Corrosion fatigue life prediction method based on damage evolution

A technology of corrosion fatigue and damage evolution, applied in the direction of weather resistance/light resistance/corrosion resistance, measuring device, testing wear resistance, etc., can solve the problems of the analytical method, inconvenient engineering application, and many test samples, etc., and achieve the prediction method. Reasonable, convenient for engineering application, strong promotion effect

Inactive Publication Date: 2015-06-10
CHINA UNIV OF PETROLEUM (EAST CHINA)
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The test method can be said to be the best method to solve the corrosion fatigue life of materials for a specific situation, but it is often limited by the test conditions or special requirements, and the results that may be made may deviate greatly from the facts
[0010] In addition, the neural network method, probability method, etc. for material corrosion fatigue life prediction can basically be said to be parameter analysis methods based on analytical methods, which do not overcome the shortcomings of analytical methods in essence. At the same time, these methods require There are many test samples, which brings inconvenience to engineering applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Corrosion fatigue life prediction method based on damage evolution
  • Corrosion fatigue life prediction method based on damage evolution
  • Corrosion fatigue life prediction method based on damage evolution

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Such as figure 1 As shown, the corrosion fatigue life prediction method based on damage evolution includes the following steps:

[0024] Step 1: Carry out the stress corrosion test of the material to be tested, and determine the stress corrosion threshold stress and damage index. The specific method is as follows:

[0025] Process the material to be tested into a funnel-shaped sample, such as figure 2 As shown, the two ends of the sample are cylindrical and processed with threads for easy clamping; the middle of the sample is the test part, which is cylindrical with variable cross-section, and is made of cross-grinding with a forming grinding wheel, and the radius R of the transition arc is not less than the minimum cross-section 5 times the diameter d.

[0026] Select 12 samples and measure the yield limit σ of the samples S .

[0027] Such as image 3 As shown, the corrosive solution circulation device includes: a circular top cover 1, a cylindrical shell-shaped...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to technical field of metal material corrosion and particularly relates to a corrosion fatigue life prediction method based on damage evolution. The method includes following steps: carrying out a stress corrosion test to a to-be-tested material for determining a stress threshold value of the stress corrosion and a damage index; carrying out a fatigue test to the to-be-tested material for determining a fatigue damage parameter; determining a corrosion fatigue damage nonlinear evolution index of the to-be-tested material; and predicting a corrosion fatigue life of the to-be-tested material. A corrosion solution circulating device in the invention can achieve cyclic refreshing of a corrosion liquid in a metal material corrosion fatigue and stress corrosion test. The corrosion fatigue life is predicted through a method of combining theory with experimental investigation so that defects in an analytical method and a test method are overcome. The prediction method is reasonable and is accurate in result. The predicted result is free of any influence due to combination of environment and the material. The prediction method is simple in operation, is easy to carry out, is strong in popularizing performance and is convenient in engineering application.

Description

technical field [0001] The invention belongs to the field of corrosion of metal materials, and in particular relates to a corrosion fatigue life prediction method based on damage evolution, which is used for prediction of corrosion fatigue life of metal materials used in marine engineering, aerospace and the like. Background technique [0002] There are various structures that bear cyclic loads in engineering, such as marine engineering structures, aircraft, etc., and their service environments are corrosive to varying degrees. The corrosive environment will reduce the fracture toughness of the material, accelerate the initiation and propagation of cracks, and reduce the service life of the structure. Corrosion fatigue has become a serious problem faced by various structures subjected to cyclic loads in engineering. The research on corrosion fatigue performance and the prediction of corrosion fatigue life have become important contents in the durability and integrity design ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N3/56G01N17/00
Inventor 黄小光曹宇光韩忠英林红徐国强
Owner CHINA UNIV OF PETROLEUM (EAST CHINA)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com