A kind of artemisinin cellulose fiber and preparation method thereof

A technology of cellulose fiber and artemisinin, applied in the field of textile, can solve the problem that artemisinin cannot be applied, and achieve the effects of good water absorption and moisture permeability, not easy to fade, and less floating color.

Active Publication Date: 2021-02-12
汕头市欣和健康管理有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] (4) Solve the problem that artemisinin cannot be applied to cellulose fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Example 1 A kind of artemisinin cellulose fiber and its preparation method

[0047] The preparation method comprises the following steps:

[0048] 1. Preparation of spinning dope

[0049] Cotton pulp with a degree of polymerization of 650 and bamboo pulp with a degree of polymerization of 700 are fully mixed with lye, soaked for 30 minutes, and pressed to make alkali cellulose;

[0050] The mass ratio of the cotton pulp, bamboo pulp and lye is 2:3:40;

[0051] The lye: a sodium hydroxide solution with a concentration of 200g / L and a temperature of 40°C.

[0052] The alkali cellulose was sheared and pulverized, and aged, the shear rate was 1800 times / min, the pulverization time was 8 min, the aging temperature was 15°C, and the aging time was 30 min;

[0053] After aging treatment, it is mixed with carbon disulfide for yellowing reaction, the yellowing temperature is 24°C, and the yellowing time is 30 minutes; cellulose xanthate is generated;

[0054] The usage amoun...

Embodiment 2

[0076] Example 2 A kind of artemisinin cellulose fiber and its preparation method

[0077] The preparation method comprises the following steps:

[0078] 1. Preparation of spinning dope

[0079] Cotton pulp with a degree of polymerization of 750 and bamboo pulp with a degree of polymerization of 800 are fully mixed with lye, soaked for 40 minutes, and pressed to make alkali cellulose;

[0080] The mass ratio of the cotton pulp, bamboo pulp and lye is 2:3:40;

[0081] The lye: a sodium hydroxide solution with a concentration of 210g / L and a temperature of 45°C.

[0082] The alkali cellulose was sheared and pulverized, and aged, the shear rate was 2000 times / min, the pulverization time was 10 min, the aging temperature was 18°C, and the aging time was 40 min;

[0083] After aging treatment, it is mixed with carbon disulfide for yellowing reaction, the yellowing temperature is 28°C, and the yellowing time is 40 minutes; cellulose xanthate is generated;

[0084] The usage amou...

Embodiment 3

[0106] Example 3 A kind of artemisinin cellulose fiber and its preparation method

[0107] The preparation method comprises the following steps:

[0108] 1. Preparation of spinning dope

[0109] Cotton pulp with a degree of polymerization of 700 and bamboo pulp with a degree of polymerization of 750 are fully mixed with lye, soaked for 35 minutes, and pressed to make alkali cellulose;

[0110] The mass ratio of the cotton pulp, bamboo pulp and lye is 2:3:40;

[0111] The lye: a sodium hydroxide solution with a concentration of 208g / L and a temperature of 43°C.

[0112] The alkali cellulose was sheared and pulverized, then aged, the shear rate was 1900 times / min, the pulverization time was 9 min, the aging temperature was 16°C, and the aging time was 35 min;

[0113] After aging treatment, it is mixed with carbon disulfide for yellowing reaction, the yellowing temperature is 26°C, and the yellowing time is 35 minutes; cellulose xanthate is generated;

[0114] The usage amou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to view more

Abstract

The invention provides artemisinin cellulose fiber and a preparation method thereof. The preparation method comprises an artemisinin dispersion liquid preparation step. The artemisinin dispersion liquid is prepared from the following ingredients in parts by weight: 1 to 1.5 parts of artemisinin, 0.8 to 1.1 parts of rose fruit oil, 2 to 3 parts of cedar camphor, 0.4 to 0.5 part of sodium surfactin,0.6 to 0.7 part of sodium alginate, 3 to 4 parts of sodium dodecyl benzene sulfonate, 7.5 to 8.2 parts of ethyl acetate, 2.5 to 3.4 parts of sodium hexametaphosphate and 8.2 to 8.8 parts of normal propyl alcohol. The cellulose fiber disclosed by the invention has the characteristics of good antibacterial and acarus killing functions, water absorption and water vapor permeability performance, highdye uptake and small surface dyeing.

Description

technical field [0001] The invention relates to an artemisinin cellulose fiber and a preparation method thereof, belonging to the technical field of textiles. Background technique [0002] The traditional cellulose fiber is made of natural fiber (wood fiber, cotton linter) as raw material, through alkalization, aging, sulfonation and other processes to make soluble cellulose xanthate, and then dissolved in dilute lye to make viscose , made by wet spinning, also known as viscose fiber; ordinary viscose fiber has general physical and mechanical properties and chemical properties, and is divided into cotton type, wool type and filament type, commonly known as artificial cotton, artificial wool and Rayon. [0003] Cellulose fibers are more absorbent, breathable, and softer than cotton and hemp fibers. [0004] Cellulose fiber is characterized by good dyeability, high brightness, comfortable wearing, dilute alkali resistance and good hygroscopicity. Therefore, it is widely lov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F2/10D01F1/10C08B9/00
CPCC08B9/00D01F1/103D01F2/10
Inventor 孔慧何志王青山刘俊纪永康
Owner 汕头市欣和健康管理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap