Rare earth doping fluozirconate luminescent material and preparing method thereof

A technology of fluorozirconate and rare earth doping, which is applied in the direction of luminescent materials, chemical instruments and methods, etc. It can solve the problems of product reunion, non-luminescence, and inaccessibility, and achieve the effect of good crystallinity and easy dispersion of particles

Active Publication Date: 2016-07-13
WENZHOU UNIVERSITY
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sintering temperature required for high-temperature solid-phase synthesis is generally higher than 1000°C and repeated grinding and sintering are required. The product agglomerates seriously, and the pulverization process seriously affects the luminous performance of the product.
[0003] In recent years, it has been found that Mn 4+ Doped with fluorosilicates such as K 2 SiF 6 [J.H.Oh, H, Kang, Y.J.Eo, H.K.Park, Y.G.Do, J.Mater.Chem.C, 2015, 3, 607‐615.], BaSiF 6 [X.Y.Jiang, Y.X.Pan, S.M.Huang, X.A.Chen, J.G.Wang, G.K.Liu, J.Mater.Chem.C.2014, 2(13), 2301‐2306.], and fluorotitanates such as BaTiF 6 [X.Y.Jiang, Z.Chen, S.M.Huang, J.G.Wang, Y.X.Pan, DaltonTrans.2014, 43, 9414‐9418.], can emit red light, in which Mn 4+ Replace Si 4+ or Ti 4+ position, without replacing the position of alkaline earth or alkali metal ions, but Mn 4+ In the matrix SrZrF of the present invention 6 does not emit light, and has not been successfully synthesized so far, it may be that Mn 4+ Can't get into SrZrF 6 Zr in 4+ Location

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth doping fluozirconate luminescent material and preparing method thereof
  • Rare earth doping fluozirconate luminescent material and preparing method thereof
  • Rare earth doping fluozirconate luminescent material and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Mole ratio Sr: [ZrF 6 ]: Eu=0.98:1:0.02, accurately weigh the solid strontium fluoride SrF with an electronic balance 2 (analytical pure) with europium oxide Eu 2 o 3 (4N), put into the polytetrafluoroethylene reactor lining, accurately measure fluozirconic acid with a pipette and add, then add deionized water to make the total volume of the reaction system reach 40mL (accounting for 80% of the inner volume of the reactor), Magnetic stirring was performed for 15 minutes, and the liner containing the mixture was placed in a closed stainless steel reaction kettle. The reaction kettle was transferred to an oven and kept at 180° C. for 12 hours. After the reaction is completed, it is cooled and dried naturally after suction filtration, and the total product is about 3 grams. The product emits bright red fluorescence under near-ultraviolet irradiation. figure 1 The XRD shows that the product is a pure phase of SrZrF 6 , slightly doped with Eu 3+ The crystal structure ...

Embodiment 2

[0027] Mole ratio Sr: [ZrF 6 ]: Eu=0.995:1:0.005, accurately weigh the solid strontium fluoride SrF with an electronic balance 2(analytical pure) with europium oxide Eu 2 o 3 (4N), put into the polytetrafluoroethylene reactor lining, accurately measure fluozirconic acid with a pipette and add, then add deionized water to make the total volume of the reaction system reach 40mL (accounting for 80% of the inner volume of the reactor), Magnetic stirring was performed for 10 minutes, and the liner containing the mixture was placed in a closed stainless steel reaction kettle. The reaction kettle was transferred to an oven and kept at 220° C. for 4 hours. After the reaction is completed, it is cooled and dried naturally after suction filtration, and the total product is about 3 grams. The product emits bright red fluorescence under near-ultraviolet irradiation. Its excitation and emission spectra are image 3 Basically similar.

Embodiment 3

[0029] Mole ratio Sr: [ZrF 6 ]: Eu=0.93:1:0.07, accurately weigh the solid strontium fluoride SrF with an electronic balance 2 (analytical pure) with europium oxide Eu 2 o 3 (4N), put into the polytetrafluoroethylene reactor lining, accurately measure fluozirconic acid with a pipette and add, then add deionized water to make the total volume of the reaction system reach 40mL (accounting for 80% of the inner volume of the reactor), Magnetic stirring was performed for 10 minutes, and the liner containing the mixture was placed in a closed stainless steel reaction kettle. The reaction kettle was transferred to an oven and kept at 220° C. for 4 hours. After the reaction is completed, it is cooled and dried naturally after suction filtration, and the total product is about 3 grams. The product emits bright red fluorescence under near-ultraviolet irradiation. Its excitation and emission spectra are image 3 Basically similar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rare earth doping fluozirconate luminescent material and a preparing method thereof.The chemical composition of the material is Sr(1-x)ZrF6: xRE3+, wherein RE can be Eu, Tb, Ce or Dy, and x is larger than or equal to 0.5% but smaller than or equal to 7.0%.The preparing method comprises the steps that solid strontium fluoride and rare earth oxide are accurately weighed according to a stoichiometric ratio and put into a reaction kettle liner, hexafluorozirconic acid and deionized water are added, stirring is conducted, the mixture is added into a reaction kettle, reaction is conducted at the temperature from 120 DEG C to 220 DEG C, and the micro-rodlike luminescent material crystallized in good condition is obtained.The material is low in phonon energy, the luminescent center is free of radiation and low in relaxation rate, and the luminescent efficiency is high.The material particles are disperse, do not unite and are beneficial to coated pipe application.The material is high in degree of crystallinity, the matrix is stable, and hydrolysis does not occur when the material is applied to a humid environment.The material can be applied to energy-saving lamps and high-pressure mercury lamps, the preparation technology is simple, and the requirement for equipment is low.

Description

technical field [0001] The invention relates to an inorganic solid luminescent material, in particular to a luminescent material based on strontium fluorozirconate which can be used in energy-saving lamps and high-pressure mercury lamps and a preparation method thereof. Specifically relates to a strontium fluorozirconate as the matrix, with Eu 3+ (or Tb 3+ 、Ce 3+ with Dy 3+ ) is a luminescent material that activates ions, and its luminous efficiency is equivalent to that of commercial phosphors synthesized by high-temperature solid-phase method. Background technique [0002] Energy-saving lamps (254nm) and high-pressure mercury lamps (365nm) are traditional photo light sources. They are still widely used in people's production and life due to their high color rendering, high efficiency, and durability. They are currently the leading products in the lighting market. In order to obtain white light, it is necessary to uniformly mix three kinds of luminescent materials that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K11/67
CPCC09K11/7705C09K11/772C09K11/7733C09K11/7748
Inventor 潘跃晓李丽刘桂朱江明吴紫英
Owner WENZHOU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com