Petal-containing paper-based decorative material and preparation method thereof

A technology for decorative materials and petals, applied to the preparation of the decorative materials and the field of paper-based decorative materials, can solve the problems of poor mechanical properties, influence the performance of decorative materials, low elongation at break, etc., and achieve a good interface bonding state. Effect

Active Publication Date: 2017-01-04
SHAANXI UNIV OF SCI & TECH
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, due to the small strength and length of plant fibers, and its low elongation at break, the mechanical properties of paper are poor, which affects the performance of decorative materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Petal-containing paper-based decorative material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The preparation method of the above-mentioned paper-based decorative material containing petals is specifically implemented according to the following steps:

[0033] Step 1, making softwood pulp fiber slurry with a mass concentration of 0.9% from softwood fibers with a length of 3 to 5 mm, and then adding 1% cationic starch and 0.5% polyoxidized starch to the mass of softwood pulp fibers. Ethylene: Water-soluble polyvinyl alcohol fibers with a length of 3-6mm and a fineness of 0.67-1.67dtex are made into water-soluble polyvinyl alcohol fiber slurry with a mass concentration of 0.05-0.08%, and then 0.5% of the mass of the water-soluble polyvinyl alcohol fibers is added. ~1.0% polyethylene oxide; polyethylene / polyester fiber or polypropylene / polyester fiber with length 3~5mm and fineness 1.67~3.33dtex is made into 0.05~0.08% polyethylene / polyester fiber or polypropylene / polyester fiber Ester fiber slurry, then add polyethylene / polyester fiber or polypropylene / polyester f...

Embodiment 1

[0040] making coniferous wood fibers with a length of 3-5mm into coniferous wood pulp fiber slurry with a mass concentration of 0.9%, and then adding 1% cationic starch and 0.5% polyoxyethylene of coniferous wood pulp fibers; It is 0.08% water-soluble polyvinyl alcohol fiber slurry (water-soluble PVA fiber slurry) that the water-soluble polyvinyl alcohol fiber of fineness 0.67dtex is made mass concentration by length 3mm, then adds water-soluble polyvinyl alcohol fiber quality 0.6% polyvinyl alcohol Ethylene oxide; polyethylene / polyester fibers with a length of 3mm and a denier of 1.67dtex are made into 0.08% polyethylene / polyester fiber slurry, and then polyethylene / polyester fiber quality 0.6% polyethylene oxide is added;

[0041] Hardwood fibers with a length of 1 to 3 mm are made into hardwood pulp fiber slurry with a mass concentration of 0.9%, and then respectively added with 1% cationic starch of hardwood fiber mass and 0.5% polyethylene oxide of hardwood fiber mass; Th...

Embodiment 2

[0046] making coniferous wood fibers with a length of 3-5 mm into coniferous wood pulp fiber slurry with a mass concentration of 0.9%, and then adding 1% cationic starch of coniferous wood fiber mass and polyethylene oxide of 0.5% coniferous wood fiber mass; Length 4mm, the water-soluble polyvinyl alcohol fiber of fineness 0.67dtex is made mass concentration and is the water-soluble polyvinyl alcohol fiber slurry (water-soluble PVA fiber slurry) of 0.08%, then adds water-soluble polyvinyl alcohol fiber quality 1.0% polyoxidation Ethylene; Polyethylene / polyester fibers with a length of 5mm and a fineness of 1.67dtex are made into 0.06% polyethylene / polyester fiber slurry, and then polyethylene / polyester fiber quality 1.0% polyethylene oxide is added;

[0047] Hardwood fibers with a length of 1 to 3 mm are made into hardwood pulp fiber slurry with a mass concentration of 0.9%, and then respectively added with 1% cationic starch of hardwood fiber mass and 0.5% polyethylene oxide o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a petal-containing paper-based decorative material and a preparation method thereof. The decorative material comprises a surface layer, a core layer and a bottom layer, wherein the surface layer and the bottom layer comprise softwood fiber pulp, water-soluble PVA (Polyvinyl Acetate) fiber pulp and double-component fiber pulp; and the core layer comprises softwood fiber pulp, hardwood fiber pulp and petal dispersant. According to the petal-containing paper-based decorative material, the surface layer and the bottom layer are rich in water-soluble polyvinyl alcohol fibers with high strength, water solubility and hot-melting adhesive effect, so that mechanical strength and interlayer adhesive force are provided for the material. The core layer supports the surface layer, and petals are natural, vivid, decorative and beautiful. Each layer adopts the same wet making method, the interlayer spray chemical aid is added for strengthening bonding, and the composite molded and hot-pressed interface is good in an adhesive status and is not layered.

Description

technical field [0001] The invention belongs to the technical field of special fiber manufacture, and in particular relates to a paper-based decoration material containing petals, and also relates to a preparation method of the decoration material. Background technique [0002] The paper-based decoration material containing petals is a kind of green packaging material made by combining synthetic fibers, petals and plant fibers. Petal decorations are popular for their beauty and pleasing to the eye. With the improvement of people's quality of life and the improvement of environmental protection awareness, the concept of "green and environmental protection" is constantly being strengthened when Chinese people buy goods. In the "green design" revolution, the pursuit of environmental protection awareness is always pursued, and the outer packaging design of products is required. beautiful. Therefore, today's environmentally friendly paper products should not only reflect safety...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/30B32B29/00D21H13/16D21H17/02D21H17/28
CPCB32B29/005D21H13/16D21H17/02D21H17/28D21H27/30
Inventor 李鸿魁党育红陈瑜唐清袁世波
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap