Novel thermal resistant casting magnesium alloy with liquid-phase spinodal decomposition form

A technology of amplitude modulation decomposition and magnesium alloy, which is applied in the field of alloys to achieve beneficial physical and mechanical properties, clear outline and smooth surface.

Inactive Publication Date: 2018-12-25
GUANGZHOU YUZHI TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But unfortunately, there are no new products based on this design concept in the field of magnesium alloys at home and abroad.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A new heat-resistant magnesium alloy for casting with liquid phase amplitude modulation decomposition type. In terms of weight percentage, the composition of the alloy is Cs:0.5wt.%, W:0.2wt.%, In:8.0wt.%, Bi:3.0wt.%, V:0.1wt.%, Hf:0.5wt.% , Si: 4.0wt.%, Sc: 1.0wt.%, and the balance is magnesium. The above-mentioned novel heat-resistant and liquid-phase amplitude-modulated magnesium alloy for casting comprises the following steps: adding the above-mentioned proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; melting at 700 degrees Keep warm for 10 minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 700 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is heated to 650-700 degrees under the protection of argon and kept for 10 minutes; t...

Embodiment 2

[0021] A new heat-resistant magnesium alloy for casting with liquid phase amplitude modulation decomposition type. In terms of weight percentage, the composition of the alloy is Cs:0.9wt.%, W:0.4wt.%, In:12.0wt.%, Bi:5.0wt.%, V:0.2wt.%, Hf:0.8wt.% , Si: 6.0wt.%, Sc: 1.2wt.%, and the balance is magnesium. The above-mentioned novel heat-resistant and liquid-phase amplitude-modulated magnesium alloy for casting comprises the following steps: adding the above-mentioned proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; melting at 700 degrees Keep warm for 10 minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 700 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is heated to 650-700 degrees under the protection of argon and kept for 10 minutes; ...

Embodiment 3

[0024] A new heat-resistant magnesium alloy for casting with liquid phase amplitude modulation decomposition type. In terms of weight percentage, the composition of the alloy is Cs:0.8wt.%, W:0.3wt.%, In:9.0wt.%, Bi:3.5wt.%, V:0.1wt.%, Hf:0.6wt.%. , Si: 4.2wt.%, Sc: 1.1wt.%, and the balance is magnesium. The above-mentioned novel heat-resistant and liquid-phase amplitude-modulated magnesium alloy for casting comprises the following steps: adding the above-mentioned proportioned raw materials into an induction furnace under an argon environment, and using a graphite crucible; melting at 700 degrees Keep warm for 10 minutes, stir evenly by high-frequency induction furnace electromagnetically; after stirring evenly, keep warm at 700 degrees for 1 minute and cast out of the furnace; alloy casting uses a steel mold with a diameter of 20-30mm, and uses water cooling to cool down. The obtained ingot is heated to 650-700 degrees under the protection of argon and kept for 10 minutes; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel thermal resistant casting magnesium alloy with a liquid-phase spinodal decomposition form. The magnesium alloy comprises the following components in percentage by weight: 0.5-0.9wt.% of Cs, 0.2-0.4wt.% of W, 8.0-12.0wt.% of In, 3.0-5.0wt.% of Bi, 0.1-0.2wt.% of V, 0.5-0.8wt.% of Hf, 4.0-6.0wt.% of Si, 1.0-1.2wt.% of Sc and the balance of magnesium. By adopting the magnesium alloy, casting defects are effectively eliminated, formation of casting pores and looseness is reduced, and excellent mechanical properties of a cast alloy part are achieved. Therefore, the invention provides a lightening solving scheme of a magnesium alloy substitution product, and updating and industry updating requirements of novel materials in China are effectively promoted in the implementation and industrialization process.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a magnesium alloy. Background technique [0002] Magnesium is one of the most abundant light metal elements on the earth, and it can be described as inexhaustible. Magnesium alloy is an alloy composed of magnesium and other elements. Its characteristics are: low density, high specific strength, large elastic modulus, good shock absorption, greater impact load capacity than aluminum alloy, and good corrosion resistance. The specific gravity of magnesium alloy is the lightest among all structural alloys. The specific strength of magnesium alloy is obviously higher than that of aluminum alloy and steel, and the specific stiffness is equivalent to that of aluminum alloy and steel. In the elastic range, when the magnesium alloy is subjected to an impact load, the energy absorbed is greater than that of the aluminum alloy, so the magnesium alloy has good shock resistance and noise red...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/00C22C1/02C22C1/10C22F1/02C22F1/06
CPCC22C1/02C22C23/00C22F1/02C22F1/06
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com