Corrosion resistant silver alloy with purple appearance for jewelry and processing process thereof

A processing technology and corrosion-resistant technology, applied in the field of alloys, can solve the problems that affect the product market sales and user experience, have not been obtained, limit the market share, etc., to achieve accelerated promotion and market share, good filling performance, metal The effect of low liquid suction

Inactive Publication Date: 2018-10-09
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The long-term unsolved problems in the industry not only affect the market sales and user experience of related products, but also seriously limit the market share of such products in the international field
The development and industrialization of silver alloys with the ability to prevent surface discoloration is an inevitable problem in the field of jewelry materials. For a long time, many domestic research institutions and enterprises have made multi-faceted attempts, but unfortunately, no substantial progress has been made so far. Progress

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A silver alloy with purple appearance and corrosion-resistant jewelry and its processing technology. In terms of weight percentage, the composition of the alloy is B:0.1wt.%, Ca:1.4wt.%, Al:34.0wt.%, Ni:6.2wt.%, W:0.4wt.%, Sm:0.1wt.%. , Si: 2.5wt.%, the balance is silver. The above-mentioned silver alloy for jewelry with a purple appearance and corrosion resistance and its processing technology include the following steps: adding the raw materials in the above ratio into an induction furnace under an argon atmosphere, and using a graphite crucible; 10 minutes, rely on high-frequency induction furnace to stir evenly; after stirring evenly, keep warm at 1100 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 50-100mm, and uses water cooling to cool down. The ingot can be used as a casting raw material for casting in the subsequent process to prepare castings of complex shapes; the final heat treatment process of these cas...

Embodiment 2

[0023]A silver alloy with purple appearance and corrosion-resistant jewelry and its processing technology. In terms of weight percentage, the composition of the alloy is B:0.2wt.%, Ca:1.6wt.%, Al:35.0wt.%, Ni:8.5wt.%, W:0.6wt.%, Sm:0.2wt.%. , Si: 2.8wt.%, the balance is silver. The above-mentioned silver alloy for jewelry with a purple appearance and corrosion resistance and its processing technology include the following steps: adding the raw materials in the above ratio into an induction furnace under an argon atmosphere, and using a graphite crucible; 10 minutes, rely on high-frequency induction furnace to stir evenly; after stirring evenly, keep warm at 1100 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 50-100mm, and uses water cooling to cool down. The ingot can be used as a casting raw material for casting in the subsequent process to prepare castings of complex shapes; the final heat treatment process of these cast...

Embodiment 3

[0026] A silver alloy with purple appearance and corrosion-resistant jewelry and its processing technology. In terms of weight percentage, the composition of the alloy is B: 0.1wt.%, Ca: 1.5wt.%, Al: 34.0wt.%, Ni: 6.8wt.%, W: 0.5wt.%, Sm: 0.1wt.%. , Si: 2.6wt.%, the balance is silver. The above-mentioned silver alloy for jewelry with a purple appearance and corrosion resistance and its processing technology include the following steps: adding the raw materials in the above ratio into an induction furnace under an argon atmosphere, and using a graphite crucible; 10 minutes, rely on high-frequency induction furnace to stir evenly; after stirring evenly, keep warm at 1100 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 50-100mm, and uses water cooling to cool down. The ingot can be used as a casting raw material for casting in the subsequent process to prepare castings of complex shapes; the final heat treatment process of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A corrosion resistant silver alloy with purple appearance for jewelry and a processing process thereof are disclosed. The silver alloy includes, by weight, 0.1-0.2 wt% of B, 1.4-1.6 wt% of Ca, 34.0-35.0 wt% of Al, 6.2-8.5 wt% of Ni, 0.4-0.6 wt% of W, 0.1-0.2 wt% of Sm and 2.5-2.8 wt% of Si, with the balance being silver. A new variety having purple gloss is provided for colorful silver in the present market, and the silver alloy has excellent discoloration resistance. The production cost is reduced, and the related production process and equipment requirements are greatly simplified, and it can be predicted that application and industrialization of the silver alloy will yield substantial achievements and social benefit.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a silver alloy. Background technique [0002] Silver is a metal with a very strong white luster. In English, silver is called Silver, which means white brilliance. Sterling silver has a soft texture and good ductility. It can be made into various ornaments through drawing, hammering and other processing techniques. It was an indispensable jewelry material in ancient times. The history of human use of silver can be traced back to about 3000 BC, and silver utensils were found in the Mesopotamia civilization in Southwest Asia. In nature, it seldom exists in the form of simple substance, and generally exists in the form of compound in deep veins, which is difficult to extract, so the discovery and utilization of silver is later than that of gold. [0003] Because of its beauty and rarity, silver has become a symbol of wealth and status. Silver coins are an important currency in cir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C5/06C22C1/02C22F1/14
CPCC22C5/06C22C1/02C22F1/14
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap