Preparation method of water-resistant and high-strength PVC wood-plastic composite

A wood-plastic composite material, high-strength technology, applied in the field of composite material processing, can solve the problems of plastic unfavorable environment protection, water resistance, poor corrosion resistance, plastic is not easy to degrade, etc., to improve comprehensive use quality, optimize strength, The effect of enhanced adsorption capacity

Inactive Publication Date: 2019-01-04
宣城市聚源精细化工有限公司
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Wood is a commonly used material in people's daily life, but with the massive felling of wood, wood resources are also in short supply, and wood has problems such as poor water resistance, poor corrosion resistance, and poor strength.
[0003] Plastic is one of the indispensable raw materials in people's life now, but plastic is not easy to degrade, and the simple use of plastic is not conducive to the protection of the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of water-resistant and high-strength PVC wood-plastic composite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A preparation method of water-resistant high-strength PVC wood-plastic composite material, comprising the steps of:

[0036] (1) Preparation of functional additives:

[0037] 1) Put the montmorillonite in the hydrochloric acid solution for 4 minutes and then take it out, then put it in the sodium hydroxide solution for 5 minutes and take it out, and finally wash it with deionized water until it is neutral and set it aside;

[0038] 2) Put the montmorillonite treated in operation 1) into the calcination furnace for calcination treatment, and take it out after 1.5h for later use;

[0039] 3) Put the montmorillonite treated in operation 2) into the microwave irradiation box for irradiation treatment, and take it out after 40 minutes for later use;

[0040] 4) 12-hydroxystearic acid, manganese sulfate, zinc sulfate, sodium pyrophosphate, lanthanum nitrate, cerium nitrate, montmorillonite, xylene, ethyl acetate, and deionized water after operation 3) are treated according t...

Embodiment 2

[0060] A preparation method of water-resistant high-strength PVC wood-plastic composite material, comprising the steps of:

[0061] (1) Preparation of functional additives:

[0062] 1) Put the montmorillonite into the hydrochloric acid solution for 5 minutes and then take it out, then put it into the sodium hydroxide solution for 7 minutes and then take it out, and finally rinse it with deionized water until it is neutral and set it aside;

[0063] 2) Put the montmorillonite treated in operation 1) into the calcination furnace for calcination treatment, and take it out after 2 hours for later use;

[0064] 3) Put the montmorillonite treated in operation 2) into the microwave irradiation box for irradiation treatment, and take it out after 43 minutes for later use;

[0065] 4) 12-hydroxystearic acid, manganese sulfate, zinc sulfate, sodium pyrophosphate, lanthanum nitrate, cerium nitrate, montmorillonite, xylene, ethyl acetate, and deionized water after operation 3) are treate...

Embodiment 3

[0085] A preparation method of water-resistant high-strength PVC wood-plastic composite material, comprising the steps of:

[0086] (1) Preparation of functional additives:

[0087] 1) First put the montmorillonite into the hydrochloric acid solution for 6 minutes and then take it out, then put it into the sodium hydroxide solution for 8 minutes and then take it out, and finally rinse it with deionized water until it is neutral and set it aside;

[0088] 2) Put the montmorillonite treated in operation 1) into the calcination furnace for calcination treatment, and take it out after 2.5 hours for later use;

[0089] 3) Put the montmorillonite treated in operation 2) into the microwave irradiation box for irradiation treatment, and take it out after 45 minutes for later use;

[0090] 4) 12-hydroxystearic acid, manganese sulfate, zinc sulfate, sodium pyrophosphate, lanthanum nitrate, cerium nitrate, montmorillonite, xylene, ethyl acetate, and deionized water after operation 3) ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a water-resistant and high-strength PVC wood-plastic composite. The method includes the following steps of 1, preparation of a functional additive, 2, weighing of raw materials for use, 3, mixing treatment, 4, extrusion molding and 5, grinding treatment. According to the preparation method of the water-resistant and high-strength PVC wood-plastic composite, all steps are reasonably matched, the process is simple, the method is easy to apply and popularize, and the prepared PVC wood-plastic composite has high mechanical strength, good water resistance, strong corrosion resistance, long service life, great market competitiveness and application value.

Description

technical field [0001] The invention belongs to the field of composite material processing, and in particular relates to a preparation method of a water-resistant high-strength PVC wood-plastic composite material. Background technique [0002] Wood is a commonly used material in people's daily life, but as wood is felled wantonly, wood resources are also in short supply, and wood has problems such as poor water resistance, poor corrosion resistance, and poor strength. [0003] Plastic is one of the essential raw materials in people's life now, but plastic is not easy to degrade, and the simple use of plastic is not conducive to environmental protection. [0004] In this regard, people compound plastic and wood together to make a wood-plastic composite material. This type of material not only has high strength quality, but also has good degradable quality. However, with the continuous improvement of people's requirements for material performance, the performance of such mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L67/04C08K9/00C08K9/02C08K3/34C08K9/04C08K3/30C08K3/28
CPCC08K2003/3045C08L27/06C08L97/02C08L67/04C08K9/00C08K9/02C08K3/346C08K9/04C08K3/30C08K3/28
Inventor 程聚光
Owner 宣城市聚源精细化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap