A technology of wireless charging and magnetic isolation sheet, which is applied in the field of magnetic isolation sheet for wireless charging and its preparation, and can solve the problems of high loss and low Bs of magnetic isolation sheet

Active Publication Date: 2018-09-07
娄底市玖鑫电子科技有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a magnetic isolation sheet for wireless charging and a preparation method to solve the problem that the Bs of the magnetic is...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetism insulation piece for wireless charging and preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The embodiment of the present application provides a preparation method of a magnetic isolation sheet for wireless charging, the preparation method comprising:

[0042] S101: The raw materials for preparing the magnetic isolation sheet are Fe according to the mass ratio 2 o 3 69.5%, Mn 3 o 4 23% and ZnO7.5% are uniformly mixed and then tableted to obtain raw material tablets.

[0043] S102: Pre-fire the raw material sheet at a temperature of 950°C until the tap density of the pre-fired raw material sheet is 1.3 g / cm 3 .

[0044] S103: Pulverize the calcined raw material pieces to form a pulverized material.

[0045] S104: Mix crushed materials, auxiliary materials, polyvinyl alcohol glue and deionized water to form a mixture. The rotational speed of the mixture was sand-milled at 2000r / min, the sand-milling time was 180min, and the sand-milled particle size was 0.8μm. The auxiliary materials include calcium carbonate, vanadium pentoxide, niobium pentoxide, elemen...

Embodiment 2

[0053] The embodiment of the present application provides a preparation method of a magnetic isolation sheet for wireless charging, the preparation method comprising:

[0054] S201: The raw materials for preparing the magnetic isolation sheet are Fe according to the mass ratio 2 o 3 69.5%, Mn 3 o 4 23% and ZnO7.5% are uniformly mixed in proportion and then tableted to obtain raw material tablets.

[0055] S202: Pre-fire the raw material sheet at a temperature of 948°C until the tap density of the pre-fired raw material sheet is 1.5 g / cm 3 .

[0056] S203: Pulverize the calcined raw material pieces to form a pulverized material.

[0057] S204: Mix crushed materials, auxiliary materials, polyvinyl alcohol glue and deionized water to form a mixture. The rotation speed of the mixture was 2000r / min, the sanding time was 120min, and the sanding time was 1.4μm. The auxiliary materials include calcium carbonate, vanadium pentoxide, niobium pentoxide, elemental iron and dicobalt...

Embodiment 3

[0065] The embodiment of the present application provides a preparation method of a magnetic isolation sheet for wireless charging, the preparation method comprising:

[0066] S301: The raw materials for preparing the magnetic isolation sheet are Fe according to the mass ratio 2 o 3 65%, MnO26% and ZnO9% are uniformly mixed in proportion and then tableted to obtain raw material tablets.

[0067] S302: Pre-fire the raw material sheet at a temperature of 945°C until the tap density of the pre-fired raw material sheet is 1.3g / cm 3 .

[0068] S303: Pulverize the calcined raw material pieces to form a pulverized material.

[0069] S304: Mix crushed materials, auxiliary materials, polyvinyl alcohol glue and deionized water to form a mixture. The rotational speed of the mixture was sand-milled at 2000r / min, the sand-milling time was 90min, and the sand-milled particle size was 1.2μm. The auxiliary materials include calcium carbonate, vanadium pentoxide, niobium pentoxide, elemen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tap densityaaaaaaaaaa
Granularityaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to view more

Abstract

The invention provides a magnetism insulation piece for wireless charging and a preparing method. The high-Bs and low-loss magnetism insulation piece is prepared through the glue discharging by a tunnel kiln, the sintering by a bell type furnace and the slicing after the preparing of raw materials, the tabletting, the low-temperature pre-sintering, the doping of a trace amount of auxiliary materials and other substances, the spray granulating, and the press-forming. Meanwhile, by means of the preparing method, magnetism insulation pieces can be prepared in batches, and the production requirement is met.

Description

technical field [0001] The invention relates to the technical field of wireless charging, in particular to a magnetic isolation sheet for wireless charging and a preparation method thereof. Background technique [0002] As a safe, fashionable and convenient new charging method, wireless charging is increasingly favored by consumers, and it is developing rapidly in the field of consumer electronics such as mobile phones and computers. [0003] During the working process of the wireless charging device, the transmitting end and the receiving end each have a coil. The transmitting end coil is connected to a wired power supply and generates an electromagnetic signal. The receiving end coil induces the electromagnetic signal at the transmitting end to generate current to charge the battery. The magnetic isolation sheet attached to the sending end can enhance the magnetic field strength of the coil, and at the same time has a high magnetic convergence effect; the magnetic isolatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/38
CPCC04B35/2658C04B2235/3239C04B2235/3251C04B2235/3275C04B2235/405C04B2235/442C04B2235/608
Inventor 林开品朱再元
Owner 娄底市玖鑫电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap