A kind of preparation method of phenylsulfonic acid group modified sba-15 composite material and its application in the synthesis structure phospholipid

A technology of phenylsulfonic acid group and composite material, which is applied in the fields of compounds of Group 5/15 elements of the periodic table, chemical instruments and methods, phosphorus organic compounds, etc., and can solve the problems that the application has not been effectively developed.

Active Publication Date: 2021-07-06
DALIAN POLYTECHNIC UNIVERSITY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the application of modified SBA-15 composites in the catalytic synthesis of structural phospholipids by transesterification has not been effectively developed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of phenylsulfonic acid group modified sba-15 composite material and its application in the synthesis structure phospholipid
  • A kind of preparation method of phenylsulfonic acid group modified sba-15 composite material and its application in the synthesis structure phospholipid
  • A kind of preparation method of phenylsulfonic acid group modified sba-15 composite material and its application in the synthesis structure phospholipid

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] The technical purpose of the first aspect of the present invention is to provide SBA-15 and the preparation method of SBA-15 catalyst containing phenylsulfonic acid group, including the preparation method of SBA-15 molecular sieve and the step of modifying phenylsulfonic acid group.

[0046] The technical purpose of the second aspect of the present invention is to provide a method for producing modified phospholipids, wherein the SBA-15 composite material modified with phenylsulfonic acid group and natural phospholipids carry out transesterification heterogeneous catalytic reaction.

Embodiment 1

[0048] The preparation method of phenylsulfonic acid group modified SBA-15 composite material comprises the steps:

[0049] S1. Weigh and mix SBA-15, phenyltrimethoxysilane and absolute ethanol according to the weight ratio of 1:1:17, reflux and stir for 24 hours under nitrogen atmosphere at 80°C at 600r / min, cool to room temperature, and pump Filter and collect the precipitate, the resulting precipitate is SBA-15-Ph;

[0050] S2. Using methanol whose volume accounts for 1 / 3 of the volume of the extraction bottle, perform Soxhlet extraction on the SBA-15-Ph obtained in step S1 with an added amount of 1 / 10 of the methanol weight, and remove the SBA-15-Ph precipitate at 70°C and reflux for 10 hours The phenylsilane in the mixture was suction-filtered to obtain a filter cake, which was dried for 10 hours at a vacuum degree of -0.02MPa and a temperature of 30°C, and ground into powder;

[0051] S3. Weigh the powder obtained in step S2 and anhydrous 1,2-dichloroethane and mix them...

Embodiment 2

[0067] The preparation method of phenylsulfonic acid group modified SBA-15 composite material comprises the steps:

[0068] S1. Weigh and mix SBA-15, phenyltriethoxysilane and anhydrous methanol according to the weight ratio of 3:3:20, reflux and stir for 30 hours in a nitrogen environment at 70°C at a speed of 1000r / min, and cool to room temperature. Suction filtration and collection of the precipitate, the resulting precipitate is SBA-15-Ph;

[0069]S2. Use ethylbenzene whose volume accounts for 1 / 3 of the volume of the extraction bottle, perform Soxhlet extraction on the SBA-15-Ph obtained in step S1 with an added amount of 1 / 100 of the ethylbenzene weight, and remove SBA-15-Ph at 140°C and reflux for 12 hours. The phenylsilane in the Ph precipitate was suction-filtered to obtain a filter cake, dried at a vacuum degree of -0.08MPa and a temperature of 90°C for 14 hours, and ground into powder;

[0070] S3. Weigh the powder obtained in step S2 and anhydrous 1,2-dibromoethan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a phenylsulfonic acid-modified SBA-15 composite material, using SBA-15, a phenylsilane coupling agent and an anhydrous organic solvent as raw materials to prepare SBA-15-Ph; The obtained SBA‑15‑Ph is sulfonated to obtain a phenylsulfonic acid group modified SBA‑15 composite material; the present invention also discloses the application of the phenylsulfonic acid group modified SBA‑15 composite material in the synthesis of structural phospholipids, Using phospholipids and fatty acid methyl esters or fatty acid ethyl esters as raw materials, under the catalysis of phenylsulfonic acid group-modified SBA-15 composite materials, a new type of structural phospholipids is obtained. The modified phospholipids prepared by the present invention broaden the application range of phospholipids, and at the same time, the residual organic matter in the product is less; it can also solve the disadvantages of expensive enzyme sources, difficult recycling, and not wide reaction conditions in the process of enzymatic production of structural phospholipids, and finally improve the structure Preparation method of phospholipids.

Description

technical field [0001] The invention relates to a preparation method and application of a catalyst, in particular to a preparation method of a phenylsulfonic acid group-modified SBA-15 composite material and its application in synthesizing structural phospholipids. Background technique [0002] Phospholipids are essential components of cellular infrastructure and play an important role in maintaining cell permeability and intracellular oxygen delivery. In addition, phospholipid is also a natural amphoteric surfactant, which has various properties such as emulsification, dispersion, and wetting, and can reduce skin surface tension and enhance bone function. Therefore, phospholipids have a wide range of applications in the fields of cosmetics, medicine, food, leather and industrial additives. Natural phospholipids exist in a wide range. Phospholipids exist in soybeans, egg yolks, and animal internal organs. Among them, soybean phospholipids are the most widely used because of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07F9/09C07F9/117B01J29/03
Inventor 张江华周大勇朱蓓薇郭伟徐同宽蔡伟杰刘中原宣皓赵一荻
Owner DALIAN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap