Polyester resin composition with improved mechanical properties and fade resistance
A technology of polyester resin and composition, applied in the field of polyester resin composition, can solve the problems of reduced impact strength and moldability, reduced light stability, etc., and achieve the effect of excellent mechanical properties and excellent optical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0132] As shown in Table 1, the (A) first polyester resin of 40wt%, the (B) second polyester resin of 10wt%, the (C) white pigment of 35wt% and the (D) inorganic filler of 15wt% were mixed, And dry blended to prepare a polyester resin composition. It was processed into pellets using a twin-screw extruder with Φ = 36 mm and a nozzle temperature of 250°C to 310°C. The prepared pellets were dried at 80°C for 4 hours, and the obtained samples were injection molded and evaluated for their physical properties, the results of which are shown in Table 2.
Embodiment 2 to 3
[0134] As shown in Table 1, the polyester resin composition was prepared in the same manner as in Example 1, except that (A) the first polyester resin, (B) the second polyester resin, (C ) white pigment and (D) content of inorganic filler. The measured physical properties are shown in Table 2.
PUM
Property | Measurement | Unit |
---|---|---|
melting point | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com