Ironware prop coloring technological process
A technological process and ironware technology, which is applied in the field of ironware props coloring process, can solve the problems that the product quality of color samples and proofing is difficult to meet customer satisfaction, and the coloring technology has not been reported, so as to ensure the geometric size and quality, and good cutting quality , the effect of narrow slit
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] Take 20kg of high-quality material with a thickness of 3cm, and process it according to the following steps:
[0022] 1) Blanking, using punch equipment for cutting and blanking;
[0023] 2) Group butt welding, using a welding machine for group butt welding;
[0024] 3) Straighten and grind, and use a grinder to grind;
[0025] 4) Surface sandblasting, using a sandblasting machine for sandblasting;
[0026] 5) Metal bluing, using an oven for bluing; before bluing, use compressed air to blow off the floating dust on the surface of the ironware props, and when the temperature of the oven rises to 250 ° C, put the ironware props into the oven Raise to 290°C and keep it for 110 minutes, the temperature and time depend on the thickness of the ironware and the weight of the ironware in the furnace;
[0027] 6) Powder spraying, use spraying equipment to spray powder; use transparent powder with a matt degree of 5, use the static electricity generated by the spraying equipme...
Embodiment 2
[0031] Take 15kg of high-quality material with a thickness of 2.5cm, and process it according to the following steps:
[0032] 1) Blanking, using punch equipment for cutting and blanking;
[0033] 2) Group butt welding, using a welding machine for group butt welding;
[0034] 3) Straighten and grind, and use a grinder to grind;
[0035] 4) Surface sandblasting, using a sandblasting machine for sandblasting;
[0036] 5) Metal bluing, using an oven for bluing; before bluing, use compressed air to blow off the floating dust on the surface of the ironware props, and when the temperature of the oven rises to 270 ° C, put the ironware props into the oven Raise to 300°C and keep it for 120 minutes, the temperature and time depend on the thickness of the ironware and the weight of the ironware in the furnace;
[0037] 6) Powder spraying, use spraying equipment to spray powder; use transparent powder with a matt degree of 5, use the static electricity generated by the spraying equip...
Embodiment 3
[0041] Get 30kg of high-quality materials with a thickness of 2.5cm, and process according to the following steps:__[0042]1) blanking, using punching equipment to cut and blank;
[0042] 2) Group butt welding, using a welding machine for group butt welding;
[0043] 3) Straighten and grind, and use a grinder to grind;
[0044] 4) Surface sandblasting, using a sandblasting machine for sandblasting;
[0045] 5) Metal bluing, using an oven for bluing; before bluing, use compressed air to blow off the dust on the surface of the iron props, and when the temperature of the oven rises to 280°C, put the iron props into the oven, and then put the Raise to the range of 310°C and keep it for 130 minutes. The temperature and time depend on the thickness of the ironware and the weight of the ironware in the furnace;
[0046] 6) Powder spraying, use spraying equipment to spray powder; use transparent powder with a matt degree of 5, use the static electricity generated by the spraying equi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com