One-time manufacturing method of colorful TPU foamed particles through double-screw equipment

A foamed particle and twin-screw technology, which is applied in the field of foaming material preparation, can solve the problems of complex foaming process, change in physical properties of TPU resin, and high cost, and achieve the effects of simplifying foaming process, reducing physical property changes and reducing costs.

Active Publication Date: 2019-10-22
东莞市元普智造科技有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of this, the present invention aims at the deficiencies existing in the prior art, and its main purpose is to provide a method for making colored TPU foamed particles at one time by using twin-screw equipment, which can effe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-time manufacturing method of colorful TPU foamed particles through double-screw equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The invention discloses a method for making colored TPU foamed particles at one time by using twin-screw equipment, which includes the following steps:

[0019] (1) Proportioning raw materials: Take 100 parts by weight of TPU resin, 2-5 parts by weight of POE-g-MAH and 1-3 parts by weight of organic pigment; in this embodiment, the organic pigment is a fluorescent pigment, which can be Various colors are not limited.

[0020] (2) Stirring and mixing: Put the above-mentioned raw materials into a blender and stir and mix evenly.

[0021] (3) Heating and melting: Put the mixed material into the twin-screw hopper and adjust the temperature of the first to fifth zones of the twin-screw to be the melting section, so that the material passes through the first to fifth zones to complete the melting process.

[0022] (4) Injecting gas: Set reverse-rotating threads in the sixth zone of the twin-screw, and inject nitrogen or carbon dioxide gas here.

[0023] (5) Uniform mixing o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a one-time manufacturing method of colorful TPU foamed particles through double-screw equipment. The method comprises the following steps of (1) proportioning raw materials comprising, by weight, 100 parts of TPU resin, 2-5 parts of POE-g-MAH and 1-3 parts of organic pigments; (2) conducting stirring and mixing; (3) conducting heating and melting; (4) injecting gas, specifically, arranging left-handed threads in a sixth area of a double-screw and injecting nitrogen or carbon dioxide gas to the sixth area; (5) evenly mixing the gas and the molted materials, specifically,arranging engagement blocks from a sixth area to a ninth area of the double-screw to enable the injected gas, the organic pigments, the TPU resin and the POE-g-MAH The invention be mixed evenly; (6)conducting cooling extrusion; and (7) conducting cooling and shaping. Through the method, the colorful TPU foamed particles are manufactured at a time, the forming process is simplified, and the costis reduced. Physical property changes, caused by repeated heating and processing, to the TPU resin originally are reduced. The method is suitable for mass production. Moreover, the color and forming density of the colorful TPU foamed particles can be adjusted at random. The method has the good promotion and utilization value.

Description

technical field [0001] The invention relates to the technology in the field of foam material preparation, in particular to a method for preparing colored TPU foam particles at one time by using twin-screw equipment. Background technique [0002] TPU foam material is actually a new type of polymer material composed of numerous elastic and light weight TPU foam balls. After foaming, the volume of this particle material expands 5-8 times, and the cells The diameter is only about 30 microns to 300 microns, the size and shape are the same as popcorn, and the density of 0.15-0.25 grams per cubic centimeter makes people hardly feel its weight. Therefore, it is called "popcorn" by the industry. It overcomes the shortcomings of TPU raw materials such as heavy weight, high hardness, and poor shock absorption performance. At the same time, it is lighter in weight, more breathable, environmentally friendly, wear-resistant, high-elastic, and yellowing-resistant. It is the insole material...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C48/04
CPCB29C48/04B29C48/0012
Inventor 陈友柱陈奎邓海平赵年红
Owner 东莞市元普智造科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap