A low-cost manufacturing method for flaw detection q345b grade steel plate

A manufacturing method and low-cost technology, applied in the field of low-cost manufacturing of Q345B-grade steel plates for protection and inspection, can solve the problems of large addition amount of manganese alloy, high production cost, long production process, etc., so as to reduce the cost of alloy and the cost per ton of steel. , Improve the effect of machine-time output

Active Publication Date: 2019-11-05
WUHAN IRON & STEEL GRP ECHENG IRON & STEEL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the current problems of long production process and relatively high production cost caused by the large amount of manganese alloy added to ensure the performance and flaw detection pass rate of Q345B grade steel plate, and provide a low-cost manufacturing method for flaw detection Q345B grade steel plate method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-cost manufacturing method for flaw detection q345b grade steel plate
  • A low-cost manufacturing method for flaw detection q345b grade steel plate
  • A low-cost manufacturing method for flaw detection q345b grade steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 130

[0045] A low-cost manufacturing method for flaw detection Q345B grade steel plate in this embodiment, the chemical composition and mass percentage content of the Q345B grade steel plate are: C 0.16%, Si 0.35%, Mn 0.75%, P 0.025%, S 0.012 %, Als 0.020, Ti 0.025%, the rest is Fe and unavoidable impurities. The present embodiment takes 130 tons of converters as an example, and its manufacturing method comprises the following steps:

[0046] (1) Hot metal KR desulfurization treatment

[0047] Add molten iron with mass fraction P≤0.150%, S≤0.050% and temperature T≥1280°C in the molten iron tank, and then pretreat the molten iron with KR heavy desulfurization. After treatment, S≤0.005% in molten iron, and add Remove at least 2 / 3 of the desulfurization slag from the molten iron tank before the converter;

[0048] (2) Converter smelting

[0049] ①Smelting the desulfurized molten iron into the top-bottom combined blowing converter, adding dephosphorization agent to reduce the phosph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-cost manufacturing method of a flaw-detection-ensured Q345B stage steel plate. The steel plate comprises, by mass percent, 0.15 to 0.20% of C, 0.15 to 0.50% of Si, 0.50 to 0.90% of Mn, not larger than 0.035% of P, not larger than 0.025% of S, 0.020 to 0.060% of Ti, 0.015 to 0.035% of Als, and the balance Fe and inevitable impurities. During preparing, molten iron is subject to KR desulfurization treatment firstly, the molten iron obtained after desulfurization treatment is subject to slag removal, the molten iron is converted into a converter to be smelted, outputmolten steel is subject to continuous casting and rolling, finally, the rolled steel plate is subject to stacking for slow-cooling for 24 to 72 hours, and then sampling inspection is carried out; thechemical components and the production process of the prepared Q345B stage steel plate are simple, the production cost is low, the flaw detection property is good, and the method has the good application and popularization prospects.

Description

technical field [0001] The invention relates to the technical field of alloy structural steel manufacturing, in particular to a low-cost manufacturing method for flaw detection Q345B grade steel plates. Background technique [0002] Q345 is a low-carbon alloy steel (C<0.2%), with good overall performance, low temperature performance, cold stamping performance, welding performance and machinability, and is widely used in bridges, vehicles, ships, buildings, pressure vessels, etc. [0003] In order to ensure the performance and pass rate of flaw detection of Q345B grade steel plate, the current practice in domestic iron and steel enterprises is to control the performance through the five elements of C, Si, Mn, P and S, and use BOF-LF-CC or BOF-LF-RH-CC And other production processes to improve the cleanliness of molten steel, so as to ensure the qualified rate of steel plate flaw detection, these processes ensure the quality of the steel plate, but the amount of manganese a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/14C22C38/06C22C33/04C21C5/28C21C7/072C21C7/06C21D8/02
CPCC21C5/28C21C7/06C21C7/072C21D8/0226C22C33/04C22C38/002C22C38/02C22C38/04C22C38/06C22C38/14
Inventor 夏金魁李相付廖广府杨波
Owner WUHAN IRON & STEEL GRP ECHENG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com