A kind of high wear resistance martensitic wear-resistant steel plate and its manufacturing method

A technology of high wear resistance, wear-resistant steel plate, applied in the field of steel plate manufacturing, can solve the problems of large micron-scale TiC size, poor plasticity and toughness of steel plate, particle concentration, etc., to increase the grain boundary area, improve wear resistance, The effect of improving plasticity and toughness

Active Publication Date: 2019-11-22
NORTHEASTERN UNIV LIAONING +2
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the size of micron-sized TiC is too large, the quantity is too large, and the particles are too concentrated, it is easy to cause the plasticity and toughness of the steel plate to deteriorate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high wear resistance martensitic wear-resistant steel plate and its manufacturing method
  • A kind of high wear resistance martensitic wear-resistant steel plate and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072]A martensitic wear-resistant steel according to the present invention comprises the following chemical composition by weight percentage: C: 0.33%; Si: 0.02%; Mn: 0.8%; Ti: 0.6%; Nb: 0.02%; Mo Cr: 0.35%; B: 0.0010%; S: 0.003%; P: 0.012%; the balance is Fe and unavoidable impurity elements.

Embodiment 2

[0074] A martensitic wear-resistant steel according to the present invention comprises the following chemical composition by weight: C: 0.36%; Si: 0.30%; Mn: 1.0%; Ti: 0.65%; Nb: 0.03%; Mo Cr: 0.45%; B: 0.0020%; S: 0.002%; P: 0.005%; the balance is Fe and unavoidable impurity elements.

Embodiment 3

[0076] A martensitic wear-resistant steel according to the present invention comprises the following chemical composition by weight: C: 0.34%; Si: 0.05%; Mn: 0.8%; Ti: 0.7%; Nb: 0.02%; Mo Cr: 0.38%; B: 0.0015%; S: 0.001%; ​​P: 0.010%; the balance is Fe and unavoidable impurity elements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a martensite wear-resistant steel plate with high wear resistance, belonging to the technical field of steel manufacturing. According to a technical scheme in the invention, the martensite wear-resistant steel plate comprises the following chemical components by weight: 0.32 to 0.38 % of C, 0.02 to 0.30% of Si, 0.8 to 1.0% of Mn, 0.6 to 0.8% of Ti, 0.02 to 0.03% of Nb, 0.15-0.20% of Mo, 0.35-0.45% of Cr, 0.0010-0.0020% of B, no more than 0.003% of S and no more than 0.012% of P, with the balance being Fe and unavoidable impurity elements. In the process of hot continuous rolling in the invention, TiC particles precipitated through continuous casting are gradually fragmented and homogenized along a rolling direction; through rolling fragmentation and solid-state precipitation of nano-sized TiC, most of the micron-sized TiC particles precipitated through continuous casting disappear; and nano-sized TiC can refine original austenite grains and improve ductility andtoughness.

Description

technical field [0001] The invention belongs to the technical field of steel plate manufacturing, and in particular relates to a martensitic wear-resistant steel plate with high wear resistance and a manufacturing method thereof. Background technique [0002] Wear-resistant steel plates are widely used in mechanical products, and their working conditions are harsh, so wear-resistant steel plates are required to have high strength and high wear resistance. [0003] The structure of traditional wear-resistant steel plates usually chooses single-phase martensite, and the main method to improve its wear resistance is to increase the hardness, which mainly depends on increasing the carbon content in the steel plate; however, the increase in carbon content, the processing performance of the steel plate And the welding performance is seriously deteriorated, and it is difficult to meet the relevant requirements of equipment manufacturing. [0004] In the prior art, micron-sized TiC...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/28C22C38/26C22C38/22C22C38/32C21D8/02B22D11/111C21D1/18
CPCB22D11/111C21D1/18C21D8/0226C21D2211/004C21D2211/008C22C38/02C22C38/04C22C38/22C22C38/26C22C38/28C22C38/32
Inventor 梁亮邓想涛刘旭辉李光辉肖尊湖黄龙汪净王昭东谢世正肖爱达徐德强汪宏兵刘浩
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com