Dyeing method of terylene, acrylic fiber, viscose glue and spandex blended fabric

A blended fabric and dyeing method technology, which is applied in the dyeing field of acrylic, polyester, viscose and spandex blended fabrics, can solve the problem of different staining effects of acrylic fiber and viscose fiber, affecting the stable control of the production process, and the waste of dyeing energy is too large and other problems, to achieve the effect of reducing the running time too long, shortening the production process, and stabilizing the process

Active Publication Date: 2014-08-06
GAOMI FUYUAN PRINTING & DYEING
View PDF3 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] First, the three-bath dyeing process is complicated and the technical risk is very large
In the process of dyeing polyester fiber in the first bath, the staining effect of acrylic fiber and viscose fiber is different after reduction, which leads to the uncontrollable shade in the process of dyeing acrylic fiber in the second bath, and in the process of dyeing acrylic fiber, cationic dyes have a negative effect on polyester fiber. The fibers and viscose fibers are also stained, which will cause color changes, which brings a lot of trouble to technical workers, affects the stable control of the production process, and leads to unstable product quality
[0005] Second, the three-bath dyeing is divided into three steps: polyester fiber dyeing, acrylic fiber dyeing, and viscose fiber dyeing, so that the dyeing energy wastes too much and the production efficiency is low
Moreover, the three-bath dyeing also has the disadvantage of a long production cycle, which seriously restricts the improvement of production efficiency, so the three-bath dyeing method needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dyeing method of terylene, acrylic fiber, viscose glue and spandex blended fabric
  • Dyeing method of terylene, acrylic fiber, viscose glue and spandex blended fabric
  • Dyeing method of terylene, acrylic fiber, viscose glue and spandex blended fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0087] The dyeing method of polyester, acrylic fiber, viscose glue and spandex blended fabric, comprises the following steps,

[0088] (1) Woven blended fabrics: Weaved blended fabrics containing polyester, acrylic, viscose and spandex. The blended fabric contains the following components by weight: 30% polyester, 45% acrylic, 15% viscose, and 10% spandex.

[0089] (2) Processing blended fabrics: pre-setting the blended fabrics in step (1) and seaming them together.

[0090] (3) One-bath dyeing of polyester and acrylic fibers: put the blended fabric treated in step (2) into cold water and heat up to 30°C, add Ao mixture 8108, degreaser 115C, high temperature leveling agent, acrylic leveling agent, dyeing acid in sequence DA, disperse dyes, and cationic dyes, then heat up to 120°C for 30 minutes, then cool down to 100°C for 20 minutes, then cool down to 70°C, take samples for comparison, then cool down to 60°C and stop for drainage, add cold water and run for 5 minutes to drai...

Embodiment 2

[0117] The dyeing method of polyester, acrylic fiber, viscose glue and spandex blended fabric, comprises the following steps,

[0118](1) Woven blended fabrics: Weaved blended fabrics containing polyester, acrylic, viscose and spandex. The blended fabric contains the following components by weight: 40% polyester, 35% acrylic, 20% viscose, and 5% spandex.

[0119] (2) Processing blended fabrics: pre-setting the blended fabrics in step (1) and seaming them together.

[0120] (3) One-bath dyeing of polyester and acrylic fibers: Put the blended fabric treated in step (2) into cold water and heat up to 50°C, add Ao mixture 8108, degreaser 115C, high temperature leveling agent, acrylic leveling agent, dyeing acid in sequence DA, disperse dyes, and cationic dyes, then heat up to 140°C for 30 minutes, then cool down to 110°C for 20 minutes, then cool down to 90°C, take samples for comparison, then cool down to 80°C, stop and drain, add cold water and run for 5 minutes to drain.

[0...

Embodiment 3

[0148] The dyeing method of polyester, acrylic fiber, viscose glue and spandex blended fabric, comprises the following steps,

[0149] (1) Woven blended fabrics: Weaved blended fabrics containing polyester, acrylic, viscose and spandex. The blended fabric contains the following components by weight: 34% of polyester fiber, 41.3% of acrylic fiber, 17.7% of viscose fiber and 7% of spandex. The polyester is 75D polyester filament, the acrylic and viscose form 40S / 1 acrylic viscose blended yarn, and the spandex is 20D spandex. Thread length: polyester filament 30cm / spandex yarn 11.5cm / acrylic viscose blended yarn 29cm (100G). Weaving method: one way of polyester filament + spandex, another way of acrylic viscose blended yarn + spandex.

[0150] (2) Processing blended fabrics: pre-setting the blended fabrics in step (1) and seaming them together.

[0151] (3) One-bath dyeing of polyester and acrylic fiber: put the blended fabric treated in step (2) into cold water and heat up ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a dyeing method of a terylene, acrylic fiber, viscose glue and spandex blended fabric. The method comprises the following steps: 1, blended fabric weaving: weaving a blended fabric containing terylene, acrylic fiber, viscose glue and spandex; 2, blended fabric treatment: carrying out scotching presetting on a gray cloth, and linking; 3, carrying out one-bath dyeing on terylene and acrylic fibers; 4, reducing, neutralizing, and washing with water; 5, carrying out two-bath dyeing on the viscose glue; 6, washing with water, neutralizing soaping, washing with water, and discharging the obtained cloth; and 7, post-treatment: dehydrating the blended fabric obtained in step 6, drying, and carrying out scotching setting to obtain a finished product. The method has the advantages of simple process, fastness, efficiency, energy saving, convenient operation, stability, and dyeing of high-quality and stable-product-quality terylene, acrylic fiber, viscose glue and spandex blended fabrics.

Description

technical field [0001] The invention relates to the technical field of dyeing of blended fabrics, in particular to a method for dyeing polyester, acrylic, viscose and spandex blended fabrics. Background technique [0002] The jersey fabric (34% polyester, 41.3% acrylic, 17.7% viscose, 7% spandex) made of polyester fiber, acrylic fiber, viscose fiber and spandex fiber is very popular in the international and domestic markets. High-grade knitted underwear fabrics are widely used. However, the conventional dyeing process of dark blended fabrics is very complicated. At present, three-bath dyeing (polyester fiber, acrylic fiber, and viscose fiber are dyed in three steps and three baths) is often used. The process flow is: weaving - blank opening Pre-shaping-sealing-pretreatment-washing-dyeing polyester-reduction-neutralization-washing-dyeing acrylic fiber-reduction-neutralization-washing-dyeing viscose-washing-neutralization-soaping-washing-fixing-cloth -Dehydration-drying-open...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06P3/87D06P1/16
Inventor 傅深环吉海东迟秀芳杜召弟鞠好友
Owner GAOMI FUYUAN PRINTING & DYEING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap