Method for thermal spraying of composite bottom layer of aluminum pan of electromagnetic oven

A technology of induction cooker and thermal spraying, which is applied in the direction of coating, metal material coating process, heating fuel, etc., and can solve the problem that the electromagnetic induction heating layer cannot be formed

Inactive Publication Date: 2010-11-10
慈溪光华金属复合材料有限公司
View PDF12 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(Aluminum is not magnetically conductive and cannot form an ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for thermal spraying of composite bottom layer of aluminum pan of electromagnetic oven
  • Method for thermal spraying of composite bottom layer of aluminum pan of electromagnetic oven
  • Method for thermal spraying of composite bottom layer of aluminum pan of electromagnetic oven

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Embodiment one: the spraying of the single-layer composite bottom (430 stainless steel) coating of induction cooker aluminum pan

[0069] 1. Conditions: the shape of the pot is attached Figure 5 , The diameter of the bottom of the pot is 150mm, the diameter of the pot mouth is 210mm, the height of the pot is 50mm, the material is aluminum alloy, and the pot body is a thin-walled and thick-bottomed structure. Spraying the composite layer on the bottom of the pot is used in the induction cooker, and it is a low-to-medium-grade pot.

[0070] 2. Coating design: According to the use conditions of the spraying object, the coating adopts a single-layer structure, and the coating material is 430 stainless steel wire with Ф1.6mm, which has the characteristics of good magnetic conductivity, corrosion resistance and wear resistance. The coating thickness after processing is 4.5mm, considering the processing allowance, the coating thickness after spraying is ≥4.8mm. The structur...

Embodiment 2

[0073] Embodiment two: the spraying of the double-layer composite bottom (iron+brass) coating of induction cooker aluminum pan

[0074] 1. Conditions: the shape of the pot is attached Figure 5 , The diameter of the bottom of the pot is 150mm, the diameter of the pot mouth is 210mm, the height of the pot is 50mm, the material is aluminum alloy, and the pot body is a thin-walled and thick-bottomed structure. Spraying the composite layer on the bottom of the pot is used for induction cooker, and it is a high-end and high-end pot.

[0075]2. Coating design: According to the use conditions of the spraying object, the coating adopts a double-layer structure, the inner layer is a magnetically conductive coating, and the outer layer is a functional coating. The magnetically conductive material is made of Ф1.6mm iron wire, which has good magnetic conductivity. , high bonding strength and low price; the functional material is brass wire with Ф1.6mm, which has the characteristics of go...

Embodiment 3

[0079] Embodiment three: the spraying of the double-layer composite bottom (iron+aluminum) coating of induction cooker aluminum pan

[0080] 1. Conditions: the shape of the pot is attached Figure 5 , The diameter of the bottom of the pot is 150mm, the diameter of the pot mouth is 210mm, the height of the pot is 50mm, the material is aluminum alloy, and the pot body is a thin-walled and thick-bottomed structure. Spraying the composite layer on the bottom of the pot is used for induction cooker, and it is a high-end and high-end pot.

[0081] 2. Coating design: According to the use conditions of the spraying object, the coating adopts a double-layer structure, the inner layer is a magnetically conductive coating, and the outer layer is a functional coating. The magnetically conductive material is made of Ф1.6mm iron wire, which has good magnetic conductivity. , high bonding strength and low price; the functional material is made of Ф1.6mm aluminum alloy wire, which has the cha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for thermal spraying of a composite bottom layer of an aluminum pan of an electromagnetic oven, which is used in the manufacturing industry of food cookers and is as shown by a drawing appended to the abstract. A magnetic composite layer with a certain thickness is formed by using an automatic spraying method, designing the joint of a coating and the pan bottom into a concave mosaic structure and spraying a magnetic material (pure iron, iron alloy or 430 stainless steel) to the bottom of the aluminum pan so as to meet the operating requirements of the electromagnetic oven. According to the requirements of a product, one or more material (copper, stainless steel, aluminum, nickel, chromium or ceramic) coatings with different thicknesses or functions can be sprayed to realize aesthetic property, practicability and functionality of the electromagnetic oven pan to ensure that the pans for the electromagnetic oven become various middle-grade and high-grade series products.

Description

Technical field: [0001] The invention belongs to the food pot manufacturing industry in the field of food cookware. Using the method of automatic thermal spraying, the magnetic conductive material is sprayed on the bottom of the flat aluminum pan to form a composite layer with a certain thickness to meet the use of the induction cooker. According to the needs of the product, one or more layers of coatings with different thicknesses or different functional materials can be sprayed, such as copper, stainless steel, aluminum, nickel, chromium, ceramics, etc., to meet the aesthetics, practicability and functionality of the induction cooker. Make the induction cooker pot form a diversified series of products. Background technique: [0002] Food pots are closely related to people’s lives. They have a long history and many varieties are well known. They are usually divided into: iron pots, aluminum pots, stainless steel pots, copper pots, magnesium alloy pots, enamel pots, ceramic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C4/12C23C4/04A47J27/00A47J36/02F24C7/02C23C4/06C23C4/131
Inventor 郭面焕丁少雄蔡林强刘爱国
Owner 慈溪光华金属复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap