Extrusion grade polypropylene material with high heat resistance and method for preparing extrusion grade polypropylene material

A polypropylene material, high heat-resistant technology, applied in the field of polypropylene materials, can solve the problems of poor impact strength, aging resistance and heat resistance, achieve excellent heat resistance, long oxidation induction time, reduce catalytic induction The effect of action

Inactive Publication Date: 2019-04-05
HEFEI GENIUS NEW MATERIALS
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the slightly poor impact strength, aging resistance and heat resistance of polypropylene materials, there are certain limitations in the pipe market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Extrusion grade polypropylene material with high heat resistance and method for preparing extrusion grade polypropylene material
  • Extrusion grade polypropylene material with high heat resistance and method for preparing extrusion grade polypropylene material
  • Extrusion grade polypropylene material with high heat resistance and method for preparing extrusion grade polypropylene material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Put 46g PPR1042, 30g talcum powder AH51210, 19g toughening agent-8150, 1g compound heat-resistant agent, 0.3g EBS / P-130, 0.2g antioxidant 1010 and 0.4g antioxidant 168 into the high-speed After mixing in the mixer for 5-8 minutes, take it out, carry out melt blending extrusion, traction, and granulation in a twin-screw extruder, the temperature of the barrel of the extruder is 170-195 ° C, and the main screw speed is fixed at 180 rpm. The obtained pellets were injection-molded using an injection molding machine at an injection molding temperature of 190° C. to obtain ISO standard mechanical test specimens for product performance testing. See Table 1 for test data.

Embodiment 2

[0032] Put 80g PPK8003, 10g talcum powder AH51210, 3g toughening agent-8150, 0.4g compound heat-resistant agent, 0.5g EBS / P-130, 0.1g antioxidant 1010 and 0.2g antioxidant 168 into the above ratio Take it out after mixing in the high-speed mixer for 5-8 minutes, and carry out melt blending, extrusion, traction, and granulation in the twin-screw extruder. . The obtained pellets were injection-molded using an injection molding machine at an injection molding temperature of 190° C. to obtain ISO standard mechanical test specimens for product performance testing. See Table 1 for test data.

Embodiment 3

[0034] Put 65g PPK8303, 20g talcum powder AH51210, 14g toughening agent-8842, 1g compound heat-resistant agent, 0.1g EBS / P-130, 0.3g antioxidant 1010 and 0.3g antioxidant 168 into the high-speed After mixing in the mixer for 5-8 minutes, take it out, carry out melt blending extrusion, traction, and granulation in a twin-screw extruder, the temperature of the barrel of the extruder is 170-195 ° C, and the main screw speed is fixed at 180 rpm. The obtained pellets were injection-molded using an injection molding machine at an injection molding temperature of 190° C. to obtain ISO standard mechanical test specimens for product performance testing. See Table 1 for test data.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an extrusion grade polypropylene material with high heat resistance and a method for preparing the extrusion grade polypropylene material. The extrusion grade polypropylene material comprises polypropylene, mineral filling, toughening agents, lubricants, antioxidants, complex heat-resistant agents and light stability complex agents. The polypropylene, the mineral filling, the toughening agents, the lubricants, the antioxidants, the complex heat-resistant agents and the light stability complex agents are mixed, extruded and granulated to obtain the extrusion grade polypropylene material. The extrusion grade polypropylene material and the method have the advantages that the complex heat-resistant agents are used, and accordingly the extrusion grade polypropylene material is high in heat aging resistance and light aging resistance; the excellent mechanical properties of the extrusion grade polypropylene material can be guaranteed, and application of the extrusion grade polypropylene material in the aspect of liquid delivery and storage systems of chemical pipelines further can be expanded.

Description

technical field [0001] The invention belongs to the technical field of polypropylene materials, and in particular relates to an extrusion-grade high heat-resistant polypropylene material and a preparation method thereof. Background technique [0002] With the wide application of polypropylene pipes in machinery manufacturing, petrochemical industry and various agricultural industries, in recent years, it has expanded to more fields. However, due to the slightly poor impact strength, aging resistance and heat resistance of polypropylene materials, there are certain limitations in the pipe market. However, polypropylene has a large proportion of raw materials and low raw material cost. After modification, its excellent top performance has made it grow into the most widely used plastic product after polyethylene. [0003] Over the years, we have been committed to improving polypropylene materials, overcoming problems such as aging resistance and poor heat resistance, and gradu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L23/00C08K13/02C08K5/134C08K5/526C08K5/524C08K5/20B29B9/06
CPCC08L23/12B29B9/06C08L2201/08C08L23/14C08L23/00C08K13/02C08K5/1345C08K5/526C08K5/524C08K5/20
Inventor 杨桂生王华朱敏
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap