Full ceramic aggregate porous concrete and preparation method thereof

A technology of permeable concrete and ceramic aggregate, applied in the field of building materials, can solve problems such as the complexity of the implementation process of recycling, and achieve the effect of overcoming the complexity of the implementation process and simple recycling

Inactive Publication Date: 2012-03-28
董再发
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of all-ceramic aggregate permeable concrete, which can solve the problem that the implementation process of recycling ceramic waste is relatively complicated in the related art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Full ceramic aggregate porous concrete and preparation method thereof
  • Full ceramic aggregate porous concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The present invention will be described in detail below with reference to the accompanying drawings and in combination with embodiments.

[0012] An embodiment of the present invention provides an all-ceramic aggregate permeable concrete, which includes aggregate, cement and water, and the aggregate is all ceramic aggregate.

[0013] The aggregates of the permeable concrete in the above embodiments are all made of ceramic aggregates, which makes it possible to recycle ceramic waste, overcomes the problems of low efficiency and complicated implementation process of ceramic waste recycling in related technologies, and realizes Implement efficient, simple and harmless recycling of ceramic waste.

[0014] In addition, the all-ceramic aggregate permeable concrete of this embodiment uses a large amount of ceramic waste as the main component of the pervious concrete, which realizes the resource utilization of the ceramic waste and reduces the production cost of the pervious co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides full ceramic aggregate porous concrete, which contains aggregate, cement and water, and the aggregate is ceramic aggregate. The invention also provides a preparation method for the full ceramic aggregate porous concrete, which includes steps of crushing and screening ceramic waste material of industrial production to ceramic pellet; carrying out surface treatment to the ceramic pellet to prepare ceramic aggregate; and mixing the cement, water and the ceramic aggregate according to predetermined proportioning to prepare the full ceramic aggregate porous concrete. The invention can efficiently and simply reuse ceramic waste material.

Description

technical field [0001] The invention relates to the field of building materials and the field of environmental protection, in particular to an all-ceramic aggregate permeable concrete and a preparation method thereof. Background technique [0002] Due to the fragile and difficult-to-repair characteristics of ceramics, a large amount of ceramic waste is generated in industrial production and daily use. [0003] In order to solve the recycling problem of waste ceramics, the relevant technology provides a composite Portland cement mixed with waste ceramics and its preparation method, wherein the content of waste ceramics in the cement raw materials is 10-35%, and the preparation process needs to be first The mixed material containing waste ceramics is dried or sun-dried, then crushed, and the particle size is controlled to be less than 30mm, and finally ground. [0004] In the process of realizing the present invention, the inventors found that the recycling efficiency of cera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C04B28/04C04B14/02C04B18/16
CPCY02W30/91
Inventor 董再发
Owner 董再发