Preparation method and application of cof-300/ppy/au(g) nanozyme catalyst

A technology of COF-300 and catalyst, applied in the direction of organic compound/hydride/coordination complex catalyst, physical/chemical process catalyst, chemical instrument and method, etc., to increase specific surface area, reduce secondary pollution, improve light The effect of catalytic performance

Active Publication Date: 2021-11-16
LANZHOU UNIVERSITY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the application of multilayer Au NPs modified COF-300 / PPy in the catalytic degradation of pollutants in water has not been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of cof-300/ppy/au(g) nanozyme catalyst
  • Preparation method and application of cof-300/ppy/au(g) nanozyme catalyst
  • Preparation method and application of cof-300/ppy/au(g) nanozyme catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] The preparation method of COF-300 / PPy / Au(G) nanozyme catalyst, the steps are as follows:

[0051] Preparation of COF-300

[0052] Accurately weigh 12mg of terephthalaldehyde and 20mg of tetrakis-(4-aminophenyl)-methane into a 10mL polytetrafluoroethylene reactor, then add 1mL of 1,4-dioxane, stir evenly with a glass rod, Add 0.2mL 3M acetic acid solution dropwise until the solution becomes transparent and bright yellow, and place it at room temperature for 2-5h; put the mixed solution in a 10mL autoclave, and react at 100°C for 72h; naturally cool to room temperature, and wash repeatedly with acetone for several times Afterwards, vacuum-dry at 60°C for 2-6 hours to obtain COF-300 light yellow powder.

[0053] Preparation of COF-300 / PPy

[0054] Under the condition of avoiding light, weigh 200mg COF-300 and add it into 20mL ultrapure water, ultrasonic 1-2h, and disperse evenly; then add 0.8mL pyrrole monomer to the above suspension, stir magnetically at 1500rpm for 2h,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of nanomaterial preparation and application, specifically the preparation method and application of COF-300 / PPy / Au(G) nano-enzyme catalyst; first, adding terephthalaldehyde and tetrakis(4-aminophenyl)methane 1,4-dioxane, stirring and dissolving, adding acetic acid and standing still, and preparing COF-300 by solvothermal method; then, using pyrrole monomer as raw material and water as solvent, using in-situ polymerization method to stir at room temperature, COF‑300@PPy composite nanomaterials were obtained; finally, COF‑300 modified with multilayer gold nanoparticles (AuNPs) was prepared by reduction and in situ growth using chloroauric acid as raw material and trisodium citrate as reducing agent / PPy / Au(G) nanozyme catalyst. The COF-300 / PPy / Au(G) nanozyme catalyst prepared by the invention exhibits high-efficiency and broad-spectrum catalysis, and has a strong catalytic degradation and removal effect on various organic substances. The preparation conditions are mild, the method is simple, and it is economically feasible.

Description

technical field [0001] The invention belongs to the technical field of nanomaterial preparation and application, in particular to a preparation method and application of COF-300 / PPy / Au(G) nanozyme catalyst. Background technique [0002] Water is the basic need to maintain life and health. With the development of social economy, water pollution is becoming more and more serious. These organic pollutants with the characteristics of heavy chroma, high concentration, stable chemical properties, complex components, and high biological toxicity are difficult to degrade when discharged into water bodies. Therefore, it is particularly important to search for a nanomaterial that is environmentally friendly, has a simple synthesis process, is cheap, and has high efficiency and can be used to remove pollutants in water. As an enzyme-mimicking catalyst, AuNPs material has the advantages of higher stability and large availability compared with natural enzymes, and has been widely used i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/06C02F1/30C02F101/34C02F101/38
CPCB01J31/069B01J35/004C02F1/30C02F2101/345C02F2101/38C02F2101/40C02F2305/10
Inventor 许银银吴涯璐冯敬博张岩李爰媛
Owner LANZHOU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com