A kind of stepped flame-retardant rubber material and preparation method thereof

A flame retardant rubber, stepped technology, applied in the field of stepped flame retardant rubber materials and their preparation, can solve the problems of poor dispersion and fluidity of non-halogen flame retardant materials, inability to provide multi-stage flame retardant effects, etc. Mechanical strength, the effect of preventing decomposition, and promoting carbonization

Active Publication Date: 2021-06-01
FOSHAN YUEJIAXIN WIRE & CABLE
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of the shortcomings of the above-mentioned prior art, the object of the present invention is to provide a stepped flame-retardant rubber material and its preparation method, aiming at solving the problem of poor dispersion and fluidity of non-halogen flame-retardant materials in rubber in the prior art , the defect of not being able to provide multi-level flame retardant effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of stepped flame-retardant rubber material and preparation method thereof
  • A kind of stepped flame-retardant rubber material and preparation method thereof
  • A kind of stepped flame-retardant rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] A stepped flame-retardant rubber material is characterized in that it comprises the following components in parts by weight:

[0073] 80 parts of rubber;

[0074] 80 parts of flame retardant;

[0075] 40 parts of stuffing;

[0076] Auxiliary 0.3 parts.

[0077] The flame retardant is an inorganic flame retardant powder coated with a liquid-terminated carboxyl nitrile rubber modified epoxy resin, and the weight of the liquid carboxyl nitrile rubber modified epoxy resin is 0.1% of the weight of the inorganic flame retardant powder , the inorganic flame retardant powder is prepared from inorganic silicon-aluminum shell-forming materials, and the inorganic silicon-aluminum shell-forming materials include:

[0078] SiO 2 30 copies;

[0079] h 3 BO 3 25 copies;

[0080] CaCO 3 5 copies;

[0081] K 2 CO 3 5 copies;

[0082] NaNO 3 5 copies;

[0083] Na 2 O 5 copies;

[0084] Al 2 o 3 1 copy;

[0085] Na 2 SO 4 0.1 copies;

[0086] La 2 o 3 0.05...

Embodiment 2

[0096] A stepped flame-retardant rubber material is characterized in that it comprises the following components in parts by weight:

[0097] 120 parts of rubber;

[0098] 200 parts of flame retardant;

[0099] Filling 60 parts;

[0100] Auxiliary 2 parts.

[0101] The flame retardant is an inorganic flame retardant powder whose surface is coated with a liquid-terminated hydroxy nitrile rubber-modified epoxy resin, and the weight of the liquid-terminated hydroxy nitrile rubber-modified epoxy resin is 0.5% of the weight of the inorganic flame retardant powder , the inorganic flame retardant powder is prepared from inorganic silicon-aluminum shell-forming materials, and the inorganic silicon-aluminum shell-forming materials include by weight parts:

[0102] SiO 2 40 copies;

[0103] h 3 BO 3 35 copies;

[0104] CaCO 3 10 copies;

[0105] K 2 CO 3 10 copies;

[0106] NaNO 3 10 copies;

[0107] Na 2 O 10 copies;

[0108] Al 2 o 3 5 copies;

[0109] Na 2 S...

Embodiment 3

[0121] A preferred stepped flame-retardant rubber material is characterized in that it comprises the following components in parts by weight:

[0122] 100 parts of rubber;

[0123] 110 parts of flame retardant;

[0124] Filling 55 parts;

[0125] Auxiliary 1.5 parts.

[0126] The flame retardant is an inorganic flame retardant powder whose surface is coated with a silicone modified epoxy resin, and the weight of the silicone modified epoxy resin is 0.3% of the weight of the inorganic flame retardant powder, and the inorganic flame retardant powder consists of The inorganic silicon-aluminum shell-forming material is prepared, and the inorganic silicon-aluminum shell-forming material includes in parts by weight:

[0127] SiO 2 35 copies;

[0128] h 3 BO 3 30 copies;

[0129] CaCO 3 8 copies;

[0130] K 2 CO 3 8 copies;

[0131] NaNO 3 8 copies;

[0132] Na 2 O 8 copies;

[0133] Al 2 o 3 2 copies;

[0134] Na 2 SO 4 0.2 copies;

[0135] La 2 o 3 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a stepped flame-retardant rubber material. The material comprises, in parts by weight, 80-120 parts of rubber, 80-200 parts of flame retardant, 40-60 parts of filler, 0.3-2 parts of auxiliary agent, The flame retardant is an inorganic flame retardant powder coated with a polymer modifier on the surface; the preparation method includes the steps of: preparation and modification of the inorganic flame retardant powder, and preparation of a flame retardant rubber material. Through the stepped flame-retardant rubber material and the preparation method thereof provided by the invention, the obtained rubber material has multi-stage flame-retardant properties, has flame-retardant effects in a wide high temperature range, and greatly improves the safe use performance of rubber.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a stepped flame-retardant rubber material and a preparation method thereof. Background technique [0002] Rubber products can be seen everywhere in people's production and life, and are widely used in various fields such as road traffic, housing construction, medical engineering, aerospace and navigation, etc., and play an important role in promoting urban construction and improving people's lives. However, since the main components of rubber are carbon and hydrogen, they are extremely flammable, especially nitrile rubber and some halogen-containing rubbers, which are very flammable. People's lives and property safety have also formed a huge threat. In the prior art, flame retardant properties of rubber are usually improved by adding flame retardants. Flame retardants, also known as flame retardants, fire retardants or fire retardants, are functional materials that en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L21/00C08K13/06C08K9/10C08K3/36C08K3/26C08K3/38C08K3/22
CPCC08K3/22C08K3/26C08K3/36C08K3/38C08K9/10C08K13/06C08K2003/221C08K2003/2227C08K2003/2244C08K2003/262C08K2003/265C08K2003/387C08L2201/02C08L21/00
Inventor 黄楚舒黄永忠黄俊温晓辉
Owner FOSHAN YUEJIAXIN WIRE & CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More