A kind of water-repellent wrapping paper based on nano plant fiber and preparation method thereof

A plant fiber and nano-cellulose technology, applied in packaging paper, wrapping paper, using microbial/enzymatic cellulose treatment, etc., can solve the problems of plant fiber paper water repellency and rareness, and achieve a small size range and a preparation method Simple, Manipulable Effects

Inactive Publication Date: 2018-11-27
SUZHOU ANTEK INDAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, packaging paper materials are all developing towards lightweight functionality, but there are few research reports on endowing plant fiber paper with water-repellent function from the aspects of structure and materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-repellent wrapping paper based on nano plant fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) The rice straw was dried in the sun, beaten thoroughly, immersed in 20g / L sodium hydroxide solution, heated and boiled for activation for 20 minutes, adjusted to neutral pH, and taken out to obtain pretreated rice straw.

[0027] (2) Place the pretreated rice straw in a biological enzyme solution containing 1% cellulase and 2% xylanase, stir it ultrasonically for 10 min at a power of 100W, and add acetic acid and molybdenum at a volume ratio of 3:1 Acid and inorganic acid mixed solution, continue to ultrasonically stir for 10min under 100W power, take it out, filter it with an ultrafiltration membrane with a pore size of 100nm, wash with water, and obtain nano-plant fibers, according to the material ratio of nano-plant fibers and hydrogen peroxide solution is 0.1g : 3ml, add dropwise hydrogen peroxide solution, and bleach at 40°C for 30min to obtain a solution containing nano-plant fibers.

[0028] (3) Add fillers, cationic starch, bentonite and sticky chemicals to ...

Embodiment 2

[0030] (1) Dry the rice straw, beat it fully, dip it in 30g / L sodium hydroxide solution, heat and boil to activate for 30min, adjust the pH value to neutral, take it out, and obtain the pretreated rice straw.

[0031] (2) Place the pretreated rice straw in a bio-enzyme solution containing 2% cellulase and 3% xylanase, stir it ultrasonically for 20min at a power of 150W, and add dropwise acetic acid and molybdenum at a volume ratio of 4:1 Acid and inorganic acid mixed solution, continue to ultrasonically stir for 20min under 150W power, take out, filter with an ultrafiltration membrane with a pore size of 100nm, and wash with water to obtain nano-plant fibers, according to the material ratio of nano-plant fibers and hydrogen peroxide solution is 0.1g : 5ml, hydrogen peroxide solution was added dropwise, and bleached at 60°C for 30min to obtain a solution containing nano-plant fibers.

[0032] (3) Add fillers, cationic starch, bentonite and sticky chemicals to the solution conta...

Embodiment 3

[0034] (1) The rice straw was dried in the sun, beaten thoroughly, immersed in 25g / L sodium hydroxide solution, heated and boiled for activation for 25 minutes, adjusted to neutral pH, and taken out to obtain pretreated rice straw.

[0035] (2) Place the pretreated rice straw in a bio-enzyme solution containing 1.5% cellulase and 2.5% xylanase, ultrasonically stir for 15 minutes at a power of 110W, and add dropwise acetic acid and molybdenum at a volume ratio of 3.5:1 Acid and inorganic acid mixed solution, continue to ultrasonically stir for 15min under 130W power, take out, filter with an ultrafiltration membrane with a pore size of 100nm, and wash with water to obtain nano-plant fibers, according to the material ratio of nano-plant fibers and hydrogen peroxide solution is 0.1g : 4ml, hydrogen peroxide solution was added dropwise, and bleached at 50°C for 30min to obtain a solution containing nano-plant fibers.

[0036] (3) Add fillers, cationic starch, bentonite and sticky ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides water-repellency packaging paper based on nanometer plant fibers and a preparing method thereof. The preparing method includes the following specific steps that rice straw is dried in the sun and beaten, the product is soaked in a sodium hydroxide solution, heated, boiled and activated, the pH value is adjusted to be neutral, and pretreated rice straw is obtained; the pretreated rice straw is put into a biological enzyme solution, the mixture is subjected to ultrasonic stirring, inorganic acid is dropwise added, the mixture is subjected to ultrasonic stirring, the product is taken out and filtered with an ultra-filtration membrane, washing is carried out, a hydrogen peroxide solution is dropwise added for bleaching, and a solution containing the nanometer plant fibers is obtained; fillers, cationic starch, bentonite and gummy-substance chemical medicine are added into the solution containing the nanometer plant fibers, the mixture is stirred to be even to form pulp, the pulp is distributed on a forming net, dehydration and drying are carried out, and the water-repellency packaging paper based on the nanometer plant fibers is obtained. According to the water-repellency packaging paper prepared with the method, the rice straw serves as a raw material, nano-cellulose whiskers are formed with the biological chemistry and physical technologies and then prepared into the packaging paper, and the packaging paper has the water-repellency effect accordingly.

Description

technical field [0001] The invention belongs to the technical field of paper packaging materials, and in particular relates to a water-repellent packaging paper based on nano plant fibers and a preparation method thereof. Background technique [0002] The packaging industry is one of the most extensive and most potential industries in my country's current national economy that involves people's lives. Modern four-pillar packaging materials include paper, plastic, metal and glass. Among them, paper packaging has a wide range of sources, cheap price, low cost, good processing performance, good printing performance, opaque, certain mechanical strength, hygiene, safety and light weight. , Degradable and other advantages, compared with other materials has great advantages, is one of the most promising green packaging materials. [0003] In modern society, people are increasingly advocating consumption patterns such as environmentally friendly consumption and reusing resources. G...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/10D21B1/02D21C5/00D21H17/29D21H17/67D21H17/68D21H21/16
CPCD21B1/021D21C5/005D21H17/29D21H17/67D21H17/68D21H21/16D21H27/10
Inventor 包伟强
Owner SUZHOU ANTEK INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap