Ecological glue-building water-permeable terrace and preparation method thereof

A technology of permeable floor and ecological glue, applied in construction, on-site coagulation pavement, roads, etc., can solve the problems of unfriendly color firmness, poor firmness of permeable floor, complicated process, etc. Rich colors, convenient and simple construction, and high overall firmness

Active Publication Date: 2016-03-23
FUJIAN DANONG LANDSCAPE CONSTR CO LTD +1
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a permeable floor made of ecological glue and a preparation method thereof, which overcomes the shortcomings of the existing permeable floor such as poor firmness, complicated process, high cost, not environmental protection and poor color firmness, and has the advantages of multilayer High interlayer firmness, good water permeability, good color firmness and environmental protection advantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ecological glue-building water-permeable terrace and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A permeable floor made of ecological glue, which comprises an original soil layer 1, a permeable cushion layer 2, a leveling layer 3, a permeable stone layer 4 and a transparent protective layer 5 arranged sequentially from bottom to top. Wherein, the original soil layer 1 is formed by the road bed itself. The permeable cushion 2 is made by mixing stones and cement with a weight ratio of 1:4, and the particle size of the stones is 4mm. The thickness of the permeable cushion layer 2 is 120mm, the particle pores are 0.8mm, and the water permeability coefficient is 2.0×10 -2 cm / S. The ecological glue-built permeable floor also includes a blind ditch 6, the blind ditch 6 is set close to the bottom of the permeable stone layer 4, and runs through the leveling layer 3 and part of the permeable cushion layer 2, the upper port of the permeable stone layer 4 and the blind ditch 6 There is a steel plate 61 that completely covers the upper end of the blind ditch 6 and is larger ...

Embodiment 2

[0050] A permeable floor made of ecological glue, which comprises an original soil layer 1, a permeable cushion layer 2, a leveling layer 3, a permeable stone layer 4 and a transparent protective layer 5 arranged sequentially from bottom to top. Wherein, the original soil layer 1 is formed by the road bed itself. The permeable cushion 2 is made by mixing stones and cement with a weight ratio of 1:3, and the particle size of the stones is 6mm. The thickness of the permeable cushion layer 2 is 100mm, the particle pores are 0.5mm, and the water permeability coefficient is 1.8×10 -2 cm / S.

[0051] The leveling layer 3 is made by mixing cement and fine sand with a volume ratio of 1:10. The leveling layer 3 has a thickness of 50mm and a water permeability coefficient of 1.8×10 -2 cm / S.

[0052] The permeable stone layer 4 is made by mixing glue with a weight ratio of 4:110 and natural ecological colored stones, and the particle size of the natural ecological colored stones is 6m...

Embodiment 3

[0061] A permeable floor made of ecological glue, which comprises an original soil layer 1, a permeable cushion layer 2, a leveling layer 3, a permeable stone layer 4 and a transparent protective layer 5 arranged sequentially from bottom to top. Wherein, the original soil layer 1 is formed by the road bed itself. The permeable cushion 2 is made by mixing stones and cement with a weight ratio of 1:5, and the particle size of the stones is 3mm. The thickness of the permeable cushion layer 2 is 150 mm, the particle pores are 1 mm, and the water permeability coefficient is 2.2×10 -2 cm / S.

[0062] The leveling layer 3 is made by mixing cement and fine sand with a volume ratio of 1:14. The leveling layer 3 has a thickness of 30mm and a water permeability coefficient of 2.2×10 -2 cm / S.

[0063] The permeable stone layer 4 is made by mixing glue with a weight ratio of 4:90 and natural ecological colored stones, and the particle size of the natural ecological colored stones is 9mm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an ecological glue-building water-permeable terrace which includes, from bottom to top successively, an original soil layer, a water-permeable pad layer, a leveling layer, a water-permeable stone layer and a transparent protective layer. The original soil layer is composed of roadbed. The water-permeable pad layer is prepared by mixing stones and cement. The leveling layer is prepared by mixing cement and fine sand. The water-permeable stone layer is prepared by mixing glue and natural ecological colorful stones. The terrace overcomes the defects that a water-permeable terrace in the prior art is poor in fastness, is complex in process, is high in cost, is not environment-friendly, and is poor in color fastness. The terrace is high in layer-to-layer fastness, is good in water permeability, is good in color fastness and is environment-friendly.

Description

technical field [0001] The invention relates to an ecological glue-built permeable floor and a preparation method thereof, especially applied to non-motor vehicle lanes. Background technique [0002] In the current landscape road construction, concrete is mostly used as the structural layer for direct pouring, or permeable bricks and permeable concrete are used as permeable garden roads. The above methods mainly have the following disadvantages: 1. The concrete road itself does not have drainage function ; 2. The permeable brick pavement is prone to cracking, and the permeable concrete pavement is easy to thresh, which reduces the service life of the pavement and increases the maintenance cost of the pavement; 3. The drainage effect of the pavement is not strong; 4. The landscape effect is single, which is difficult to meet the requirements of landscape design. Require. [0003] Although there are also some permeable floors now, they have the following disadvantages: 1. Dir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E01C7/32E01C11/22
CPCE01C7/32E01C7/325E01C11/226
Inventor 方龙俊钟舜杰韩文集庄钟阳朱斯华
Owner FUJIAN DANONG LANDSCAPE CONSTR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap