dust is severe during the manufacturing process, and there may also be problems when using the getter composition. The hidden danger of composition crushing
[0015] If it is a getter with a low mercury release effect, the size of the unit getter required when manufacturing a lamp is larger, so the manufacturing cost will be increased, and a certain mercury release rate cannot be maintained when manufacturing a lamp. As a result, there is a problem that the quality of the lamps varies greatly, so a mercury introduction device with a high mercury release effect is required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Getter composition and device for introducing of mercury into fluorescence lamp for BLU
  • Getter composition and device for introducing of mercury into fluorescence lamp for BLU
  • Getter composition and device for introducing of mercury into fluorescence lamp for BLU

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0066] Example 2 is an example in which the content of Zr and Al was reduced and 2% by weight of Ti was added to the composition of Comparative Example 1. After adding Ti, it can be seen that the mercury release rate is increased by 1% compared with Comparative Example 1.

Embodiment 3

[0067] Example 3 is an example in which 2% by weight of Ta was added to the composition of Example 2. Compared with Example 2, the mercury release efficiency increased by 4% due to the addition of Ta.

[0068] In addition, when comparing Example 1 and Example 3, even in a composition containing 2% by weight of Ta, the mercury release rate can be improved by reducing the Zr and Al contents and adding 2% by weight of Ti.

Embodiment 4

[0069] In Example 4, 1% by weight of Fe was added to the composition of Comparative Example 1. Compared with Comparative Example 1, the mercury release rate of Example 4 was increased by 2%.

[0070]In Examples 5 and 6, 2% by weight of Ta was added to the composition of Comparative Example 1, and a small amount of Fe was added to produce getter compositions. In this case, the mercury release rate was increased by 6-7% compared with Comparative Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a getter combination which is used on back light units as LCD TV and monitor and used for leading mercury in an external electrode fluorescent lamp or a cold cathode adding Ti to the getter combination made from Ti-Hg Zr-Al to raise the adsorption efficiency of getter and prevent getter from being oxidized owing to the inoxidability of Ti; adding Ta to raise the release effect of mercury and to reduce the activation temperature by 100 DEG C; the activation can also be carried out from 550 to 650 DEG C; therefore, the getter combination can be prepared by making use ofcommon stoves or gas flames used in the lamp manufacturing procures without expensive high-frequency equipment, and the electrode is damaged to minimum extent. Besides, with adding 0.05 to 5 percent of Fe to the getter combination, the release effect of mercury is raised, the cost of raw material is reduced, and the activation effect is raised with the same function as medium in the getter activation process.

Description

technical field [0001] The present invention relates to a getter composition for introducing mercury into an EEFL (External Electrode Fluorescent Lamp) or a CCFL (Cold Cathode Fluorescent Lamp) used as a BLU (Back Light Unit) for LCD TVs and displays, etc. device. Background technique [0002] Usually, the getter is manufactured and used by mixing various metal components according to the composition of the residual gas to be removed and the use conditions, so that it has the property of chemically absorbing the gas to be removed. [0003] The getter composition can be manufactured in a mixture of various metal forms, and can also be formed in a structure or compound state of various forms, but the ultimate goal is to retain mercury stably and be easily activated in the lamp according to specific temperature conditions , so that it is easy to release mercury, and it is easy to absorb the doping gas in the lamp. In addition, once the luminaire is completed, it is easy to re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01J61/26H01J9/39
CPCG02F1/133603G02F1/133606H01J7/183H01J9/38H01J9/39H01J61/26H01J61/28
Inventor 南基平姜宗太金在哲
Owner HEESUNG MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products