A kind of nano-silver and gelatin modified antibacterial ink and preparation method thereof

A nano-silver and gelatin technology, applied in inks, household appliances, applications, etc., can solve the problems of low biological safety and strong odor, and achieve the effects of simple preparation process, fluent and smooth writing, and black and bright ink marks.

Active Publication Date: 2020-09-04
BEIJING UNIV OF CHEM TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems of low biological safety and strong smell of existing ink products such as ink, the present invention provides a nano-silver and gelatin modified antibacterial ink and a preparation method thereof. The prepared antibacterial ink has strong antibacterial property, non-toxic and non-toxic Stinky, suitable for large-scale promotion and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nano-silver and gelatin modified antibacterial ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] 1) dissolving gelatin in water to prepare a gelatin aqueous solution with a concentration of 2wt% for later use;

[0044] 2) Dissolve silver nitrate with a proportion of 0.3 parts by weight in the gelatin solution described in step 1) with a proportion of 180 parts by weight, and stir evenly;

[0045] 3) Take ascorbic acid with a proportion of 0.15 parts by weight and dissolve it in the gelatin solution described in step 1) with a proportion of 180 parts by weight, stir evenly, and adjust the pH to 9.5;

[0046] 4) Slowly add the well-stirred ascorbic acid solution dropwise into the well-stirred silver nitrate solution, stir magnetically at 60°C, and react for 1.5h to prepare a nano-silver solution;

[0047] 5) Take ink toner with a ratio of 10 parts by weight, and grind it into fine toner for later use;

[0048] 6) Take the above-mentioned fine carbon powder and slowly add it to the nano-silver solution after the reaction, and keep stirring to make it evenly dispersed...

Embodiment 2

[0052] 1) dissolving gelatin in water to prepare a gelatin aqueous solution with a concentration of 2wt% for later use;

[0053] 2) Dissolve silver nitrate with a proportion of 1.35 parts by weight in the gelatin solution described in step 1) with a proportion of 270 parts by weight, and stir evenly;

[0054]3) Take ascorbic acid with a proportion of 0.7 parts by weight and dissolve it in the gelatin solution described in step 1) with a proportion of 270 parts by weight, stir evenly, and adjust the pH=10;

[0055] 4) Slowly add the well-stirred ascorbic acid solution dropwise into the well-stirred silver nitrate solution, stir magnetically at 70°C, and react for 1 hour to prepare a nano-silver solution;

[0056] 5) Take ink toner with a ratio of 10 parts by weight, and grind it into fine toner for later use;

[0057] 6) Take the above-mentioned fine carbon powder and slowly add it to the nano-silver solution after the reaction, and keep stirring to make it evenly dispersed; ...

Embodiment 3

[0061] 1) dissolving gelatin in water to prepare a gelatin aqueous solution with a concentration of 2wt% for later use;

[0062] 2) Dissolve silver nitrate with a proportion of 0.005 parts by weight in the gelatin solution described in step 1) with a proportion of 60 parts by weight, and stir evenly;

[0063] 3) Take ascorbic acid with a proportion of 0.0025 parts by weight and dissolve it in the gelatin solution described in step 1) with a proportion of 60 parts by weight, stir evenly, and adjust the pH to 9;

[0064] 4) Slowly add the well-stirred ascorbic acid solution dropwise into the well-stirred silver nitrate solution, stir magnetically at 50°C, and react for 2 hours to prepare a nano-silver solution;

[0065] 5) Take ink toner with a ratio of 10 parts by weight, and grind it into fine toner for later use;

[0066] 6) Take the above-mentioned fine carbon powder and slowly add it to the nano-silver solution after the reaction, and keep stirring to make it evenly disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to nano silver and gelatin modified antibacterial ink and a preparation method thereof. The nano silver and gelatin modified antibacterial ink is prepared from the following ingredients in parts by weight: 10 parts of ink carbon powder, 60 to 540 parts of gelatin solution, 0.0025 to 1.8 parts of silver salt, 0.0015 to 0.9 parts of reducing agent, 0.5 to 10 parts of emulsifier, 0.5 to 15 parts of wetting agent and 0 to 1 parts of spice. The prepared antibacterial ink is high in antibacterial property, non-toxic, odourless and suitable for large-scale popularization and application.

Description

technical field [0001] The invention relates to an antibacterial ink modified by nanometer silver and gelatin and a preparation method thereof, belonging to the field of calligraphy and painting utensils. Background technique [0002] In Chinese traditional art, calligraphy occupies a very important position and has very Chinese national characteristics. Ink, one of the four treasures of the study, which is closely related to calligraphy, has a very long history of use, dating back thousands of years. As an indispensable art expression product in the field of Chinese art, the performance of ink should be continuously improved, perfected, and then passed on and carried forward. [0003] There are also a lot of inks on the market today, and there are various types. They are basically made of carbon black and animal rubber. Since the rubber is perishable, in order to prevent the deterioration of ink products, toxic substances such as phenol and xylenol are added as preservativ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/16C09D11/17
CPCC09D11/16C09D11/17
Inventor 黄雅钦李静慧
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap