High-performance long-service-life EPDM pump valve body material

A long-life, high-performance technology, applied in the field of pump and valve materials, to achieve the effect of improving mechanical quality, improving market competitiveness and production efficiency, and improving performance

Inactive Publication Date: 2019-04-16
安徽江南泵阀集团有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although certain effects have been achieved, as the market continues to improve product performance requirements, its performance needs to be further enhanced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance long-service-life EPDM pump valve body material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A high-performance and long-life EPDM pump valve body material is made of the following substances by weight:

[0030] 45 parts of ethylene propylene rubber, 26 parts of nano-silica, 3 parts of calcium carbonate, 2 parts of epoxy soybean oil, 18 parts of plasticizer, 2 parts of activator, 0.5 parts of vulcanizing agent, 1 part of accelerator, 5 parts of modification filler.

[0031] Further, the particle size of the nano white carbon black is 30-70nm.

[0032] Further, the particle size of the calcium carbonate is 500-600 mesh.

[0033] Further, the preparation method of the modified filler comprises the following steps:

[0034] 1) First put the silicon substrate into the acetone solution for 6 minutes of ultrasonic treatment, then take out the silicon substrate and dry it for later use;

[0035] 2) Put the silicon substrate treated in step 1) into a magnetron sputtering apparatus, and then coat a layer of gold film with a thickness of 15-20nm on the surface of the ...

Embodiment 2

[0047]A high-performance and long-life EPDM pump valve body material is made of the following substances by weight:

[0048] 48 parts of ethylene propylene rubber, 28 parts of nano-silica, 5 parts of calcium carbonate, 3 parts of epoxy soybean oil, 20 parts of plasticizer, 2.3 parts of activator, 1 part of vulcanizing agent, 1.5 parts of accelerator, 7 parts of modification filler.

[0049] Further, the particle size of the nano white carbon black is 30-70nm.

[0050] Further, the particle size of the calcium carbonate is 500-600 mesh.

[0051] Further, the preparation method of the modified filler comprises the following steps:

[0052] 1) Put the silicon substrate into the acetone solution to soak and ultrasonicate for 7 minutes, then take out the silicon substrate and dry it for later use;

[0053] 2) Put the silicon substrate treated in step 1) into a magnetron sputtering apparatus, and then coat a layer of gold film with a thickness of 15-20nm on the surface of the sil...

Embodiment 3

[0065] A high-performance and long-life EPDM pump valve body material is made of the following substances by weight:

[0066] 50 parts of ethylene propylene rubber, 30 parts of nano-silica, 6 parts of calcium carbonate, 4 parts of epoxy soybean oil, 22 parts of plasticizer, 2.5 parts of activator, 1.5 parts of vulcanizing agent, 2 parts of accelerator, 8 parts of modification filler.

[0067] Further, the particle size of the nano white carbon black is 30-70nm.

[0068] Further, the particle size of the calcium carbonate is 600 mesh.

[0069] Further, the preparation method of the modified filler comprises the following steps:

[0070] 1) First put the silicon substrate into the acetone solution for 8 minutes of ultrasonic treatment, then take out the silicon substrate and dry it for later use;

[0071] 2) Put the silicon substrate treated in step 1) into a magnetron sputtering apparatus, and then coat a layer of gold film with a thickness of 15-20nm on the surface of the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-performance long-service-life EPDM pump valve body material. The material is prepared from ethylene propylene rubber, nano white carbon black, calcium carbonate, epoxy soybean oil, a plasticizer, an activating agent, a vulcanizing agent, a promoting agent and modified filler. The material has the advantages that raw material components of the EPDM pump valve body material are optimized and improved, the using performance of the EPDM pump valve body material is well improved, the mechanical quality of the EPDM pump valve body material is improved, the service lifeof the EPDM pump valve body material is prolonged, the marketing competition performance and the production efficiency are improved, and the EPDM pump valve body material has high popularization andapplication value.

Description

technical field [0001] The invention belongs to the technical field of pump valve materials, and in particular relates to a high-performance and long-life EPDM pump valve body material. Background technique [0002] Seals are components that prevent fluid or solid particles from leaking from adjacent joint surfaces and prevent external impurities such as dust and moisture from intruding into the interior of machinery and equipment. Seals can be divided into static seals and dynamic seals. Static seals mean that the seals and the device chamber they seal are relatively fixed, while dynamic seals are relatively moving. For example, the seals of valve pumps are usually equipped with constant Reciprocating dynamic seals. [0003] The traditional EPDM (ethylene propylene diene monomer) rubber formula is mainly filled with carbon black, and the EPDM material itself is not wear-resistant, so the EPDM material is used to make dynamic seals (such as O-Ring), in dynamic seals In the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L91/00C08K13/06C08K3/36C08K3/26C08K9/06C08K9/10C08K3/22
CPCC08L23/16C08K2201/011C08K2003/2231C08K2003/265C08K2201/003C08L91/00C08K13/06C08K3/36C08K3/26C08K9/06C08K9/10C08K3/22
Inventor 吴同茂吴敏吴瑞斌戴高岩
Owner 安徽江南泵阀集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com