One-component flame-retardant deketoxime/alcohol room temperature vulcanized silicone sealant and preparation method

A technology of room temperature vulcanization and removal of ketoxime, which is applied in chemical instruments and methods, adhesives, and other chemical processes. It can solve problems such as slow vulcanization speed, poor storage stability, increased process complexity, and production costs, and achieve good flame retardancy. properties, good mechanical properties, and excellent storage stability

Active Publication Date: 2016-02-24
BAIMTEC MATERIAL CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Deketoxime type one-component room temperature vulcanizing silicone sealant has the advantages of high storage stability, fast vulcanization speed and good adhesion to various substrates, but has the disadvantages of slight corrosion to copper and strong odor
Dealcoholized one-component room temperature vulcanizing silicone sealant has the advantages of environmental protection, low odor, and no corrosion to substrates, but it also has disadvantages such as poor storage stability, slow vulcanization speed, and poor adhesion to various substrates.
In the fields of energy-saving lamps, LED lamps, and electronic and electrical components, one-component room temperature vulcanized silicone sealants that are flame-retardant, good in storage stability, non-corrosive to substrates, and good in adhesion to various substrates are required. Both deketoxime type and one-component dealcoholized room temperature vulcanizing silicone sealants are difficult to meet the application requirements
[0004] One-component deketoxime / alcohol type one-component room temperature vulcanizing silicone sealant combines the advantages of deketoxime and dealcoholized room temperature vulcanizing silicone sealant, but they basically do not contain flame retardants, and neither of them can produce flame retardant room temperature vulcanized silicone sealants, and some additional inorganic moisture scavengers, such as molecular sieves, anhydrous calcium chloride, etc., will increase the process complexity and production costs if thixotropic agents are added
None of the existing technologies is aimed at preparing a flame-retardant one-component room temperature vulcanizing silicone sealant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component flame-retardant deketoxime/alcohol room temperature vulcanized silicone sealant and preparation method
  • One-component flame-retardant deketoxime/alcohol room temperature vulcanized silicone sealant and preparation method
  • One-component flame-retardant deketoxime/alcohol room temperature vulcanized silicone sealant and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Below in conjunction with embodiment technical solution of the present invention will be described in further detail:

[0021] The composition and mass parts dosage of the sealant described in the technical solution of the present invention are shown in Table 1.

[0022] Taking each component of No. 1 in Table 1 as an example, the method for preparing a single-component flame-retardant deketoxime / alcohol room temperature vulcanizing silicone sealant is described in detail below:

[0023] Weigh each component according to the proportion, first put 100 parts of α, ω-dihydroxy polydimethylsiloxane and 1.5 parts of methyl tributylketoxime silane into a vacuum kneader, heat to 70℃~ 90°C, vacuumize to 0.06-0.09MPa and stir at a constant speed for 1h-1.5h, then add 20 parts of aluminum hydroxide and 50 parts of calcium carbonate and vacuumize to 0.06-0.09MPa at 60°C-80°C and stir at a constant speed for 1h ~1.5h, then put in 2.5 parts of methyl orthosilicate and 1.2 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a single-component flame-retardant ketoxime-removed / dealcoholized room temperature vulcanized organosilicon sealant and a preparation method thereof. The single-component flame-retardant ketoxime-removed / dealcoholized room temperature vulcanized organosilicon sealant is prepared from the following materials in parts by weight: 100 parts of alpha, omega-dihydroxy polydimethylsiloxane, 10-60 parts of a flame-retardant filler, 50-150 parts of a reinforcement filler, 1.5-2 parts of a ketoxime silane cross-linking agent, 1.5-3 parts of an alkoxysilane cross-linking agent, 1.5-3 parts of an adhesion promotor and 0.5-1.5 parts of a catalyst. The single-component flame-retardant ketoxime-removed / dealcoholized room temperature vulcanized organosilicon sealant is flame-retardant, has excellent high-temperature resistance and yellowing resistance, and has favorable bonding performance to various base materials, such as metal and plastics.

Description

technical field [0001] The invention relates to a single-component flame-retardant deketoxime / alcohol room-temperature vulcanized silicone sealant and a preparation method, belonging to the technical field of polymer materials and their production. Background technique [0002] One-component condensation type room temperature vulcanizing silicone sealant is the most common and most used room temperature vulcanizing silicone sealant. widely used. One-component condensation type room temperature vulcanizing silicone sealants can be divided into deketoxime type, deacidification type, dealcoholization type, deacetone type and deamidation type according to different crosslinking agents. The current practical application in engineering is mainly deketoxime type and deacidification type one-component room temperature vulcanizing silicone sealant. [0003] The deketoxime type one-component room temperature vulcanizing silicone sealant has the advantages of high storage stability, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J183/06C09J11/06C09J11/04C09K3/10
Inventor 刘梅范召东张鹏孙全吉吴娜
Owner BAIMTEC MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com