Asphalt warm mix agent, its preparation method and application

A warm mix agent and reaction technology, applied in building thermal insulation materials, climate change adaptation, building components, etc., can solve the problems of poor thermal stability and anti-aging performance, high use temperature, environmental pollution, use temperature, etc., to improve Anti-aging performance, stable performance, the effect of improving thermal stability

Active Publication Date: 2018-12-04
CHINA PETROLEUM & CHEM CORP +1
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] In order to solve the problems in the prior art that the use temperature of asphalt warm mix agent is too high, it is easy to cause environmental pollution or the use temperature is low, but the thermal stability and anti-aging performance are not good, the present invention provides a warm mix agent, which can be applied to In the preparation of various asphalt or asphalt mixture, it can significantly reduce the production and use temperature of asphalt, reduce the air pollution caused by asphalt production and use, and at the same time improve the performance of asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Asphalt warm mix agent, its preparation method and application
  • Asphalt warm mix agent, its preparation method and application
  • Asphalt warm mix agent, its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) Preparation of warm mix agent

[0045] Using Ni metal as a catalyst, the CO obtained after gasification of coal, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 30 to 60 account for 90%.

[0046] ①Weigh 1000g of the above-mentioned mixed alkanes, about 1.2mol, put them in a closed container, heat to 480°C, add 3g of catalyst anhydrous CuCl 2 , keep introducing 0.89mol of chlorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 3MPa, and react for 30min to obtain the intermediate;

[0047] ②Weigh 7000g of the fourth-line extraction oil with 70% aromatics content, and add 441g of complex [Cu(NH 3 ) 4 ] SO 4 And 44.1g of catalyst Cu, packed in another airtight container and heated to 350 ° C, at this temperature constant temperature reaction for 180min, to obtain aromatic complex components;

[0048] ③Introduce aromatic complex components into the intermediate, keep...

Embodiment 2

[0053] (1) Preparation of warm mix agent

[0054] Using Co metal as a catalyst, the CO obtained after gasification of coal, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 30 to 130 account for 90%.

[0055] ① Weigh 3500g of the above-mentioned mixed alkanes, about 4.5mol, put them in a closed container, heat to 400°C, add 31.5g of catalyst anhydrous MnCl 2 , keep introducing 1.16mol of chlorine at this temperature, and feed nitrogen to keep the pressure of the reaction vessel at 5MPa, and react for 60min to obtain the intermediate;

[0056] ②Weigh 1000g of catalytic cracking oil slurry with an aromatics content of 63%, and add 19g of complex K to it 4 [Fe(CN) 6 ] and 1.9g of catalyst Fe were installed in another airtight container and heated to 270°C, and reacted at a constant temperature for 120min at this temperature to obtain the aromatic hydrocarbon complexing component;

[0057] ③Introduce the aromatic hyd...

Embodiment 3

[0062] (1) Preparation of warm mix agent

[0063] Using Fe metal as a catalyst, CO obtained from gasification of coal, and H 2 The synthesis reaction is carried out to obtain mixed alkanes in which alkanes with carbon numbers of 70 to 90 account for 90%.

[0064]①Weigh 1000g of the above-mentioned mixed alkanes, about 0.8mol, put them in a closed container, heat to 440°C, add 6g of catalyst anhydrous NiCl 2 , keep the temperature and introduce 0.31mol of fluorine, and feed nitrogen to keep the pressure of the reaction vessel at 4MPa, and react for 45min to obtain the intermediate;

[0065] ②Weigh 3500g of phenolic refined extract oil with aromatics content of 78%, and add 164g of complex Ni(CO) to it 4 And 16.4g of catalyst Ni, packed in another airtight container and heated to 310 ° C, at this temperature constant temperature reaction for 160min, to obtain aromatic complex components;

[0066] ③Introduce the aromatic hydrocarbon complexing component into the above-mentione...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides an asphalt warm mixing agent as well as a preparation method and application thereof. The warm mixing agent is prepared by adopting a method as follows: enabling high polymer alkane to react with elemental halogen under a certain temperature and pressure so as to obtain an intermediate under the action of a catalyst; enabling aromatic hydrocarbon oil to react with a complex so as to obtain an aromatic hydrocarbon complexing component under the action of the catalyst; enabling the aromatic hydrocarbon complexing component to react with the intermediate at a certain temperature, and curing, so as to obtain the warm mixing agent disclosed by the invention. The warm mixing agent disclosed by the invention is applied to preparation of warm mix asphalt, can achieve the asphalt warm mixing effect and has high / low-temperature performances of the asphalt, the melting temperature of the asphalt and the viscosity at the temperature are reduced, and the thermal stability and ageing resistance can be improved.

Description

technical field [0001] The invention relates to a warm mix agent, in particular to an additive for warm mix asphalt, and belongs to the field of petroleum industry and basic material chemistry. Background technique [0002] The asphalt mixture used in road engineering in the past is generally divided into two types according to the mixing construction temperature: cold mix asphalt mixture CMA (Cold Mix Asphalt) and hot mix asphalt mixture HMA (Hot Mix Asphalt). Cold-mix asphalt mixture is generally mixed and paved with emulsified asphalt or liquid asphalt and aggregate at room temperature, without heating the aggregate and binder, which can save a lot of energy. However, the initial strength of cold-mix asphalt mixture is low, and it is difficult to meet the requirements of important projects such as expressways and heavy-duty traffic roads. Hot mix asphalt mixture is widely used and has good road performance. However, in the production process of hot mix asphalt mixture, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L101/00C08K3/06C04B26/26
CPCY02A30/30
Inventor 陈保莲范思远张静宁爱民李志军程国香
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com