A kind of architectural powder coating with anti-mildew properties

A powder coating and construction technology, applied in the field of architectural powder coatings, can solve the problems that the coating is easy to breed bacteria and mold, does not have antibacterial and antifungal properties, and affects people's quality of life, etc., to maintain antibacterial and antifungal properties and long-term antibacterial and antifungal properties , the effect of stabilizing the dielectric constant and dielectric loss

Active Publication Date: 2021-09-21
安徽群升建筑工程有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In areas with high humidity or continuous rainy weather, the coatings used for walls and roofs are prone to breed bacteria and mold, or the dark corners of the house, especially the kitchen, are prone to breed bacteria and mold, and the mold will spread with the air flow. If the room is full, touching the wall after cleaning will lead to the spread of mold, which will seriously affect people's quality of life and bring certain harm to human health.
[0004] Acrylic resin has excellent weather resistance, chemical resistance, excellent color retention and adhesion, high gloss and durability, and is widely used in surface protection and decoration of architectural coatings, automobiles, home appliances, metal products, etc., but with When used in architectural coatings, acrylic resins are limited in their application due to hot stickiness, cold brittleness, high water absorption and no antibacterial and antifungal properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of architectural powder coating with anti-mildew properties
  • A kind of architectural powder coating with anti-mildew properties
  • A kind of architectural powder coating with anti-mildew properties

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Raw material source:

[0034] 2-(2-Benzothiazole) ethyl acetate: CAS number: 29182-42-1; purchase source: Shanghai Xianding Biotechnology Co., Ltd.;

[0035] Aminoethylaminopropyldimethoxysilane: CAS number: 3069-29-2; purchase source: Bailingwei Technology Co., Ltd.;

[0036] 1,2-Epoxy-9-decene: CAS number: 85721-25-1; purchase source: Shanghai Xianding Biotechnology Co., Ltd.

[0037] The preparation method of mildew-resistant modifier is:

[0038] A1. Add 10mmol 2-(2-benzothiazole)ethyl acetate 2 and 800ml DMF as a solvent into the reaction kettle, start stirring, heat up to 95°C, add 0.2mmol sodium ethoxide, then dropwise add 10.6mmol aminoethylaminopropyl Dimethoxysilane 1 was fed into nitrogen gas at the same time, stirred and reacted for 3 hours, after the reaction was completed, the solvent and the reacted methanol were distilled off under reduced pressure to obtain amide compound 3 with a yield of 95.2%. The reaction formula is as follows:

[0039]

[004...

Embodiment 2

[0046] A kind of architectural powder coating with anti-mold performance, including the following raw materials in parts by weight: 55g modified acrylic resin, 8g polyvinyl acetate emulsion, 6g polyurethane, 20g titanium dioxide, 1g leveling agent polyacrylic acid, 1.5g antioxidant 1010 ;

[0047] The preparation method of this architectural powder coating is:

[0048] S1, preparation of modified acrylic resin

[0049] The modified acrylic resin is formed by free radical solution polymerization of 60g of 2-methyl methacrylate monomer, 30g of polyethylene glycol diacrylate monomer and 10g of anti-mold modifier monomer. Include the following steps:

[0050] The first step, pre-mixing

[0051] Add 2-methyl methacrylate monomer, polyethylene glycol diacrylate monomer and mildew-resistant modifier monomer into the ball mill, grind and mix for 15 minutes, then add 1.5g initiator and 8g medium ethanol, continue Carry out grinding and mixing for 10 minutes to obtain a homogeneous ...

Embodiment 3

[0057] A kind of architectural powder coating with anti-mildew performance, comprises the raw material of following weight part: 62g modified acrylic resin, 4g polyvinyl acetate emulsion, 4g polyurethane, 30g titanium dioxide, 1.5g leveling agent polyacrylic acid, 0.5g antioxidant 1010;

[0058] The preparation method of this architectural powder coating is:

[0059] S1, preparation of modified acrylic resin

[0060] The modified acrylic resin is formed by free radical solution polymerization of 75g of 2-methyl methacrylate monomer, 20g of polyethylene glycol diacrylate monomer and 5g of anti-mold modifier monomer. Include the following steps:

[0061] The first step, pre-mixing

[0062] Add 2-methyl methacrylate monomer, polyethylene glycol diacrylate monomer and anti-mildew modifier monomer into the ball mill, grind and mix for 20 minutes, then add 2g initiator and 10g medium ethanol, and continue Grind and mix for 15 minutes to obtain a uniformly mixed premix;

[0063]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a building powder coating with anti-mildew performance, which comprises the following raw materials in parts by weight: 55-70 parts of modified acrylic resin, 4-8 parts of polyvinyl acetate emulsion, 4-8 parts of polyurethane, 15-30 parts Titanium dioxide, 1-1.5 parts of leveling agent, 0.5-1.5 parts of antioxidant; modified acrylic resin is used as a matrix, and other components are obtained through melt extrusion, crushing, grinding, and sieving; among them, modified acrylic acid The resin is formed by free radical solution polymerization of monomer 2-methyl methacrylate, polyethylene glycol diacrylate and anti-mold modifier. The anti-mold modifier is firmly embedded in the acrylic resin through chemical bonds. , applied in architectural coatings, can maintain the water resistance and antibacterial and antifungal properties of architectural coatings for a long time, and provide people with a healthy living environment.

Description

technical field [0001] The invention belongs to the technical field of architectural coatings, in particular to an architectural powder coating with anti-mildew performance. Background technique [0002] Coating refers to a general term for a class of materials that can form a tough protective film when applied to the surface of an object. Generally, the coatings used for interior walls, exterior walls, ceilings and floors of buildings are called architectural coatings. Architectural coatings are an important category within coatings. According to the part where the paint is used, it is divided into wall paint, floor paint, roof paint, wood paint, and metal antirust paint. [0003] In areas with high humidity or continuous rainy weather, the coatings used for walls and roofs are prone to breed bacteria and mold, or the dark corners of the house, especially the kitchen, are prone to breed bacteria and mold, and the mold will spread with the air flow. If the room is full, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/12C09D131/04C09D175/04C09D5/03C09D5/14C08F220/14C08F230/08C08F222/20
CPCC08F220/14C08K2003/2241C08L2205/035C09D5/033C09D5/14C09D143/04C08L31/04C08L75/04C08L33/02C08K3/22
Inventor 代群鲁荣范红代琴
Owner 安徽群升建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com