Lead-free high-hardness yellow Lima alloy for cast Buddha figures in Tibetan region and process thereof

A high-hardness, Buddha-like technology, applied in the field of alloys, can solve problems that have not yet been achieved, and achieve the effects of clear outline, excellent corrosion resistance, and improved recycling performance

Inactive Publication Date: 2018-10-26
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The development and industrialization of Lima alloys with advanced performance is an inevitable problem. For a long time, many domestic research institutions and enterprises have made multi-faceted attempts, but unfortunately, no substantial progress has been made so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A lead-free high-hardness yellow Lima alloy for casting Buddha statues in Tibetan areas and its technology. In terms of weight percentage, the composition of the alloy is Ba:0.6wt.%, Mg:5.0wt.%, Zn:12.0wt.%, Bi:4.0wt.%, Sb:3.0wt.%, Mo:1.0wt.% , Au: 2.0wt.%, Ag: 18.0wt.%, and the balance is copper. The above-mentioned lead-free high-hardness yellow Lima alloy and its process for casting Buddha statues in Tibetan areas include the following steps: adding the above-mentioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; The raw materials are added to the induction furnace under the argon environment, and graphite crucible is used; when smelting, it is kept at 1200 degrees for 10 minutes, and it is stirred evenly by high-frequency induction furnace; after stirring, it is kept at 1200 degrees for 1 minute and cast out of the furnace; the alloy Casting adopts a steel mold with a diameter of 20-30mm, and uses water cooling ...

Embodiment 2

[0022] A lead-free high-hardness yellow Lima alloy for casting Buddha statues in Tibetan areas and its technology. In terms of weight percentage, the composition of the alloy is Ba:0.8wt.%, Mg:8.0wt.%, Zn:14.0wt.%, Bi:6.0wt.%, Sb:4.0wt.%, Mo:2.0wt.% , Au: 3.0wt.%, Ag: 24.0wt.%, and the balance is copper. The above-mentioned lead-free high-hardness yellow Lima alloy and its process for casting Buddha statues in Tibetan areas include the following steps: adding the above-mentioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; The raw materials are added to the induction furnace under the argon environment, and graphite crucible is used; when smelting, it is kept at 1200 degrees for 10 minutes, and it is stirred evenly by high-frequency induction furnace; after stirring, it is kept at 1200 degrees for 1 minute and cast out of the furnace; the alloy Casting adopts a steel mold with a diameter of 20-30mm, and uses water cooling ...

Embodiment 3

[0025] A lead-free high-hardness yellow Lima alloy for casting Buddha statues in Tibetan areas and its technology. In terms of weight percentage, the composition of the alloy is Ba:0.7wt.%, Mg:6.0wt.%, Zn:13.0wt.%, Bi:5.0wt.%, Sb:3.5wt.%, Mo:1.4wt.% , Au: 2.5wt.%, Ag: 19.0wt.%, and the balance is copper. The above-mentioned lead-free high-hardness yellow Lima alloy and its process for casting Buddha statues in Tibetan areas include the following steps: adding the above-mentioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; The raw materials are added to the induction furnace under the argon environment, and graphite crucible is used; when smelting, it is kept at 1200 degrees for 10 minutes, and it is stirred evenly by high-frequency induction furnace; after stirring, it is kept at 1200 degrees for 1 minute and cast out of the furnace; the alloy Casting adopts a steel mold with a diameter of 20-30mm, and uses water cooling ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lead-free high-hardness yellow Lima alloy for cast Buddha figures in the Tibetan region and a process thereof. The alloy comprises the following components in percentage by weight: 0.6-0.8 wt.% of Ba, 5.0-8.0 wt.% of Mg, 12.0-14.0 wt.% of Zn, 4.0-6.0 wt.% of Bi, 3.0-4.0 wt.% of Sb, 1.0-2.0 wt.% of Mo, 2.0-3.0 wt.% of Au, 18.0-24.0 wt.%, and the balance of copper. The material provides a lead-free and mercury-free new material scheme to the Lima alloy for bronze statue casting in the Tibetan region; and the obtained product achieves excellent yellow appearance. Throughimplementation and industrialization of the material, the new material updating and industrial updating demands can be effectively promoted.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a copper alloy. Background technique [0002] The copper casting process has a long history in our country, and it appeared as early as the Shang and Zhou dynasties. The early copper casting process was mostly used for casting Buddha statues, which has low cost and great flexibility. The production process of copper Buddha statues in Tibet is divided into two categories: one is the casting process, and the cast bronze Buddha statues are mainly small Buddha statues. The other category is the craftsmanship of making Buddha statues, mainly large Buddha statues. These cultural treasures embody the superb casting skills and splendid culture in ancient my country. [0003] There are currently two known casting processes for bronze Buddha statues: the lost wax method and the sand fan method. [0004] (1) Lost wax method. The principle is to use wax to make the same mold as the casti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C9/00C22C1/02C22F1/08C22F1/02
CPCC22C9/00C22C1/02C22F1/02C22F1/08
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com