Retardation film, polarizing plate and display device using same
A technology of retardation film and retardation enhancer, which is applied in the fields of polarizers, display devices and retardation films, and can solve the problems of fluctuation and uneven color of liquid crystal display devices.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Synthetic example
[0207] (Synthesis example: Synthesis example of sugar ester compound)
[0208] [chemical formula 22]
[0209]
[0210] 34.2g (0.1 mol) of sucrose, 135.6g (0.6 mol) of benzoic anhydride, and 284.8g (3.6 mol) of pyridine are charged in a four-necked flask with a stirring device, a reflux cooler, a thermometer and a nitrogen inlet pipe, while stirring While boiling nitrogen gas from a nitrogen gas introduction tube, the temperature was raised, and esterification reaction was performed at 70° C. for 5 hours.
[0211] Next, reduce the pressure in the flask to 4×10 2 Pa or below, after distilling off excess pyridine at 60° C., the inside of the flask was depressurized to 1.3×10 Pa or below, the temperature was raised to 120° C., and most of benzoic anhydride and generated benzoic acid were distilled off. Then, 1 L of toluene and 300 g of a 0.5 mass % sodium carbonate aqueous solution were added, and after stirring at 50° C. for 30 minutes, the mixture was left still, and the to...
Embodiment
[0504] Hereinafter, although an Example is given and this invention is demonstrated concretely, this invention is not limited to these. In addition, in an Example, the expression of "part" or "%" is used, and unless otherwise specified, it means "part by mass" or "% by mass".
[0505] "Retardation film production"
[0506] [Production of Retardation Film 101]
[0507]
[0508] A retardation enhancer obtained by mixing Compound 38 (nitrogen-containing compound (A)) and Compound 150 (nitrogen-containing compound (B)) at a mass ratio of 99.9:0.1 was used.
[0509]
[0510] While heating, the following components were sufficiently stirred and dissolved to prepare a main dope liquid.
[0511] Cellulosic resin C1 (diacetyl cellulose having an acetyl substitution degree of 2.41 and a weight average molecular weight (Mw) of 56,000): 100 parts by mass
[0512] Phase difference enhancer (nitrogen-containing compound (A)+nitrogen-containing compound (B)): 3 parts by mass
[0513]...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
acid value | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com