Kapok fiber pretreatment auxiliary agent and kapok fiber pretreatment method

A kapok fiber and pretreatment technology, which is applied in the field of kapok fiber pretreatment aids and kapok fiber pretreatment, can solve the problem of cotton wax dissolving and sticking to rollers when it encounters high temperature

Inactive Publication Date: 2015-02-25
上海鼎乘生物科技有限公司 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The second technical problem to be solved by the present invention is to provide a pretreatment method of kapok fiber, which solves the problem of cotton wax dissolving and sticking to rollers in the high temperature of the prior art and further simplifies the kapok fiber pretreatment process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Kapok fiber pretreatment auxiliary agent and kapok fiber pretreatment method
  • Kapok fiber pretreatment auxiliary agent and kapok fiber pretreatment method
  • Kapok fiber pretreatment auxiliary agent and kapok fiber pretreatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Each raw material component of Example 1 corresponding to Table 1 was weighed in turn.

[0032] Configuration method: first add water to the stirring tank, then add polyethylene glycol PEG, cross-linking agent EH, castor oil, cationic polyacrylamide and octadecyl dimethyl hydroxyethyl quaternary ammonium nitrate in sequence, and stir well , to prepare kapok fiber pretreatment additives. Stirring time: 40 minutes, rotational speed: 70 rpm, temperature: room temperature.

Embodiment 2

[0034] Each raw material component of Example 2 corresponding to Table 1 was weighed in turn. The method described in Example 1 was used to prepare the kapok fiber pretreatment aid.

Embodiment 3

[0036] Each raw material component of Example 3 corresponding to Table 1 was weighed in turn. The method described in Example 1 was used to prepare the kapok fiber pretreatment aid.

[0037] Table 1: Formulation of Kapok Fiber Pretreatment Auxiliary Unit: Kilogram

[0038] raw material

Example 1

Example 2

Example 3

PEG8000

2

8

4

Cross-linking agent EH

15

5

10

castor oil

1

5

2

Cationic polyacrylamide with a molecular weight of 8 million

10

5

8

Octadecyldimethylhydroxyethyl quaternary ammonium nitrate

5

10

8

water

80

50

68

[0039] The specific sources of each raw material are:

[0040] PEG8000: Jiangsu Haian Petrochemical Plant;

[0041] Cross-linking agent EH: Shanghai Tiantan Auxiliary Co., Ltd.;

[0042] Castor oil: Changzhou Xinliyuan Oil Co., Ltd.;

[0043] Cationic polyacrylamide (CPAM, molec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a kapok fiber pretreatment auxiliary agent and a kapok fiber pretreatment method. The kapok fiber pretreatment auxiliary agent comprises the following ingredients by weight: 2-8 parts of PEG 2000-8000; 5-15 parts of cross-linking agent; 1-5 parts of castor oil; 5-10 parts of cation polyacrylamide; 5-10 parts of antistatic agent; 50-80 parts of water. The kapok fiber pretreatment auxiliary agent is sprinkled on the kapok fiber, and is placed at room temperature for 6-24 hours, and the kapok fiber pretreatment method is completed. After the kapok fiber pretreatment is carried out by the kapok fiber pretreatment auxiliary agent of the present invention, the strip weight unevenness decreases by 18-25%, the hairiness index decreases by 55-65%, the single thread strength increased by 20-25%, the spun yarn twisting efficiency increases by 10-15%, and the roll banding case obviously improves.

Description

technical field [0001] The invention relates to a fiber pretreatment auxiliary agent and a fiber pretreatment method, in particular to a kapok fiber pretreatment auxiliary agent and a kapok fiber pretreatment method. Background technique [0002] Kapok fiber is the thinnest, lightest, highest hollow and warmest fiber material among natural ecological fibers. It has the characteristics of smoothness, antibacterial, anti-moth, anti-mildew, soft, not easy to tangle, impermeable, non-heat-conducting, ecological, warm, and strong hygroscopicity. It can be widely used in knitted underwear, fleece, sweaters, and woven casual outerwear. , bedding, hosiery and other fields. [0003] The fineness of kapok fiber is only 1 / 2 of that of cotton fiber, but the hollow rate reaches more than 86%, which is 2-3 times that of ordinary cotton fiber. The length of kapok fiber is 8-34mm, the diameter of the middle fiber is 18-45μm, the average is 30-36μm, the wall thickness is 0.5-2μm, the fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/285D06M15/53D06M13/224D06M13/463D06M13/385D06M101/06
Inventor 张庆蒋敏庆李颖君李慧霞姚晓静王蓉
Owner 上海鼎乘生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products