Persimmon-shaped visible light catalyst biobr and preparation method thereof

A visible light and catalyst technology, which is applied in the field of photocatalysis and material chemistry, can solve the problems such as the influence of particle shape on the photocatalytic performance of samples, and achieve good visible light catalytic activity, simple production process and great market potential.

Inactive Publication Date: 2016-09-07
YULIN NORMAL UNIVERSITY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, factors such as the phase structure, grain size, and particle morphology of BiOX have a great influence on the photocatalytic performance of the sample.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Persimmon-shaped visible light catalyst biobr and preparation method thereof
  • Persimmon-shaped visible light catalyst biobr and preparation method thereof
  • Persimmon-shaped visible light catalyst biobr and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Weigh 3 millimoles of bismuth nitrate pentahydrate and dissolve it in 8 mL of ethylene glycol, and stir evenly;

[0027] Weigh 6.5 mmol of cetyltrimethylammonium bromide and dissolve it in 15mL of ethylene glycol, and stir evenly;

[0028] Slowly add the solution obtained in step to the solution obtained in step , and stir for 30 minutes;

[0029] Weigh 0.5g of polyvinylpyrrolidone into the solution obtained in step , and stir for 30 minutes;

[0030] Transfer the mixture to a 50mL stainless steel hydrothermal kettle lined with polytetrafluoroethylene, add ethylene glycol to control the volume of the solution to 30mL, then let it stand and heat at 120°C for 10 hours;

[0031] After step finishes the reaction and cools down naturally, remove the upper liquid, vacuum filter and separate the solid product, wash the gained solid product with deionized water and absolute ethanol to neutrality respectively, then dry at 60°C for 20 hours, a white BiOBr solid powder w...

Embodiment 2

[0033] Weigh 5 mmoles of bismuth nitrate pentahydrate and dissolve it in 10 mL of ethylene glycol, and stir evenly;

[0034] Weigh 7 mmoles of cetyltrimethylammonium bromide and dissolve it in 15mL of ethylene glycol, and stir evenly;

[0035] Slowly add the solution obtained in step to the solution obtained in step , and stir for 30 minutes;

[0036] Weigh 0.7g of polyvinylpyrrolidone into the solution obtained in step , and stir for 30 minutes;

[0037] Transfer the mixture to a 50mL stainless steel hydrothermal kettle lined with polytetrafluoroethylene, add ethylene glycol to control the volume of the solution to 40mL, then let it stand and heat at 120°C for 12 hours;

[0038] After step finishes the reaction and cools down naturally, remove the upper layer liquid, vacuum filter and separate the solid product, wash the gained solid product with deionized water and absolute ethanol to neutrality respectively, then dry at 60°C for 24 hours, a white BiOBr solid powde...

Embodiment 3

[0040] Weigh 5 mmoles of bismuth nitrate pentahydrate and dissolve it in 10 mL of ethylene glycol, and stir evenly;

[0041] Weigh 7.5 millimoles of cetyltrimethylammonium bromide and dissolve it in 15mL of ethylene glycol, and stir evenly;

[0042] Slowly add the solution obtained in step to the solution obtained in step , and stir for 50 minutes;

[0043] Weigh 0.7g of polyvinylpyrrolidone into the solution obtained in step , and stir for 50 minutes;

[0044] Transfer the mixture to a 50mL stainless steel hydrothermal kettle lined with polytetrafluoroethylene, add ethylene glycol to control the volume of the solution to 40mL, then let it stand and heat at 120°C for 12 hours;

[0045] After step finishes the reaction and cools down naturally, remove the upper layer liquid, vacuum filter and separate the solid product, wash the gained solid product with deionized water and absolute ethanol to neutrality respectively, then dry at 80°C for 10 hours, a white BiOBr solid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a dried persimmon-shaped visible-light-driven photocatalyst BiOBr and a preparation method thereof. The inventor adopts a low-temperature solvothermal method, controls the morphology of a halogen-bismuth-oxide visible-light-driven photocatalyst by controlling the dosage of a bismuth source and a bromine source and adding a structure guiding agent, and successfully prepares the novel efficient visible-light-driven photocatalyst BiOBr with novel and special morphology, the dried persimmon shape, for the first time. The preparation method disclosed by the invention is simple in overall production technology, easy to operate, low in synthesis temperature, high in reaction yield (89%), friendly to environment and low in cost, and accords with the requirements of practical production, and the raw materials are readily available. The visible-light-driven photocatalyst disclosed by the invention has good visible-light catalytic activity, can completely degrade a plurality of organic pollutants (such as methylthionine chloride and methyl orange) within a short period of time under irradiation of visible light, is small in light corrosivity, good in reusability and large in market potential, can be applied to industrial production, and especially has good application value in photocatalytic decomposition of organic pollutants by solar energy.

Description

technical field [0001] The invention belongs to the technical field of photocatalysis and material chemistry, and in particular relates to a persimmon-shaped visible light catalyst BiOBr and a preparation method thereof. Background technique [0002] Over the years, people have been interested in TiO 2 Various pathways of modification or sensitization have been carried out to enhance their response to visible light to enhance their photocatalytic activity. However, due to TiO 2 Due to its own properties, the application of modified photocatalytic materials is still greatly restricted, especially the shortage that ultraviolet light sources must be used. Therefore, finding new photocatalysts that can directly absorb visible light is of most interest to researchers. Bismuth oxyhalide BiOX (X=Cl, Br, I) is a new type of semiconductor material, which has a unique open structure and indirect transition mode, which is conducive to the effective separation and charge transfer of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/08B01J35/02C02F1/30C02F101/30
CPCY02W10/37
Inventor 陈渊朱万仁杨家添谢祖芳韦庆敏朱立刚庞起
Owner YULIN NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com