Self-repairing polyurethane based on two-way repairing structure, preparation method and application thereof

A technology for repairing structure and polyurethane, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems such as no self-healing polyurethane material reports, loss of use efficiency, cracking, etc., and achieve the effect of excellent repair rate

Active Publication Date: 2021-04-23
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, these products are often exposed to the environment during use, and will suffer from external collisions, scratches, kinks, chemical corrosion, UV photolysis aging or a combination of effects, resulting in micro-cracks and cracks inside, making them useless. ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-repairing polyurethane based on two-way repairing structure, preparation method and application thereof
  • Self-repairing polyurethane based on two-way repairing structure, preparation method and application thereof
  • Self-repairing polyurethane based on two-way repairing structure, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0084]Preparation Example 1: Preparation of Solid Product A1 and Solid Product A2

[0085] At 40° C., 1.1 mol of p-hydroxybenzaldehyde in isopropanol (300 mL) was added into 0.5 mol of oxalodihydrazide in glacial acetic acid (250 mL), and stirred at 300 rpm for 4 h. After the reaction, filter under reduced pressure, wash with ethanol three times at 50° C., then wash with water three times, and dry the washed product to obtain solid product A1.

[0086] At 60° C., 0.2 mol of furfurylamine was added into a solution of resorcinol diglycidyl ether (0.1 mol) dissolved in methanol (50 mL), and reacted for 6 h under stirring at 500 rpm. After the reaction, the product was distilled under reduced pressure, washed with secondary water, and dried to obtain the solid product A2.

[0087] And, the proton nuclear magnetic spectra of solid product A1 and solid product A2 are respectively as follows figure 1 and figure 2 shown.

Embodiment 1

[0088] Embodiment 1: prepare polyurethane

[0089] At 50°C, 0.1 mol of isophorone diisocyanate was slowly added to the molecular weight M dissolved in N,N-dimethylformamide (300 mL) n In the polyethylene glycol (PEG 600, 0.05mol) of =600, add the dibutyltin dilaurate of 500ppm (based on the total weight of isophorone diisocyanate and polyethylene glycol), react 3h under rapid stirring, Obtain polyurethane prepolymer pre-600.

[0090] At 50°C, dissolve 0.22mol of polyurethane prepolymer pre-600 and 0.1mol of mixture A (0.05mol of solid product A1 in Preparation 1 and 0.05mol of N,N-dimethylformamide (200mL in total)) The solid product A2) in Preparation Example 1 was mixed and reacted for 12 h under stirring at 200 rpm to obtain linear polyurethane 1-600.

[0091] Add 0.06 mol of N,N'-(4,4'-methylenediphenyl)bismaleimide to linear polyurethane 1-600 (the entire amount obtained in the previous step) at 55 °C N,N-dimethylformamide dispersion liquid, mixed and stirred evenly, t...

Embodiment 2

[0092] Embodiment 2: prepare polyurethane

[0093] At 35°C, 0.1 mol of isophorone diisocyanate was slowly added to the molecular weight M dissolved in N,N-dimethylformamide (300 mL) n In the polyethylene glycol (PEG 1000, 0.05mol) of =1000, add the dibutyltin dilaurate of 500ppm (based on the total weight of isophorone diisocyanate and polyethylene glycol), react 4h under rapid stirring, The polyurethane prepolymer pre-1000 was obtained.

[0094] At 40°C, 0.22mol of polyurethane prepolymer pre-1000 and 0.1mol were dissolved in dimethyl sulfoxide (200mL in total) in mixture A (0.05mol of solid product A1 in Preparation 1 and 0.05mol of Preparation 1 The solid product A2) was mixed and reacted for 20h under stirring at 200rpm to obtain linear polyurethane 1-1000.

[0095] Add 0.06 mol of N,N'-(4,4'-methylenediphenyl)bismaleimide to linear polyurethane 1-1000 (the entire amount obtained in the previous step) at 60 °C N,N-dimethylformamide dispersion liquid, mixed and stirred e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of self-repairing photo-curing materials, and discloses self-repairing polyurethane based on a two-way repairing structure, a preparation method and application thereof. The polyurethane contains structural units provided by R1, R2, R3, R4, R5, R6 and R7; wherein R1 is polyethylene glycol, R2 is isophorone diisocyanate, R3 is terephthalaldehyde, R4 is oxalyl dihydrazide, R5 is resorcinol diglycidyl ether, R6 is furfuryl amine, and R7 is N, N'-(4, 4'-methylene diphenyl)bismaleimide. The polyurethane provided by the invention has excellent self-repairing capability and high self-repairing efficiency, the service life of the material can be prolonged, and the hidden danger of microcracks caused by mechanical damage is reduced.

Description

technical field [0001] The present invention relates to the field of self-healing polyurethane, in particular, to a self-healing polyurethane based on a two-way repairing structure, a method for preparing a self-healing polyurethane based on a two-way repairing structure, and a self-healing polyurethane based on a two-way repairing structure prepared by the method Application of polyurethane and self-healing polyurethane based on bidirectional repair structure in at least one product selected from coatings, electronic products and packaging materials. Background technique [0002] Due to its excellent mechanical properties and good chemical stability, polyurethane materials are widely used in the fields of transportation, electronics, packaging, construction and biomaterials. [0003] However, these products are often exposed to the environment during use, and will suffer from external collisions, scratches, kinks, chemical corrosion, UV photolysis aging or a combination of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/66C08G18/48C08G18/32C08G18/83C09D175/14
CPCC08G18/6685C08G18/4833C08G18/325C08G18/3834C08G18/833C09D175/14
Inventor 唐瀚滢解希铭杜影王丽静王丽丽赵丽娜赵青松
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap